Spherulites dimension also decreases due to the chemical changes occurred during pan - milling. viscosity test shows that chain scission occurred during pan - milling, which caused slight reduction of mechanical properties. polypropylene / polyamide 6 ( pp / pa6 ) ultra - fine powder was prepared through pan - milling at ambient temperature
通過磨盤碾磨在常溫下制備了聚丙烯/尼龍6 ( pp / pa6 )超細復合粉體,其粒徑可通過碾磨時間、磨盤轉速、磨面靜壓力、碾磨溫度等工藝參數控s摘要一制。 -
W - cu composites prepared from the precipitation w - cu powder have higher sintered density, better mechanical and physical property, more homogeneous and finer microstructure than those prepared from w - cu powder by the balling - reduction method. in chapter 5, a combination of homogeneous precipitation and ball - milling process, namely the mechano - thermochemical process was employed to prepare ultra - fine w - cu powder
其中,球磨w一cu復合粉( hp一m )壓坯在1150下燒結30min后,可獲得相對密度大於99 %的幾乎全緻密的超細晶粒w一cu復合材料, w的顆粒度小於0 . 5林m 。