The results showed that : there were five stages in the rising process of the internal temperature of untreated, fire - retardant solution soaked, and fire - proof paint coated wood during the fire ; the carbonization rate of wood decreased by 21. 1 % ~ 35. 6 % and the rising speed of internal temperature also declined greatly when wood was soaked in fire - retardant solution or coated with fireproof paint ; the carbonization rate of white pine was 8. 5 % ~ 17. 4 % higher than that of the northeast china ash ; for untreated wood, the carbonization rate in tangential direction was 5. 8 % ~ 10. 5 % higher than that in radial direction ; the internal temperature of wood varies with the developing direction of combustion
結果表明:火災發生過程中未處理木材、阻燃浸漬處理和塗刷防火徐料木材內部溫度上升過程出現5個階段;經過阻燃浸漬處理和塗刷防火塗料后,木材的燃燒炭化速度降低了21 . 1 % ~ 35 . 6 % ,內部溫度上升速度大幅度下降;白皮松木材的燃燒炭化速度比水曲柳木材的燃燒炭化速度快8 . 5 % ~ 17 . 4 % ;未處理木材沿弦向的燃燒炭化速度比徑向快5 . 8 % ~ 10 . 5 % ;木材內部的溫度變化沿燃燒推進方向不同而不同。 -
In order to make clear the regulation of the combustion and the heat - transport process of fire - retardant treated wood, the combustion of untreated, fire - retardant solution soaked, and fire - proof paint coated white pine ( pinus bungeana ) and northeast china ash ( fraxinus mandshurica ) wood as well as the rising process of temperature at different sites in wood were measured in this study, taking a multi - function fire - proof experiment oven to simulate the typical process of fire
摘要為了弄清楚阻燃處理木材的燃燒及其熱傳導規律,該研究採用多功能耐火實驗爐模擬典型火災的發生過程,測定了未處理、阻燃劑水溶液浸漬處理、塗刷防火塗料白皮松和水曲柳木材的燃燒及木材內不同位置的升溫過程。 -
Bpfld - x is a range of flat absorbers consisting of a single of polyurethane foam with a dielectric carbon solution, a binder and a fire retardant
型吸波材料是一種平板狀的聚氨酯泡沫吸波材料,採用優質聚氨酯泡沫經過浸碳工藝生產而生,具有良好的電磁波吸收性能及防火性能。