debonding 中文意思是什麼

debonding 解釋
界面脫離
  1. Debonding was detected for hot water immersions.

    熱水浸泡后能檢驗出脫粘。
  2. A double trapezoidal specimen will generate shear debonding.

    雙梯形的試樣將產生切變脫膠現象。
  3. Currently, the main methods used to measure the fiber / matrix interface properties of composite were based on micro - mechanics, including single - fiber composites fragmentation test ( sfc ), micro - debonding technique, single - fiber pull - out test, and single - fiber push - out test, in which sfc was most widely used

    目前直接用來測定纖維增強復合材料界面力學性能的主要微觀力學方法有單纖維復合材料斷裂實驗（ sfc ） 、微脫粘方法、單纖維拔出法、單纖維頂出法，其中以單纖維復合材料斷裂實驗的應用最為廣泛。
  4. Here, fem is applied in the analyses of i ) fiber axial stress and interphase shear stress in fragmentation tests during initially applied strain, ii ) influence of temperature on the stress transfer across the interface, iii ) modulus and thickness of the interphase and their influence on interfacial stress transfer, iv ) interfacial debonding process, and v ) fragment aspect ratio, contact friction along the interface and their influences to the interfacial stress transfer efficiency

    在論文的這部分工作中，使用有限元法描述和分析了逐節斷裂試驗中初始應變下的纖維軸向應力和界面相剪切應力，溫度對界面應力傳遞的影響，界面相模量和厚度、纖維節長寬比、界面脫粘過程、界面接觸中的摩擦效應等因素對逐節斷裂試驗中應力傳遞的影響。
  5. The research results show that transducer partially debonding results in clear change of instantaneous frequencies, mode frequencies and damping ratio of the structures

    研究結果表明，傳感器局部開膠對結構的瞬時頻率和模態頻率以及阻尼比均有明顯的影響。
  6. The results of numerical simulations and analytical solution show good accordance, except in the region near the fiber ends, where the shear - lag approach causes considerable discrepancy. next, to overcome the unrealistic assumption of perfect bonding, augmented - lagrange contact algorithm, element " birth - death " and fem are combined in the study of the partial debonding between fiber and matrix under pull out forces

    然而完全粘結的假設過于理想，與實際應用相差較大，因此，本論文將有限元法，接觸演算法和單元生死法結合起來，研究較大抽拔力作用下，纖維與基體之間發生的逐步脫粘的過程，所得到的抽拔力的變化結果，與試驗數據比較，較為一致。
  7. Several types of damage had been identified, including the matrix microcrack, fiber fracture, debonding and sliding between fiber - bundles, and fiber oxygen involved in the interaction fatigue - creep of 30 - c / sic composites

    3d - c sic1300疲勞蠕變交互作用的損傷形式包括基體開裂、纖維和纖維束的斷裂和拔出，還有纖維的氧化而引起的損傷。
  8. In this paper, the two debonding failure modes of the compound beam externally glued by frp sheets are comprehensively studied. its displaying part, style, condition, influential factors and mechanism is investigated

    本文對外貼frp加固鋼筋混凝土梁兩種粘結破壞方式進行了系統的研究，分析了粘結破壞發生的部位、方式、條件、影響因素以及粘結破壞機理。
  9. Debonding failure of beams combined strengthened with cfrp and steel plate

    碳纖維布與鋼板復合加固梁剝離破壞研究
  10. Debonding failure of reinforced concrete beams strengthened with carbon fiber sheets

    碳纖維布加固混凝土梁的剝離破壞
  11. With high performance environment friendly adhesive for automatic bonding, with no bubble and no debonding

    使用高性能的環保粘著劑（靜電吸附） ，自動貼合，無氣泡，不脫離
  12. According to different failure mechanism and displaying part, the failure modes are divided into plate end debonding failure and intermediate crack induced interfacial debonding failure

    這種粘結破壞按形成機理及破壞部位的不同可分為板端剝離破壞和跨中受彎裂縫導致的粘結破壞。
  13. However, this newly arisen method is associated with brittle debonding failure modes - flexural strength of the compound beams without omen cannot reach that under ductile failure modes, even that of unreinforced members

