monomer ratio 中文意思是什麼

monomer ratio 解釋
單體配比
  • monomer : n. 【化學】單體。adj. -ic
  • ratio : n. （pl. ratios）1. 比，比率，比值；比例；系數。2. 【經濟學】復本位制中金銀的法定比價。vt. 1. 用比例方式表達；求出…的比值；使…成比例。2. 將（相片）按比例放大或縮小。
  1. And the adsorbability of this novel adso rbent for ldl was determined. in order to prepare the solid supports in accordance with with the request of adsorbent for ldl, paam beads were synthesized by inverse suspension polymerization. the composition of the polymerization system is shown as follows : the concentration of monomer and dispersant are 12 % and 0. 65 % respectively, the volume ratio of oil / water isl : 3, the mole ratio of aam and mba is 18 : 1

    本文用反相懸浮聚合法合成符合ldl吸附劑載體要求的聚丙烯酰胺微珠，經實驗篩選出反應體系所需的最佳單體濃度（ 12 ） 、最佳分散劑用量（ 0 . 65 ） 、最佳油水比值（ 1 ： 3 ） 、最佳單體（ aam ）與交聯劑（ mba ）的物質的量之比（ 18 ： 1 ） 。
  2. The influence of monomer mass ratio, reaction temperature, reaction time, emulsifying agent content and mixing speed on polycarboxylic acid type waterproofing agent were studied in this article

    本文研究了單體質量比、皂化反應溫度、皂化反應時間、乳化劑摻量、攪拌速度等工藝參數對多元羧酸系防水劑性能的影響。
  3. The different ratio and dosage of composite surfactants were researched about the polymer latex ' s stabilization and structure. afterwards, the emulsion polymerization of tris, mma, and p ( mma - co - ptris ) were carried out. some different monomer ratio copolymer latex and homopolymer latex are prepared by emulsion polymerization used self - made organosilicone monomer - [ tris ( trimethylsiloxy ) silyl ] propylmethacrylate and mma

    用ir ， tem ， dma ，水滴接觸角測試等方法表徵所制備的均聚物和共聚物膜發現：採用有機硅表面活性劑與十二烷基硫酸鈉復配使用，用量在6 8 （相對單體量）可得到粒徑分佈均勻且穩定的均聚和共聚乳液。
  4. Results show that self - crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60 %, and amount of methyl methacrylate is 40 %, and mass ratio of nonionic emulsifier to anionic emulsifer is 3 : 1, and amount of initiator is 0. 6 %, and amount of self - crosslinkable monomer and protective colloid is 2 % and 0. 4 % respectively

    研究結果表明：當丙烯酸丁酯的質量為60 % ，甲基丙烯酸甲酯的質量為40 % ，非離子乳化劑和陰離子乳化劑的質量配比為3 : 1 ，引發劑的質量為0 . 6 % ，自交聯單體的質量為2 % ，保護膠體的質量為0 . 4 %時，可以制備出高彈性自交聯乳液。
  5. Effect of polymeric processes, emulsifier, amount and type of initiators, monomer ratio on processes and properties for emulsion are studied

    討論了聚合工藝，乳化劑及引發劑用量種類，核殼兩階段單體用量比例對乳液聚合工藝和乳液性能的影響。
  6. Monomer reactivity ratio

    單體反應性比率