  1. Nonpolar polypropylene has bad compatibility with mmt even after organic modification to mmt. so polypropylene ( pp ) grafting acrylic acid was produced by the suspension grafting method as compatilizer. as pp / mmt nanocomposites prepared from htab modified mmt as concerned, the interlayer spacing of mmt is 4. 61nm, 4. 2nm and 4. 09nm respectively when the mmt content is 1 %, 2 % and 3 %. so, the abtained nanocomposites has intercalated structure

    當土含量為2 ，相容劑用量為15時力學性能最好，缺口沖擊強度和拉伸強度分別達到16 . 45kj m ~ 2和35 . 77mpa ，分別比純pp增加了280和4 . 3 ，蒙脫土的加入起到了增韌和增強的雙重作用。
  2. The result shows that dmso were intercalated into the interlayer of kaolinite and basal spacing was swelled from 0. 715nm to 1. 110nm, so the kaolinite - organic matter intercalation compound was formed

    結果表明，二甲基亞碸進入了高嶺土的層間，層間距由0 . 715nm增加到1 . 110nm ，形成高嶺土有機插層材料。
  3. The content of pema affects on interplanar distance of pe / mmt composite. the content of pema increases as the interplanar distance, barrier properties and melting point of composites increased, when the critical content of pema ( wpema = 30 % ) could get exfoliated composites. the interlayer spacing of pe / mmt composites depends on content of mmt, but not the content of mmt increases as the interlayer spacing increases

    同時用x射線衍射（ xrd ）衍射實驗、紅外光譜（ ir ）實驗、差熱分析試驗（ dta ） 、力學性能測試等手段，研究了採用不同的相容劑改善聚乙烯與蒙脫土之間的相容性的情況；相容劑的用量對聚乙烯/蒙脫土復合材料層間距、性能的影響；蒙脫土的含量對pe / mmt對復合體系的層間距影響；以及工藝條件對復合體系的層間距和性能的影響。
  4. Exfloited nanocomposites were successfully synthesized. the study of melting compound about pet eva abs pvc cpe and montmorillonite has been carried out. we abtained several intercalated nanocomposites, tem shows the interlayer spacing is no more than 100nm

    首次對pet 、 eva 、 abs 、 pvc 、 cpe 、 pp與蒙脫土熔融復合進行了研究，制得多種插層型納米復合材料， tem照片顯示：多數粘土片層的厚度在100nm以內。
  5. Montmorillonite ( mmt ) clay is an important class of lamellar inorganic compounds, contains negatively charged layered silicates, which are bonded with metal cations such as na + or ca2 + by ionic bonding. whose interlayer spacing can be modified by cation exchange. when the mmt is exchanged with cations, its inner layer spacing becomes large enough to be penetrated by a monomer

    蒙脫土（ montmorillonite ， mmt ）是一種天然礦物，具有層狀結構，層間靠吸附陽離子如na ~ + 、 ca ~ （ 2 + ） 、 mg ~ （ 2 + ）等來維持電荷平衡，這些離子可與其它陽離子進行交換，使有機單體分子進入層間，聚合后即可形成有機無機納米復合材料。
  6. In this thesis, intercalated polypropylene / montmorillonie nanocomposite was prepared by melt intercalation and exfoliated aa - co - am / montmorillonite nanocomposite was prepared by in - situ copolymerization. htab was used to modify na - montmorillonite ( na - mmt ) and the interlayer spacing of mmt increased from 1. 2 nm to 3. 84nm. in addition, water - soluble monomer was used to in - situ polymerize in the suspension of montmorillonite and exfoliated organic mmt was preprared

    以htab為插層劑得到的聚丙烯蒙脫土納米復合材料中，當土含量為1 ， 2 ， 3時，復合材料中蒙脫土的層間距分別為4 . 61nm ， 4 . 2nm和4 . 09nm 。
  7. But the presence of al iron was helpful to incorporate fe iron into interlayer of montmorillonites. introducing zr helped al - plms getting better larger spacing, thermal stability, surface area and pore volumes

    實驗採用ticl _ 4 、無水乙醇、丙三醇為原料制得鈦柱撐蒙脫石，其層間距為19 . 78 （