Owing to the abundant output and broad applications of poiyolefine, pls nanocomposites based on poiyolefine have become an enormous commercial allure. the studies on the melt compounding of polymer / compatibilizer - layered silicates system and their structure and properties were carried out
提出聚合物粘土（ pls ）納米復合材料的阻隔幾何模型，推導出適合pls納米復合材料體系的相對透氣性公式，並探討影響透氣性的各種因素。 -
Preparation, structure and properties of hdpe ~ g ~ aa / mmt nanocomposites melt grafting reaction of hdpe with aa was performed in thermohaake rheomix and hdpe - g - aa with high grafting degree and high grafting efficiency was prepared. the change of torque indicated that the graft copolymerization was existed during melt compounding. the extent of grafting was analyzed by ftir and element analysis
在hdpe中只加過氧化二異丙苯（ dcp ）時，由於發生交聯反應而使平衡扭矩明顯增加，熔點和結晶度降低，加入aa后， aa與hdpe的接枝和hdpe自身的交聯並存，前者對後者有抑制作用，從而使扭矩下降，熔點和結晶度部分恢復。 -
However, when aa content exceeded 10wt. - %, the increment of the extent of grafting level off and the grafting efficiency decreased remarkably. afterward hdpe - g - aa / mmt composites and hdpe / mmt composites were prepared via melt compounding
然後用十八烷基季胺鹽處理過的鈉基蒙脫土（ mmt ）分別與hdpe以及hdpe - g - aa熔融插層后制備了兩種復合材料。 -
Moreover when aa content exceeded 10wt. - %, the increment of the extent of grafting level off and the grafting efficiency decreased remarkably. then hdpe - g - ydh151 / mmt composites and hdpe / mmt composites were prepared via melt compounding. ftir proved that there were interactions between ydh151 and mmt sheets
接著用十八烷基季胺鹽處理過的鈉基蒙脫土分別與hdpe以及兩種hdpe一物h151熔融插層后制備了三種復合材料，研究了mmt和ydh151間的相互作用對分散和性能的影響。 -
In this paper, high density polyethylene / bentonite nanocomposites were prepared by simple melt compounding, their structures were demonstrated with x - ray diffraction, ft - ir spectra and dta. it was proved that the molecular chain of pe could be intercalated in layered silicate of organobentonite ， the intercalation nanocomposites were obtained
本文採用簡單熔融插層復合法制備高密度聚乙烯/膨潤土納米復合材料，用x -射線衍射、紅外光譜和差熱分析等手段表徵了復合材料的結構，證實聚乙烯分子鏈確已進入有機膨潤土的硅酸鹽片層間，形成插層型納米復合材料。