eutectic phases 中文意思是什麼
-
Following these two examples of two and three phases, regarding ternary and quarternary metallic melts involving eutectic as melts consisting of three and four non - homogeneuos solutions correspondingly, and using thermo - dynamic parameters of binary metallic melts involving eutectic, calculating models of mass action concentrations for ternary symmetrical melts formed from similar metastable compounds, ternary unsymmetrical melts formed from unsimilar metastable compounds and quarternary metallic melts involving eutectic have been formulated
仿照這兩個二、三相熔體的例子，將含共晶體三、四元金屬熔體看作由3 ， 4個溶液組成的非均相熔體，並利用含共晶體二元金屬熔體的有關熱力學參數，針對由同類亞穩態化合物組成的對稱型三元系、不同類型亞穩態化合物組成的非對稱型三元系及四元系含共晶體金屬熔體，制定了相應的作用濃度計算模型。 -
The result indicated that the two phases in eutectic had difficulty in growing regularly on condition that the floating zone melting rate was in the scope of 0 ~ 0. 3mm / min. the matrix phase was directional grown and the other phase was grown with no order
結果表明，在區熔速率r = 0 0 . 3mm min范圍內兩相很難形成規則共晶，其中基體相定向生長，第二相混亂生長，彌散分佈於基體中。