  1. In this paper, 6013al / sicp / gr metal matrix composite ( mmc ) was produced by spray codeposition, by means of changing the medium of quenching, influence of five types of heat treatment system ( furnace cooling, air cooling, water quenching, dry ice quenching, liquid nitrogen quenching ) and different aging temperature on the damping was studied systematically

    本文採用噴射共沉積方法制備了6013al sicp gr金屬基復合材料（ mmc ） ，通過改變淬火介質，較為系統地研究了五種熱處理制度（爐冷、空冷、水冷、乾冰冷及液氮冷）以及不同時效溫度（ 120 、 150 、 170 、 190及210 ）對6013al sicp grmmc阻尼性能影響。
  2. The results indicate that in niobate glasses, as the concentration of nb2o5 increases, the covalence becomes strong, the symmetry becomes low and the electron - phonon coupling becomes strong, thus the lifetimes become short, the nonradiative transition processes and the temperature - quenching become strong and the value of crystal field parameter b20 becomes small

    （ 6 ）研究了妮硅與妮磷系列玻璃發光特性與組份的關系，發現隨著nbzos濃度的增加， eu一o鍵共價性增強，局域環境對稱性降低，電一聲子禍合增強從而導致sd 。
  3. Medium frequency induction heating equipment are used in metal melting, temperature keeping, diathermic technology, metal - heat processing brass soldering, quenching, tempering and sintering

    中頻感應加熱設備適用於各種金屬熔煉，保溫，透熱，金屬熱處理，釬焊，淬火回火，燒結，釬絲鋼絲等。
  4. Oxygen sensor based on palladium - porphyrin room - temperature phosphorescence quenching

    鈀卟啉室溫?光氧傳感器的研究
  5. Determination of trace cobalt by solid substrate room temperature phosphorescence quenching method on hydrogen peroxide oxidizing pyrogallol red

    催化過氧化氫氧化鄰苯三酚紅固體基質室溫?光猝滅法測定痕量鈷
  6. Our company endeavors to quenching & tempering, normalizing, tempering, high and medium temperature quenching, mesh belt furnace quenching, carbonizing, aging subzero and high temperature heat treatment, etc

    本公司是一家致力於從事調質、正火、回火、高中溫淬火、網帶爐淬火、滲碳、時效冰冷及其高溫熱處理的廠家。
  7. In this investigation carbon black - filled electrical conductive composites of poly ( ethylene terephthalate ) / polyethylene were first prepared through the single - screw melt - blended extrusion, then drawing, followed by the quenching and subsequent press molding. the relationships among the influencing factors including composition, hot stretching ratio and compatibilizer, morphology and properties of composites were systematically investigated. positive temperature coefficients effect and crystallization behaviors of composites were preliminarily analyzed

    本文擬採用單螺桿熔融共混擠出?熱拉伸?淬冷的新的成型方法制備炭黑填充的pet pe復合導電材料，熱拉伸的目的是使材料的分散相（ pet相）在加工過程中原位形成纖維，而炭黑基本分散在纖維中或纖維的表面上，使炭黑粒子間間距減小，形成更多的導電通路，從而提高材料的導電性能，同時保持或提高材料的力學性能。
  8. But the activation energy of water quenching samples are very different at different aging temperature, the lowest is 1. 27ev and the highest is 2. 4 lev

    而水淬試樣在不同的時效溫度下激活能計算的結果有很大的不同，激活能最低為1 . 27ev ，最高為2 . 4lev 。
  9. After the coke being puted into the coke - quenching device, the lid of the device should be shut at once. while the suction pump, refrigeration compressor, high pressured water circuling pump are started, the subpressure will be produced by the burning coke. then, in the vacuum, the coke will be extinguished in a flash. the burning of the coke instantly, still, produces a large quantity of heat which can be taken away by circulating water in refriger and the interlayer, after that, the temperature will fall to 60oc, even lower. in this condition, the coke will be pushed out to be stored, thus, the coke won ' t rekindle

    當焦炭推上攔焦車進入熄焦器后，立即關閉罐蓋，同時啟動真空泵、冷凍機、高壓循環水泵，這時，燃燒著的焦炭就會因真空泵把熄焦器內抽成負壓，由於缺氧，使焦炭熄滅，雖然煤炭在瞬間被熄滅，但由於焦炭生成過程中所產生的大量的熱量還存在，這時，冷凍機和夾層中的循環水的工作就會把焦炭中的熱量帶走，使之在短時間內將溫度降到60以下，在這種狀態下把焦炭從熄焦器內推出入庫，焦炭就不會復燃。
  10. The influences of isothermal quenching temperature on the retained austenite and mechanical properties of adi were studied

