The result shows, for this composite cement system, retarding action of dihydrate gypsum is more obvious than that of anhydrite, meanwhile, anhydrite tends to cause setting time short and water needed increased
結果表明：二水石膏對該種復合體系水泥的緩凝作用比硬石膏明顯，硬石膏易引起復合體系水泥急凝和需水量增大。 -
Hi this thesis, the setting time of various retarders had been tested, in which three retarders with good retarding action, citric acid, sodium tripolyphosphate, bone glue are respectively chosen from three types of retarders, hydroxyl carboxylic acid type, phosphate type and protein type, and the strength and setting time of gypsum added with them are determined. effect of some factors, such as ph value, fineness of hemihydrate, type of gypsum on the retarding action of the retarders is also studied
本文對多種緩凝劑進行凝結時間測試，選擇效果良好的羥基羧酸、無機鹽和蛋白質類型的三種緩凝劑：檸檬酸、多聚磷酸鈉和骨膠，測定它們對石膏凝結時間、強度等宏觀性能的影響，並分別研究ph值、石膏細度和石膏種類等因素對它們的緩凝效果的影響。 -
The intelligent time relay is intelligent double row four location display instrument, it is the operation of three keys, have the function of single setting double setting time, it applies special technique to resist interference, avdvanced craft, high technology, satisfied the clients need. its the new product which assimilate the nation and internationals same products character
名稱： sng智能時間繼電器sng智能時間繼電器是智能型雙排四位顯示儀表，儀表為三鍵操作，具有單雙時間設置，參數設置快捷，符號顯示簡潔，儀表採用進口超強抗干擾晶元設計質量可靠。 -
The result shows that blended cement mixed with activatory coal gangue powder has high compressive strength, however, with the increase of the admixture of coal gangue powder, flowability of blended cement paste become worse, and the setting time is not obviously affected
結果表明，摻入經活化處理的煤矸石粉配製的混合水泥具有較好的強度性能；隨摻量增加，水泥漿體的流變性能變差，但對凝結時間並無明顯影響。 -
It has a good high tenperature flow ability short setting time, rignersintered strcngth and high corrosion resistance
該產品具有良好的高溫流動性，較短的硬化時間，較高的燒結強度優質的耐侵蝕性能。 -
The effects of gypsum on fluidity of cement mortar and setting time of cement paste are not significant when it used as retarder of cement. whereas, when 0. 3 % ca - lignosulphonate or ca - solassate added in cement used anhydrite gypsum as retarder, loss of fluidity of cement mortar is rapid, quick setting is occurred
但是，在硬石膏調凝水泥中摻加0 . 3的木鈣和糖鈣緩凝減水劑卻能使水泥砂漿流動度經時損失加快，凈漿表現出促凝現象，發生外加劑與水泥的不相容問題。 -
Abstract : the cause of underwater concrete reinforcing cage up - floating accident is improper operation, such as loose - placement of reinforcing cage, fast - drawing of conduct pipe, improper embedded depth of conduct pipe ; and the poor quality of concrete, for example, the slump, sand percentage, adhesiveness and initial setting time don " t meet requirement
文摘:水下混凝土澆注鋼筋籠上浮事故的原因是操作不當，如鋼筋籠固定不牢、提升導管過猛、導管埋深不當等，以及混凝土品質差，如坍落度、含砂率、粘聚性、初凝時間等不合要求。 -
Testing method for setting time of refractory mortars
耐火泥固化時間的試驗方法 -
Admixtures for concrete, mortar and grout. test methods. part 2 : determination of setting time
混凝土灰泥和薄漿混合料.試驗方法.第2部分:凝結時間測定 -
Selection of suitable retarding agent and its addition is particularly important for controlling the setting time of gypsum - based material in a certain rang, meeting the requirement of construction process. though the retarder is widely used, the influence factor, the intrinsic reason that induces the strength drop and retarding mechanism are still studied superficially
盡管石膏緩凝劑的用途廣泛，但是對於它的影響因素、緩凝劑強度降低的內在原因和緩凝劑阻礙石膏水化形成緩凝作用的機理的研究粗淺，認識模糊。 -
This method can decrease the gap setting time for which the oil column of hydraulic cylinder is not retracted and there is no minute adjustment of oil column for the first several passes
採用該方法，軋制過程液壓缸油柱不用回縮，而且前面道次液壓不進行微調，從而節省了輥縫設定時間。 -
