The lcf behavior of a recrystallized zircaloy - 4 plate at room temperature and 400 show that alloy has better lcf property at rt than at 400, and cyclic hardening at 400 which could be attributed to the dynamic strain aging effects. it is noticeable that the hydrided plate has the same cyclic behavior as the above unhydrided sample at room temperature
在400下，合金錶現出與常溫下不同的循環特性，其循環穩定滯后回線出現鋸齒狀波形，且在整個疲勞過摘要程中呈現出一致循環硬化的現象，這主要是因為合金在400下發生動態應變時效效應的結果。 -
It can be noticed that both r and t specimens show initial hardening and subsequent softening at the strain amplitude higher than 0. 8 % and cyclic softening from the beginning to fracture under strain amplitude less than 0. 8 % at room temperature, and the cyclic flow stress was always lower in r specimen than in t specimen at the same strain range
且在相同的應變幅下， t向試樣比r向試樣具有更高的循環流變應力。此外，對r向及t向試樣，低應變幅下呈現出循環軟化現象是因為晶粒旋轉導致循環軟化；而在高應變幅下發生循環硬化是由於孿晶作用的結果。 -
The rupture mode of the composite at room and elevated temperature depends upon the work - hardening characteristics of the nickel alloy matrix
復合材料常溫和高溫的拉伸斷裂模式與基體相的形變強化特性有關。 -
For the cyclic deformation under a given strain at room temperature, cyclic softening is usually displayed till to failure in the lower range of strain ; however, cyclic hardening is displayed in the early stage in the higher range of strain, subsequent cyclic softening in the later stage and till to failure
對于室溫下恆應變幅的循環變形，在應變幅較低時表現為循環軟化直至疲勞破壞;在應變幅較高時，循環變形的初期為循環硬化，隨后是循環軟化直至疲勞破壞。