Making sensitive material : made in non - sulfur vulcanization system with the formula : epdm 100kg, dicumylperoxide ( dcp ) 2kg as cross - linking agent, stearic acid 1kg as processing aid, oxidized zinc ( zno ) 3kg as accelerant, wax oil 10kg as lubricant ; and made in vulcanizing condition : vulcanizing temperature 170 c, vulcanizing time 15minutes, vulcanizing pressure 3 mpa, the vulcanized epdm is optimal sensitive material for petrol. the sensing head equipped with the vulcanized rubber possesses two qualities : better swelling response and better anti - interfere against temperature variation
敏感材料的制備:用無硫硫化體系;配方為:生膠100kg , dcp2kg ,硬脂酸1kg , zno3kg ,石蠟油10kg ;硫化條件:硫化溫度170 ,硫化時間15分鐘,硫化壓力3mpa ,制備的硫化橡膠對汽油的監測較理想,用其裝備的傳感頭不僅有較好的溶脹響應性能,而且有很好的抗溫變干擾能力。 -
These reaction products exhibited fluorescent spectra ( 400nm - 490nm ) akin to those of extracts from liposcin - rich tissues. considering that dehydroascorbic acid and mda are active in biological system, the oxidation - enhanced carbonyl - protein cross - linking is suggested to be an important chemical reaction which may take place during ageing and be involved in lipofuscinogenesis
氧化asa的化學性質非常活潑又是常見的還原酮,在我們的實驗中氧化的維c與谷氨酰氨也生成類似的熒光,所以asa與gln生成交聯產物的反應可能與衰老過程中脂褐素的生成相關。
分享友人