melting capacity
解釋
熔化率-
And through the comprehensive comparisions, along with the dsc analysis of different pcms, it was determined to select the stearic acid ( c18h36o2 ) as the pcm in this paper, provided by beijing chemical reagent company. the stearic acid has an ideal melting point and attractive thermal capacity. all these properties make it an attractive candidate as a potential pcm for heat storage in mid - temperature lhtes systems
並在對多種相變材料做全面比較以及dsc分析的基礎上，確定選用北京化學試劑公司提供的硬脂酸（ c18h36o2 ）作為本文的相變材料（ pcm ） ，其熔點（相變溫度）適中，相變潛熱較大，這些特性使其成為一種中常溫相變儲熱裝置中理想的相變儲熱介質。 -
The results showed the thermal energy for the melting of the extrudate came from the rotating shearing sets, the stronger the shearing force, the more the thermal energy ; when the extrudate was different, the screw - thread sets should also be different, and the processing technology should also be different, too ; the production capacity of the extruder was linear to the screw - thread sets and revolution
研究結果表明，物料的熔融熱能來自於轉動的剪切組合；螺紋組合的剪切能力越強，所產生的熱量也越大；不同的物料需選用不同的螺紋組合，並配以不同的工藝條件；雙螺桿擠出機的產能與螺桿的組合及轉速存在線性關系。 -
While testing ofeis at different depth of dischargeand charge - discharge at different charge - discharge rate reveale that, these material indicate lower conductivity at highcharge - discharge rate, resulting in bad electrochemical perforemence. melting - cooling and inorganic sol - gel were adopted, which facility - simpleand operating - easy, to prepare v _ 2o _ 5 xeroxes as positive material of li - ion battery. the comparision of structual and electrochemical performance between thesecathode materials were investigated for the first time. their electrochemicalbehaviorswerestudiedbygalvanostaticcharge - discharge, cyclicvoltammetry ( cv ), and electrochemical impedance spectroscopy ( eis ) techniques. the results indicte the sample that prepared by melting - cooling revealed moreexcellent performance at low charge - discharge rate, which achieved a high initialdischarge specific capacity of approximate 320 mah ? g - 1
通過各種充放電測試，循環伏安（ cv ）曲線以及電化學阻抗譜（ eis ）等測試手段對材料的電化學性能進行表徵，結果發現，在低倍率放電下，熔融淬冷法合成的材料具有更好的電化學性能， 0 . 1c恆流放電至1 . 8v時首次放電容量達320mah ? g - 1 ，並且發現， v _ 2o _ 5作為正極材料組裝成的鋰離子二次電池，除首次循環具有較大的不可逆容量外，其餘循環可逆且容量保持能力較好， 20次循環后，容量只衰減了6 . 40 % 。 -
Based on the melting experiments of pp powder in twin - screw extruder, the melting capacity of different screw - thread sets and the revolution of the screw was studied
摘要通過對pp粉料在雙螺桿擠出機中的熔融實驗，研究了不同螺紋組合和螺桿轉速對物料的熔融能力。