latex particles 中文意思是什麼
-
The size and distribution of polyacrylate / caco3 latex and composite particles were determined by dynamic laser scattering. the morphological structures of latex particles were investigated through tem
藉助動態光散射粒徑分析儀、 tem分別考察了acr膠乳和復合膠乳粒徑及其分佈、乳膠粒的微觀形態結構。 -
Preparation and characterization of mc pmma core - shell composite latex particles
殼復合膠粒的制備與表徵 -
The results showed that the rubber latex particles separated the clay into nanometer units, accompanied with the competition between separation of rubber latex particles and re - aggregation of single silicate layers upon addition of flocculant during the process of co - coagulating, while the intercalation of rubber molecules into clay galleries did not occur
結果表明，在加入絮凝劑使橡膠乳液黏土水懸浮液共凝聚的過程中，由於存在膠乳粒子對黏土片層的隔離作用與在混合液中分散的黏土單片層的重新聚集作用的競爭，因此，在絮凝物中，橡膠大分子將黏土片層隔離成納米分散單元（包括單片層和多片層的聚集體） ，在多片層的黏土聚集體層間沒有橡膠大分子插入。 -
The size distribution of composite latex particles is similar to that of polyacrylate / caco3 latex. their mean particle diameters gradually decrease with amount of polyacrylate / caco3 latex and caco3 / monomers increasing, but the mean particle diameters of the composite latex are much bigger than particle diameters of caco3 latex. molecular weight of pvc composite resin was determined by viscometer
結果表明：復合膠乳呈現與種子粒徑相近的單峰分佈，其平均粒徑隨聚丙烯酸酯caco _ 3種子膠乳中caco _ 3加入量的增加而逐漸減小，但復合乳膠粒徑比種子粒徑要大很多；用粘度法測定了復合樹脂中pvc的粘均分子量。 -
The infrared spectroscopy, transmission electron microscopy, light scattering and x - ray photoelectron spectroscopy are used to characterize the polymer structure and the morphology of the latex particles. the results demonstrate that composite latex with core / shell morphology is indeed successfully prepared
利用紅外光譜、透射電鏡、激光粒度儀、表面能譜分析等手段對聚合產物的化學結構及乳膠粒粒子形態進行了表徵。 -
Moreover, template can be pre - designed according to the size and shape of objective materials. microgels are cross - linked latex particles with narrow size distribution and the inherent steric stability
微凝膠是一種交聯型的膠乳粒子，它具有較窄的尺寸分佈和空間位阻作用。 -
Composite latex particles of disproportionated - rosin ( dpr ) and polyacrylates were synthesized by miniemulsion polymerization
摘要通過細乳液聚合方法成功制備了歧化松香丙烯酸酯復合高分子乳液。 -
The particle size of pba latex particles is in the range of 40 - 100 nm, as measured by tem observation, suggesting that ultrasonic irradiation offers a new route to the preparation of mini - or micro - emulsion polymerization
Pba乳膠粒尺寸范圍為40 - 100nm ，表明超聲輻照提供了一種新的用於制備聚合物納米粒子的細乳或微乳液聚合技術。