superplasticized concrete 中文意思是什麼
superplasticized concrete
解釋
連混凝土- concrete : adj 1 具體的，有形的；實在的，實際的。2 固結成的，混凝土製的。3 圖案詩歌的（參閱concrete poetry）...
-
After bfs is put into high strength superplasticized expansive concrete ( substituted for cement ), autogenous shrinkage does n ' t appear in 1 day standard curing, and e2 in 14 day ' s age is higher than that of high strength superplasticized expansive concrete without bfs in the same age
高強流態膨脹混凝土摻入磨細礦渣（等量替代水泥）后，標準養護1天未出現自收縮， 14天的限制膨脹率明顯高於未摻磨細礦渣的高強流態膨脹混凝土的對應值。 -
Bfs can reduce the early strength of high strength superplasticized expansive concrete and make expansion effect develop fully. so high strength concrete with bfs shows higher e2
磨細礦渣的加入使高強膨脹混凝土的早期強度降低，膨脹效應得以較充分發揮，所以加入磨細礦渣的高強混凝土顯示出較高的膨脹率。 -
This seemingly contrary phenomenon is rooted in the coordination of expansion and strength development : the high strength especially high early strength of high strength superplasticized expansive concrete confined expansion effect, and there is " self - restricted effect " in concrete
上述看似矛盾的現象源於膨脹混凝土的膨脹與強度的協調性：高強流態膨脹混凝土的高強度，特別是較高的早期強度限制了膨脹效應的發揮，在混凝土內部存在「自約束效應」 。 -
From the research on hpec we can know that expansion property of high strength superplasticized expansive concrete shows obvious particularity compared with ordinary expansive concrete. when bfs is not put in, high strength superplasticized expansive concrete shows autogenous shrinkage in 1 day standard curing. and in 14 day ' s age e2 is less than half of middle strength superplasticized expansive concrete ' s with same csa dosage, and this shows expansion effect is confined more
對hpec混凝土的研究發現，與普通膨脹混凝土相比，高強流態膨脹混凝土的膨脹性能表現出明顯的特殊性，在不摻超細礦物質摻合料（磨細礦渣）時，高強流態膨脹混凝土標準養護1天時出現自收縮， 14天時其限制膨脹率不到相同csa摻量的中強流態膨脹混凝土限制膨脹率的一半，表現為膨脹效應受到更大限制。 -
The expansion and strength of middle strength superplasticized expansive concrete develop more coordinately. fa reduces the early strength of middle strength superplasticized expansive concrete, and this make more expansion become invalid when the concrete is in plastic state
中強流態膨脹混凝土的膨脹與強度性能發展比較協調，粉煤灰的加入降低了早期強度，使更多的膨脹變為無效膨脹消耗在仍處于塑性狀態的混凝土中，混凝土限制膨脹率減小。 -
The high performance concrete is synthesized by superplasticized admixture, high quality fly ash, air entraining and low water / cement ratio in this paper
高性能混凝土以其良好的抗碳化性能，在工程中日益得到廣泛應用。