impact ductility 中文意思是什麼
impact ductility
解釋
沖擊韌性-
The strength of extension of low carbon ductile cast iron can reach 750mpa in casting state, the impact ductility can reach 20j / cm2. the diameter of graphite nodule is 5 - 20 ( am, the base body is consisted of pearlite -
低碳球鐵在鑄態下的抗拉強度可達750mpa ，沖擊韌性可達20j cm ~ 2 ，其中石墨球直徑在5 20 m ，基體以珠光體為主，有少量的鐵素體與滲碳體。 -
It ' s the advantage of jmfc to apply the centrifugal casting technology to the small size of compound rolls, which characteristics are as follows : combining high hardness, anti - wear, impact and breakage resistance : spun cast the shell by proper charging of alloys and use high strength and impact ductility material as core
將離心澆鑄工藝用於小型復合軋輥的製造，是金環廠的優勢，採用該工藝的軋輥具有以下特點：兼得高硬度耐磨損與抗沖擊抗斷裂性能：按耐磨性和硬度要求，將合金科學配比，溶解澆鑄成輥身的工作層，再採用高強度抗沖擊的材料澆鑄輥頸和輥芯，冶金結合，兩者兼得。 -
Simultaneity, through contrast analysis validate that antiseimic capacity of expansion web is better than that of steel web. therefore, based on the experiences summed up by precedence, the formulation for calculating the crack load and limit load of brick masonry house reinforced by expansion web is advanced, which provides project reference. based on the analysis and studies of masonry shearing strength, test of prestressed single brick masonry wall, and test of prestressed brick masonry house models, and ect, the article has carried through several aspect research as below : 1. a series of experiment on material capability of expansion web, including intensity of single thread and expansion web, ect ; 2. research on influence of loading and destroy of masonry brick building reinforced by expansion web under lowcyclic loading ; 3. study of impact of expansion web on ductility, energy dissipation, intensity, ect under the same situation as above ; 4. put forward computation formulation of masonry brick building reinforced by expansion web
本著以上的研究目的，本文在分析和借鑒前人砌體抗剪強度理論、預應力單片墻試驗研究、預應力模型抗震性能試驗研究等基礎上，進行了以下幾方面的研究工作: 1 .作為一種新型結構材料擴張網，進行了一系列的材性試驗（單絲強度、網片強度和在砂漿中被約束條件下的網片強度及其相應的彈性模量） ； 2 .研究了水平荷載往復作用（低周交變）下，普通鋼絲網和擴張網砂漿對砌體結構抗裂及承載能力和破壞形態的影響，並將這兩種材料的加固效果進行了對比； 3 .上述狀態下，兩種網片水泥砂漿對砌體結構變形、延性、耗能、剛度退化等抗震性能的影響及其影響效果的比較； 4 .提出擴張網水泥砂漿加固砌體結構的抗剪強度計算建議公式。 -
The results show that, with the quenching temperature ( 270 ~ 380 ) increasing, the carbon content and percentage content of retained austenite increase first and then decrease, which are up to a maximum value at 360 ; the tensile strength of adi decreases ; the elongation and impact ductility of adi increase first and then decrease, which are up to a maximum value at 360 ; but the hardness of adi decreases first and then increases, which is up to a minimum value at 360
結果表明，在試驗溫度范圍內（ 270 ~ 380 ） ，試樣中殘余奧氏體的含碳量及其含量隨著等溫淬火溫度的升高先增大后減小，均在360等溫淬火時出現最大值；抗拉強度隨著等溫淬火溫度的升高而逐漸降低；伸長率和沖擊韌度隨著等溫淬火溫度的升高先增大后減小，在360等溫淬火時出現最大值；硬度則隨著等溫淬火溫度的升高先減小后增大，當360溫淬火時硬度最低。 -
( 2 ) the tensile, bend and impact ductility experiment of the resin cast with fsmf filler are employed
（ 2 ）進行了fsmf填充樹脂澆鑄體的拉伸、彎曲和沖擊韌性實驗。 -
Which has high strength, good ductility, impact bearing, erode - bearing, besides, its linear expanding coefficient is almost equivalent to concrete, and it has excellent performance - price ratio etc. this paper is related to 8 rc - poles wrapped by gfrp ( sgfw430 ) and rc - poles are compressed axially, in order to analyze the influence of different stick layer over the pole ' s work performance and the influence between three type axial compress ratio ( 0, 0. 8, 1. 1 ) with one layer gfrp with the contrast poles about limit load - bearing capability, failure state, ductility, section stiffness, restrict losing owing to stress - difference
其具有強度高，延性好；抗沖擊、耐腐蝕；線膨脹系數與混凝土接近；性能價格比高等多個特點。本文通過8根外包單向gfrp （ sgfw430 ）的rc組合柱，以及混凝土對比柱在軸心荷載作用下的試驗為基礎，具體詳細地分析柱子在粘貼不同層數的高性能玻璃纖維和在不同的軸壓比（ 0 、 0 . 8 、 1 . 1 ）下粘貼一層的高性能玻璃纖維后混凝土組合柱相對對比柱在極限承載能力、破壞形態、延性、截面剛度、應力差帶來的約束損失等方面的變化情況。