decarburization 中文意思是什麼
decarburization
解釋
鋼鐵脫碳作用-
Specifically for the iron and steel industry during the past 15 years, thermo electron has installed over 100 mass spectrometers for gas analysis applications involving the following plants : coke ovens, blast furnace ( bf ), direct reduction iron ( dri ), basic oxygen furnace ( bof ), electric arc furnace ( eaf ), argon oxygen decarburization ( aod ) furnace, vacuum oxygen decarburization vod furnace and ruhrstahl - hausen ( rh ) furnace
尤其在過去15年的鋼鐵行業中，超過100臺過程質譜儀用於氣體分析，包含：焦爐，高爐，直接還原煉鐵爐，氧氣頂吹轉爐，電弧爐，氬氧脫碳轉爐，真空氧氣脫碳爐和循環法真空脫碳爐。 -
An activity decarburization model in rh vacuum refining
處理過程的脫碳動態模型 -
The fatigue fracture occurred in the root of the screw where defects such as decarburization and cracks existed, and these defects made the zone to be a stress concentration area and caused the bolts to break finally
疲勞裂紋的形成是由於螺紋牙底存在脫碳和折疊裂紋等缺陷，這些缺陷的存在使該材料產生了較大的應力集中，從而導致螺栓開裂失效。 -
Fasteners, decarburization in hardened and tempered threaded
淬硬及回火螺紋緊固件的脫碳 -
An analysis of heavy rails ' decarburization
重軌鋼脫碳的研究 -
Determination of depth of decarburization of steel
鋼的脫碳層深度測定法 -
Steels - determination of depth of decarburization
鋼.脫碳層深度的測定 -
Aod argon - oxygen decarburization
氬氧脫碳 -
Standard test method for determining decarburization and carburization in hardened and tempered threaded steel bolts, screws and studs
淬火和回火的螺紋鋼螺栓螺母和螺柱的脫碳和滲碳性測定的標準試驗方法 -
Abstract : according to the character and actual condition of rh in shanghai baogang, molten steel flow in ladle and its effect on decarburization were studied with a three dimension turbulent flow and concentration modelling. the results show that, within a certain range, the decarburization rate increases not only with the increase of snorkel diameter and ar fluid flow but also with the decrease of the immersed depth of the snorkel
文摘:根據上海寶鋼rh的特點和實際情況，建立了三維流場、濃度場程序，對鋼包內鋼水的流動、處理過程的脫碳進行了研究，並對它們的影響因素進行了分析.結果表明，在一定范圍內增加循環管直徑和吹氣流量、減小浸漬管浸入深度有助於提高脫碳速度 -
Test methods for estimating the depth of decarburization of steel specimens
估計鋼樣品脫碳深度的試驗方法 -
For grade 1, no complete decarburization shall be present. the depth of partial decarburization at any point on the periphery shall not exceed the value in table 1
對于等級1 ，沒有完整的脫碳。外圍任何點的部分脫碳深度不得超過表1中的數值。 -
Standard test method for determining decarburization and carburization in hardened and tempered threaded steel bolts, screws and studs metric
淬火和回火的螺紋鋼螺栓螺釘和螺柱的脫碳和滲碳性測定的標準試驗方法 -
Decarburization in hardened and tempered metric threaded fasteners
淬火和回火米制螺紋緊固件的脫碳 -
The effect of oxidation and decarburization on examining grain size of austenite with oxidizing method
氧化和脫碳對用氧化法檢驗鋼的奧氏體晶粒度的影響 -
Induction heat oil tempered wire and rod can be directly used in the manufacture of spring and pusher and the quenching - tempering process thereafter can be omitted, thus the quality problems such as deformation of workpiece, decarburization, un - stability and un - qualification of mechanical property can be avoided and the quality stability and reliability of product can be improved
感應加熱油淬火-回火鋼絲及線材，能直接用於繞簧和製造推桿，可省去一般材料繞簧和推桿加工成形后的淬火-回火工序，避免了由此帶來的工件變形脫碳及力學性能不穩定甚至不合要求等質量問題，提高了產品的質量穩定性和可靠性。
分享友人