    然而，這個新興的技術卻時常受到粘結破壞的困擾? ?沒有破壞徵兆，而且不能達到適筋破壞梁的承載力，甚至低於未加固梁的承載力。
  14. Based on analysis and comparison of existing test data applied to existing ultimate strength prediction models, interfacial stress at the end of plate is deduced. after formulas for calculating the effective moment of inertia for frp - strengthened beams being revised and adjustment coefficient related to nominal main steel reinforcement ratio and curtailment length ratio being put forward, strength prediction formulas of compound beams under plate end debonding failure are established. in analysis of strength of compound beams under intermediate crack induced interfacial debonding failure mode, several bond strengths and their relation are introduced

    對于板端剝離破壞，在總結現有承載力模型的基礎上，利用已有試驗數據對各承載力計算公式進行了分析比較，進一步採用分階段分析法，推導了板端界面應力的計算公式，在此基礎上，採用加固復合梁有效慣性矩的修正公式，建立了考慮名義配筋率和板端偏移比影響的板端剝離破壞梁承載力的計算公式；對于跨中受彎裂縫導致的粘結破壞，闡述了常見的幾種粘結強度之間的區別和聯系，並基於拉剪粘結強度，提出了跨中受彎裂縫導致粘結破壞的承載力計算公式，並利用現有試驗結果確定了模型中的一些參數；最後，利用試驗數據對本文建立的兩種粘結破壞承載力計算公式進行了檢驗，結果基本吻合。
  15. The response of mmcs has a turning point, associated with the initiation of interfacial debonding, which is decided by the interfacial strength. unlike the two predecessors, the evolving complaint interface ( eci ) model allows unloading of interfacial stresses

    在常響應界面情況下，復合材料橫向拉伸應力?應變曲線存在明顯的轉折點，對應于界面分離的始發點，轉折點的位置取決于界面粘結強度。
  16. Elastoplastic behavior of particle reinforced metal matrix composites considering the interfacial debonding

    有界面脫粘時顆粒增強金屬基復合材料的彈塑性性能分析
  17. Some technical problems concerning the development of end burning motors, such as low takeoff acceleration, long tail - off duration and interface debonding of the stress relief flap etc are analyzed and some appropriate measures are put forward. the measures have been proved to be suitable and valuable for improving the motor performance

    就貼壁澆注的端面燃燒發動機容易產生的起動加速慢、工作拖尾時間長及尾端部人工脫粘層（蓋層）粘接脫粘等技術問題進行了分析，提出了適用的解決辦法，這些方法已被實踐證明是有效的，對提高發動機性能非常重要。
  18. Abstract : some technical problems concerning the development of end burning motors, such as low takeoff acceleration, long tail - off duration and interface debonding of the stress relief flap etc are analyzed and some appropriate measures are put forward. the measures have been proved to be suitable and valuable for improving the motor performance

    文摘:就貼壁澆注的端面燃燒發動機容易產生的起動加速慢、工作拖尾時間長及尾端部人工脫粘層（蓋層）粘接脫粘等技術問題進行了分析，提出了適用的解決辦法，這些方法已被實踐證明是有效的，對提高發動機性能非常重要。
  19. During stage i, the macro - stiffness of mmcs is reducing because of interfacial debonding

    當存在漸進適應界面時，復合材料橫向拉伸應力?應變曲線存在三個階段。
  20. First, the one - dimension load transfer model presented by cox was studied in details. based on the ideal interface bonding load transfer model, a fibre fracture criterion and an interface debonding criterion were established in terms of fracture mechanics, which bettered the interphase load transfer model. this model could also describe the process of single - fiber composites fragmentation

    首先，本文充分研究了cox一維界面載荷傳遞模型，在完美界面粘結載荷傳遞模型的基礎上根據斷裂力學觀點建立了纖維斷裂判據和界面脫粘判據，完善了界面載荷傳遞模型，以該模型為基礎較好地描述了單纖維復合材料拉伸實驗過程。