After looking up a large amount of native and foreign information, the materials used in the experiment were as follows : ptfe base, graphite filler, molybdenum disulfide filler, copper powder filler, carbon fiber and so on. the experimental method is that the formula was designed according to uniform experimental method, the relationship between formula and frictional property was found with spline function and then the representative test points were chosen from fitting curve to make verification test for optimization. the preparative technique of solid lubricant is cold - press sintering method
經過查閱大量國內外文獻資料后確定原料為：聚四氟乙烯樹脂為基體，加入石墨、二硫化鉬、銅粉、碳纖維等填料；試驗方法為：根據均勻試驗方法設計配方，用樣條函數找出配方與摩擦性能的關系，然後在擬合曲線上選取具有代表性的試驗點進行驗證試驗，達到優化的目的；制備工藝：冷壓燒結法制備固體潤滑劑。 -
The results indicated that the dimension, shape and purity of base material could meet the functional demand of solid lubricant ; the thermal decomposition temperature of ptfe resin exceeds 400 c, but organic and inorganic packing filler added in ptfe made the water absorption rate of composite material increased, melting temperature and decomposition temperature decreased, in the meanwhile oxidative decomposition reaction was accompanied ; polar groups such as c = o, c - o - c and so on in the carbon fiber surface is advantageous to increase compatibility with other components and interlayer shearing strength ; uniform design experimental method could help to find the relationship between formula and frictional property by relatively small tests. the developing trend of each formula ' s friction coefficient could be showed by fitting curve ; the friction coefficient with no copper powder or graphite in formula was relatively big. this fact showed that copper powder and graphite should be used cooperatively ; it was found that when the ratio of copper powder to graphite by weight is 15 : 60, 30 : 30 - 40 and 60 : 15 - 30 respectively, the friction coefficient was relatively small. the degree of crystallinity of pure ptfe reached maximum by air cooling and the abrasion loss also reached maximum among three ones ; at the same time, the abrasion loss of solid lubricant sample was also the biggest among three ones ; when solid lubricant matched with 45 # steel axle or gcrl5 steel axle, lubricant transfer film could be formed on metal surface, thus direct contact between the surface of metal friction pair rings was reduced. their working life was elongated extremely ; there was mainly much graphite, a little ptff, moo3, feso4, cus and so on in lubricant transfer film
試驗結果表明：所選原料的尺寸、形狀及純度可滿足固體潤滑劑的性能要求；聚四氟乙烯樹脂熱分解溫度超過400 ，但在ptfe中加入無機填料會使復合材料吸水率提高，熔融溫度及分解溫度降低，且伴有氧化分解反應；碳纖維表面含有c = o及c - o - c等極性基團，有利於提高其與其它組分的相容性，提高層間剪切強度；均勻設計試驗方法能夠用較少的試驗次數找出配方與摩擦性能間的關系，擬合曲線基本能表示各配方的摩擦系數發展趨勢；配方中不加銅粉或不加石墨，其摩擦系數均較高，說明銅粉和石墨應該配合使用；當銅粉15份、石墨60份時，銅粉30份、石墨30 - 40份時，銅粉60 、石墨15 - 30份時，摩擦系數均具有較低值；純聚四氟乙烯樹脂在空氣冷卻時結晶度最大，磨損量也是三者中最大的；同時，固體潤滑劑試樣在空氣冷卻時的磨損量也是三者中最大的：不論是固體潤滑劑與45 #鋼軸配副或是固體潤滑劑鑲嵌入銅套后與gcr15鋼軸配副，在金屬表面均可形成潤滑轉移膜，從而減少金屬摩擦副表面間的直接接觸，大大延長其使用壽命;轉移膜中主要含有較多的石墨、少量聚四氟乙烯、 moo 。 -
Under the condition of distilled water working as lubricant, the weight percentage of cu or cuo powder in composites has less influence on tribological properties of composites
在水潤滑條件下， cu粉或cuo的填料含量對復合材料摩擦和磨損性能影響很小。 -
The results showed that the oil sludge is a kind of viscous black mixture of about 40 % aluminum powder, 60 % rolling lubricant and its oxidate, and the aluminum soap in the surface of aluminum powder plays an important role in accelerating aggregation of aluminum powder, and the oxidation of rolling lubricant is not a negligent factor of producing oil sludge
結果表明，油泥主要由約40 %的鋁屑、 60 %的軋制油及其氧化物組成的粘稠狀黑色混合物；鋁屑表面脂肪酸鋁鹽在促使鋁屑聚集成油泥過程中起著重要作用，軋制油氧化也是生成油泥的一個不可忽視的因素；油泥的生成與軋制油的性能密切相關，軋制油的潤滑性能差、承載能力低、酸值高、抗氧化穩定性能低均可促使油泥的生成。 -
Lubricated metal - powder mixes - determination of lubricant content - modified soxhlet extraction method iso 13944 : 1996 ; german version en iso 13944 : 2006
含潤滑劑的金屬粉末混合物.潤滑劑含量測定.改進的索格 -
Soxhlet lubricated metal - powder mixes - determination of lubricant content - modified soxhlet extraction method
含潤滑劑金屬粉末中潤滑劑含量的測定修正的索格利特 -
Powder metallurgy. lubricated metallic powders. determination of lubricant content by soxhlet extraction method
粉末冶金.潤滑金屬粉末.用索氏提取法測定潤滑劑的含量