in-situ coating 中文意思是什麼
in-situ coating
解釋
現場塗敷-
90 % uv below 400nm could be shielded by the nano - sio2 sol. the time of the artificial aging of nano - sio2 - modified coatings prepared by the way of in - situ dispersion method was about twice as long as that of the nano - sio2 - modified coatings prepared by dispersing the nano - sio2 powder in the coating directly. on the other hand, the fadeproof time ( reaching the second level of color aberration ) of the nano - sio2 - modified coatings was 1. 83 times as long as that of the national standard for the super coatings
實驗證明:納米510 :溶膠具有很強的紫外散射屏蔽性能，對400nm以下的紫外光能屏蔽90 %以上;在位分散法納米510 :改性塗料的耐人工老化粉化時間比直接分散法納米510 :改性塗料提高了近1倍，耐變色時間（達到色差2級的時間）是國標優等品要求的1 . 83倍，較相應的未改性塗料提高了約25 % 。 -
This part emphasizes the synthesis of nanoarrays, aiming at controlling the size and distance of nanocrystallites using calixarene derivatives by altering the size, length and chemical structure of the organic molecules ; 2. this part emphasizes in situ synthesis strategy for fabrication of polymer network of zns based nanopowder, aiming at size controls, coating and preventing agglomeration following " one - pot " synthesis ; this method fits to low cost, large scale production ; 3. according to development in zno nanomaterials, we first report on the synthesis, characterization of amorphous zno, aiming at describing the principles and approaches of synthesis techniques, optical properties, spatial structure and doped effect ; the amorphous zno displays cage - like structure, showing a strong ultraviolet emission while the visible emission is nearly fully quenched, a potential uv - emission material ; 4
本論文以量子結構自組裝為出發點，提出利用杯芳烴及其衍生物的化學受限反應實現尺寸可調半導體納米粒子自組裝；提出有機聚合網路原位組裝zns基納米熒光粉方法，把熒光粉的納米化、包敷、防團聚在「一鍋」反應中完成，適于低成本，批量生產；根據當前zno的研究情況，我們首次合成了非晶zno ，研究了它的光學性質，確定了它的結構，並對其摻雜進行了初步的研究，非晶zno表現出強的深紫外發光特性，而可見發射非常弱，是一種有巨大潛在應用價值的深紫外發光材料；利用非晶zno的亞穩特性，對晶化過程中非晶zno納米晶zno三維受限量子結構特性，界面特性進行了深入的研究；利用固相熱分解一般受擴散控制特性，實現了尺寸可控的zno三維量子結構的自組裝；利用非晶zno的高度分散性，容易均勻成膜特性，實現了非晶籽晶誘導低溫液相外延自組裝生長高取向zno晶體薄膜。 -
Self - reaction in - situ synthesis of tic fenicr composite coating in centrifugal field
復合材料塗層的原位反應合成