The method of obtaining high concentration of na2feo4 solution by quick electrolysis mainly contains four aspects : adoption of either a diaphragm or an ionic membrane electrolytic cell in which a thin anodic cell lying between the two cathodes, ( 2 ) using an iron anode that has larger specific surface area, ( 3 ) keeping suitable concentration of naoh in the anodic cell, adoption of lower current density and higher electrolyzing speed. the practical technique parameters follow a s below : the naoh solution of 14 - 16mol / l, the temperature of 303 - 308k, the surface anodic current density of 300a / m2, the unit electrolyzing speed of efficiency larger than 6. 0a / l
快速電解獲取高濃度na _ 2feo _ 4溶液的方法，主要包括四個方面：採用兩陰極室夾一厚度較小的陽極室的隔膜（或離子膜）電解槽；使用比表面積較大的鐵網陽極；保持陽極室中有適宜濃度的濃naoh溶液；採用較低的電流密度和較高的電解速度。具體工藝參數是： 14 16mol / lnaoh溶液、溫度303 308k 、表觀陽極電流密度300a m ~ 2 、有效單位電解速度6 . 0a / l 。 -
As for the method of preparing solid potassium ferrate from electrolytic synthesis of sodium ferrate solution, it is compared that the effects of the main procession facts of electrolysis upon both the anodic current efficiency and the relative concentration of na2feo4. one method was put forward to obtain high concentration of na2pe04 in the high concentration of alkaline by quick electrolyzing iron anode
針對由電解法合成na _ 2feo _ 4溶液進而制備固態k _ 2feo _ 4的方法，通過比較研究電解過程中主要工藝因素對陽極電流效率和相應na _ 2feo _ 4濃度的影響，提出了在濃堿液中快速電解鐵源陽極獲取高濃度na _ 2feo _ 4溶液的方法。 -
Detail specification for fixed tantalum electrolytic capacitors - porous anode, polar non - solid electrolyte - tubular insulated metallic case, ptfe elastomer seal, axial wire terminations - full plus additional assessment level
固定式鉭介質電容器詳細規范.極性非固體介質多孔陽極.軸向引線終端ptfe彈性密封管狀絕緣金屬殼.全面附加評定級 -
Electroplating : the electrochemical deposition of reduced metal ions from an electrolytic solution onto the cathode by applying a dc current through the electrolytic solution between two electrodes, cathode and anode, respectively
電鍍：在電解質溶液中的兩個電極，陰極和陽極之間施加直流電，使電解質溶液中的金屬離子還原沉積在陰極上的電化學沉積過程。 -
Lucky tcl is contributed in the import & export businesses of anode paste, carbon materials and factory equipments of electrolytic aluminum, aluminium ingot, aluminium semi - product and other non - ferrous metal
正彩有限公司是專業從事有色金屬等出口貿易，其北京代表處成立於2000年。 -
Respectively proceeding with bromine complexing agent of anode, modified membrane and electrolytic additive of cathode, mainly referring to specific power of battery, ratio of self - discharge and zinc dendrite, this paper has studied the influences of different anode additive and modified membrane on specific energy of battery by means of charge and discharge curves, and the influences of electrolytic additive ( nh4 +, op - 10, tx - 10 and dodecyl trimethyl ammonium bromide ) on zinc dendrite by means of current - time curve and microscopic morphology observation
本文分別從正極溴絡合劑、隔膜改性和負極的電解液添加劑入手，以電池的比能量、自放電率以及鋅枝晶生長情況為主要的性能指標，用電池充放電曲線等方法研究不同正極添加劑和隔膜改性對電池比能量的影響；用電流-時間曲線以及微觀形貌觀察等方法研究電解液添加劑（ nh _ 4 ~ + 、 op - 10 、 tx - 10以及十二烷基三甲基溴化銨）對鋅枝晶生長的影響。
分享友人