pyrolytic graphite 中文意思是什麼
pyrolytic graphite
解釋
高溫分解石墨-
In the surface processing of pyrolytic graphite grid, we had done mainly in completely to clear all kinds of ordures, impurities and grime block which was born in the laser cutting process of the grid
在熱解石墨柵極處理方面，主要為完全清除激光加工過程中產生的各種污物、雜質及垢塊，保證熱解石墨柵極內外表面的清潔度。 -
The problems of insulation resistance between the electrodes is too lower when the filament is on and the ability of bearing high voltage is too lower are rather outstanding and general during designing and manufacturing the tube with pyrolytic graphite grids in xuguang corporation. the technological experiments and the academic discussing which this article did to aim at these problems possess values of using for reference by other type tubes
其中，熱態時極間絕緣低和耐高壓能力差的問題是旭光公司在研製和生產熱解石墨柵極發射管中遇到的比較突出的共性問題，課題針對這些問題所做的工藝試驗和理論探討對其它管型具有借鑒和參考價值。 -
This paper discusses property of the pyrolytic graphite firstly, analyzes its application on the high power and supper high power ’ s electric tubes and points out the prevalence of the pyrolytic graphite used for grid ’ s material. then through experiment and discussion, this paper has obtained the scientific depositional technology of the pyrolytic graphite grid ’ s rough and accomplished this subject
本文首先對熱解石墨材料的性能進行了討論，並就其在大功率、超大功率電子管中的應用作了分析，指出了熱解石墨作為柵極材料的優越性能;然後通過試驗研究和討論，獲得了優化的石墨柵極毛坯沉積工藝，完成了課題目標。 -
According to these technologies, the pyrolytic graphite grid that we disposed meets requirements of the electron tubes assembly
按照這些規范處理的熱解石墨柵極質量符合電子管裝配的要求。 -
As a engineer, i have researched the technology of the deposition of the pyrolytic graphite grid ’ s rough in detail and deeply, in order that xuguang electric ltd. co. achieves the producing from the deposition of the pyrolytic graphite grid ’ s rough to grid. in this research, propane and nitrogen gases has been used in the deposition of the pyrolytic graphite grid ’ s rough at about 1800 and in vacuum
為了使旭光電子股份有限公司順利實現從熱解石墨柵極毛坯沉積到柵極成品的生產，本人作為工藝研究人員，對熱解石墨柵極毛坯沉積工藝進行了詳細、深入的研究。在本課題研究工作中，採用了丙烷有機碳氫化合物氣體和稀釋用氮氣、氬氣，在高溫1800左右的真空條件下試驗研究了熱解石墨柵極毛坯的沉積。 -
In the process of the deposition of the pyrolytic graphite grid ’ s rough, experiment which adopts same discharge and proportion of those gases at different temperature has been done, the test which adopts different discharge and proportion of those gases at same temperature to deposit grid ’ s rough has also been done. at same time, the test which adopts different dilute gases at same technological condition to deposit the grid ’ s rough has been done. in order to obtaining the grid ’ s rough which thickness is able to use, the test has been done at different temperature and depositional time
在研究過程中，試驗了在不同溫度下採用相同的氣體比例和流量沉積熱解石墨柵極毛坯;還試驗了在相同溫度下，採用不同的氣體比例、不同的流量沉積熱解石墨柵極毛坯;同時，試驗了在相同工藝條件下採用不同的稀釋氣體沉積石墨柵極毛坯;為了獲得厚度合適的石墨柵極毛坯，試驗了不同溫度下採用不同的沉積時間來沉積毛坯;對不同溫度下沉積的毛坯進行了x射線衍射分析、密度分析及晶相分析。 -
Using this stm, many samples were scanned to test its capability. the atom graphics and nano - structure graphics of highly oriented pyrolytic graphite ( hopg ) were gained as well as some other samples. stable scan has been observed during all of the experiments, it has been concluded that the system works well in open environment
對整個系統進行了聯合調試，對多種樣品進行了掃描實驗以測試系統綜合性浙江大學碩士學位論文能，成功獲得了高定向熱解石墨（ highlyorientedpyrolyticgraphite ，簡稱hopg ）的原子圖像和納米結構圖像以及其他一些樣品表面的原子圖像。 -
Db930 tube has been developed successfully after through three years exploring and especially after xuguang corporate has established the whole pyrolytic graphite grid product line which is exclusive in china. it has filled up the domestic blank and own advanced technique and preferable economic beneficial foreground
在經過三年的努力工作，特別是在建立國內唯一完整的熱解石墨柵極生產線后，終于研製成功了db930 ，填補了國內空白，具有先進的技術性能和較好的經濟效益前景。