    摘要研究了等溫淬火溫度對adi中殘余奧氏體及其力學性能的影響。
  11. The principle of multi - method and multi - parameter is suggested, which should be followed during characterizing microstructures of alloy steels by ultrasonic not method. ultrasonic velocity ( c, ) of transformation products through different heat processes of three steels was measured by high - accuracy ultrasonic installation. the velocity of quenched microstructure of 38crmoal is the lowest, which gradually increases with increasing tempering temperature between 200 ? and 650 ? after quenching process

    利用ti - 40n高精度超聲波測厚儀，研究了超聲波在不同鋼種、不同熱處理轉變產物中的超聲波速度c _ 1 : 38crmoal鋼淬火組織c _ 1最小，淬火后在200 650范圍內進行回火處理時，隨回火溫度的升高， c _ 1逐漸升高， hrc與c _ 1之間具有較好的相關性；正火組織的c _ 1介於淬火后中溫回火及高溫回火產物組織的c _ 1之間。
  12. Aiming at the obvious temperature difference on the slab surface after descaling in hot rolling mill, this paper studied the parameters of the descaling system and numerically simulated the descaling quenching process

    摘要從熱軋廠除鱗后板坯表面所產生的明顯溫差入手，研究了除鱗系統的參數配置並對除鱗冷卻過程進行了數值模擬。
  13. Sub - temperature quenching process of high strength bolts

    高強度螺栓的亞溫淬火工藝
  14. Influence of parallel plate temperature on flame quenching

    平板阻火單元溫度變化對火焰淬熄的影響
  15. It was pointed out that with different chemical composition and different iso - quenching temperature, the structure morphologies of the bainite transition products are different from each other, the ferrite is the indispensable constituent, and whether there is or not carbide existing is not the necessary criterion to discern the bainite

    指出不同化學成分和不同等溫溫度時貝氏體相變產物的組織形態不同，鐵素體是貝氏體中不可缺少的組成部分，以及碳化物的存在與否不是判斷貝氏體的必要依據。
  16. The variation principle of wave velocity in different microstructures of 40cr is similar with that of 38crmoal. the velocity in quenching and low temperature tempering structure of gcrlssimn is much lower than the velocity in normalizing, annealing and high temperature tempering structure

    Gcr15simn鋼淬火+低溫回火組織的c _ 1遠大於正火、退火及淬火+高溫回火組織的c _ 1 ；正火、退火及淬火+高溫回火組織的c _ 1比較接近。
  17. Second, on the numerical arithmetic of the quench - induced residual stresses ground, the quenching process of 7075t73 aluminum plate is simulated, the effect of material characteristics along with the plate temperature varying in quenching is considered, and on conditions of the different water temperature and different plate thickness, the quenching processes are compared

    2 、建立了航空鋁合金板材淬火過程的彈塑性力學模型，對航空鋁合金板材溫度場與應力場進行了數值模擬，模擬過程考慮了材料特性隨溫度變化的影響，並對不同的淬火影響因素進行了分析。
  18. The results show that, with the quenching temperature ( 270 ~ 380 ) increasing, the carbon content and percentage content of retained austenite increase first and then decrease, which are up to a maximum value at 360 ; the tensile strength of adi decreases ; the elongation and impact ductility of adi increase first and then decrease, which are up to a maximum value at 360 ; but the hardness of adi decreases first and then increases, which is up to a minimum value at 360

    結果表明，在試驗溫度范圍內（ 270 ~ 380 ） ，試樣中殘余奧氏體的含碳量及其含量隨著等溫淬火溫度的升高先增大后減小，均在360等溫淬火時出現最大值；抗拉強度隨著等溫淬火溫度的升高而逐漸降低；伸長率和沖擊韌度隨著等溫淬火溫度的升高先增大后減小，在360等溫淬火時出現最大值；硬度則隨著等溫淬火溫度的升高先減小后增大，當360溫淬火時硬度最低。
  19. For the fe - 2 % c - 4 % v - 4 % mo - 5 % cr - x % w alloy system, the peak value of quenching appears in 950 - 1100. the peak value increases with the increment of w. when the content of w is 2 %, the temperature of temper hardening is 550. for the fe - 2 % c - 4 % v - 4 % mo - 5 % cr - 2 % w alloy, the appropriate quenching temperature can be controlled in 1000 1050 and the time of preserving heat is 12min

    57 （原於百分比，人分析表明， mg的變質作用的產生是由於mg影響了合金元素的偏析，使得基體組織中合金元素含量增加，相當于使合金分配系數k更偏離於1 ，從而促進了形成縮頸、晶粒繁殖和成分過冷傾向。
  20. Quenching and tempering were chosen to strengthen the material. the quenching temperature and time were adjusted based on the hardness measurement

    選擇淬火和回火作為本課題的熱處理工藝，並用硬度法確定可行的淬火溫度和保溫時間。