By means of comparative experiments, this paper illustrates the influences of different cements, admixtures of flash - setting agents, water cement ratios, curing temperatures and raw materials on the performances of sprayed concrete, such as the setting time, strength and shrinkage ratio, on different conditions of efflorescence and hydration, so as to present references with regularity for the practical application of sprayed concrete
摘要通過對比試驗，闡明了不同水泥、不同速凝劑摻量、水灰比、養護溫度以及原材料在不同風化和水化程度條件下，對噴射混凝土凝結時間、強度、收縮率等性能的影響，以期為噴射混凝土的實際應用提供規律性的參考資料。 -
Based on the selection of the accelerating agents for the wet shotcrete, the applicability of the setting time for the accelerating agents got from the tests concerned are discussed herein, from which a proposal is put forward that the alkali - free accelerating agent is suggested to be preferentially applied to the wet shotcrete for the permanent project
摘要根據濕噴混凝土速凝劑品種選擇試驗結果，討論了速凝劑凝結時間試驗結果的適用性，開提出了永久工程濕噴混凝土應優先選用無堿速凝劑的建議。 -
Methods of test for hydraulic setting floor smoothing and or levelling compounds - determination of setting time
水凝地面鏝光和或找平填料的試驗方法.凝固時間 -
The paper first reviews the research background and actuality of the filter " s design in china and other country, introduces the meaning of the project and the work of the paper, narrates the theory of the switched - capacitor network and the basic switch building blocks, analyses the related factors of the design of sc filter. such as the selection of the architecture, the trade off of the opamp " s gain, bandwidth, phase margin, slew rate and setting time, the effect of the switch " s on resistor, how to reduce the charge injection and the clock feed - through, the power consumption and the selection of the sampling frequency and so on
本文首先回顧了濾波器設計的國內外研究背景和現狀，介紹了本課題提出的意義以及本文的主要工作，論述了開關電容網路原理和基本開關模塊，分析了開關電容濾波器設計的相關因素：電路結構的選擇，對運算放大器設計中高增益、寬帶寬、相位裕度、轉換斜率和建立時間等的折中考慮，開關的打開電阻對電路的影響，開關電容電路中怎樣減少電荷注入和時鐘饋通，以及整個電路的功耗問題和采樣頻率的選擇等。 -
According to many years experience of dealing with client quality complains, the author introduced in brief its principle and content, and laid emphsis on the common quality complains of cement enterprise, such as concrete strength is lack, the concrete setting time is unnormal, the concrete slump constant is a little small and the loss is high, compatibility between cement and admixture is bad, cement color changes, concrete surface rise sand and cement agglomerate
作者結合自己多年處理顧客質量投訴的經驗，簡單介紹了處理顧客質量投訴的調查原則和內容；重點對水泥廠最常見的質量投訴內容包括混凝土強度不足，凝結時間異常；混凝土坍落度偏小，經時損失大；水泥與外加劑相容性不好；水泥顏色變化、混凝土地面起砂及水泥結塊等等投訴，分別進行了現象描述，原因分析和調查方法介紹。 -
The cause of underwater concrete reinforcing cage up - floating accident is improper operation, such as loose - placement of reinforcing cage, fast - drawing of conduct pipe, improper embedded depth of conduct pipe ; and the poor quality of concrete, for example, the slump, sand percentage, adhesiveness and initial setting time don " t meet requirement
水下混凝土澆注鋼筋籠上浮事故的原因是操作不當，如鋼筋籠固定不牢、提升導管過猛、導管埋深不當等，以及混凝土品質差，如坍落度、含砂率、粘聚性、初凝時間等不合要求。 -
As a kind of cement retarder, normal setting time and good effect for mechanical properties and soundness of cement can be got when adding desulfurization gypsum in cement, so it can used instead of natural gypsum to produce cement entirely, coal gangue is activated and coal ash desulfurized have good active, can improve cement output and also can depress consumption when them be used as mixed material, have well economic and environmental effects
脫硫石膏作水泥緩凝劑時，水泥的安定性、凝結時間正常，可改善水泥的力學性能，完全可替代天然石膏；活化后的煤矸石和脫硫煤灰具有較好的活性，用作水泥混合材可增加水泥產量、降低生產成本，具有良好的經濟和環境效益。 -
Final setting time
終凝時間 -
Setting time of gypsum plaster is very short, usually only 6 ~ 30 min, and operation time is only 5 - 10 min, which cannot satisfy the practical plastering and construction of gypsum - based material
半水石膏凝結硬化很快，其初終凝時間為6 30分鐘，可操作時間只有5 10分鐘，往往不能滿足石膏基材料的成型與施工的需要。