In this paper, in order to study the influence of electrolyte to the lithium - ion battery performance, we assembled the lithium - ion battery using the different electrode material ( limn _ 2o _ 4, licoo _ 2 and natural graphite ) and the electrolytes which were mainly composed of lipf _ 6 as the electrolyte lithium salt and the different solvents ( including additives ) which were mixed according to the certain proportion

本論文主要以lipf _ 6為電解質鋰鹽，採用不同溶劑（添加劑）按一定比例混合，對有機電解液進行優化，與不同的電極材料（ limn _ 2o _ 4 、 licoo _ 2或天然石墨）組裝成電池，研究電解液對鋰離子電池性能的影響。

By hot pressing, the licoo _ 2 target was produced. different moulds were used in the hot pressing including the graphite mould and the sic mould

在熱壓法制備licoo _ 2靶材的過程中，使用了石墨模具，碳化硅模具。

In this article, by rf sputtering the licoo _ 2 film was produced. by hot pressing and cold pressing ( and sintering ), the licoo _ 2 targets used in the rf sputtering were produced differently. both technics of the preparation of the licoo _ 2 film and the licoo _ 2 target were studied

本文使用熱壓燒結方法和冷壓后燒結方法制備了磁控濺射用的licoo _ 2靶材，並使用磁控濺射方法制備了licoo _ 2薄膜，對兩者的制備工藝進行了研究。

While adding 1 % binder the preferable target was produced, and the density was 4. 89g. cm - 3, which was 88 % of the theoretic density of the licoo _ 2 with ar as the sputtering gas, the technics of rf sputtering to produce the licoo _ 2 film were studied systematically

在冷壓燒結方法制備licoo _ 2靶材的過程中，燒結前添加了不同量粘結劑，就綜合純度和粘結性能兩方面考慮，加入1 %的粘結劑較為理想。所制備的licoo _ 2靶材密度為4 . 89g / cm3 ，達到licoo _ 2理論密度的88 % 。

The density of this target was 5. 21 g / cm3, which was 94 % of the theoretic density of the licoo _ 2 。 in cold pressing and sintering process different percentage of binder were added to the target and the best percentage was found

其中使用碳化硅模具，制備出純度和密度較高的熱壓靶材，靶材密度為5 . 21g / cm3 ，達到licoo _ 2理論密度的94 % 。

For films thinner than 1 m, the preferred orientation was ( 101 ) and ( 104 ) plane while the sputtering gas was ar only, and the preferred orientation was ( 003 ) plane while the sputtering gas was ar and o2 mixing. this is because of the excessive o in the licoo _ 2 film produced by the ar / o2 r. f

當薄膜厚度在1 m左右時，以ar 、 o _ 2混合氣氛為濺射氣氛，薄膜中晶體生長的優選晶向為（ 003 ）晶面群方向;以ar氣為濺射氣氛，薄膜中晶體生長的優選晶向為（ 104 ） 、 （ 101 ）晶面群方向。

The key part of this battery is the licoo _ 2 film as the cathode film, which has high voltage stage, high energy density, and stable charge / discharge ability

薄膜鋰電池是具有廣泛應用前景的一種二次電池， licoo _ 2是被研究最多的一種正極材料。

The influence of thickness, kinds of rf sputtering gas, flux of gas, and gas pressure to the produced licoo _ 2 film was studied, which affected the preferable orientation of the crystal

研究了厚度、濺射氣氛、氣體流量、氣壓值等對制備licoo _ 2薄膜中晶體生長擇優取向的影響。

By comparing the xrd charts of licoo _ 2 films produced with different ratio of ar / o2, the preferable ratio was determined, which was 3 / 1. with ar / o _ 2 ( 3 / 1 ) as the sputtering gas, the technics of rf sputtering to produce the licoo _ 2 film were studied systematically. the best conditions to produce the licoo _ 2 film were that the power of rf sputtering was 75w, the flux of ar / o2 was 28sccm, and the pressure was 15mtorr

通過對不同ar 、 o2混合氣的比率濺射得到的樣品xrd譜圖比較，確定了濺射licoo _ 2薄膜時的最佳ar / o2配比，並通過正交實驗確定了濺射氣氛為ar / o2混合氣且配比為3 / 1時濺射licoo _ 2薄膜的最佳工藝條件:濺射功率為75w 、氣體流量為28sccm 、氣壓值為15mtorr 。