  1. The results indicate that the optical performance and coating quality have been improved drastically by using ion - assisted deposition technology in the vacuum deposition, in comparison with the traditional thermal vapor deposition

    結果表明，與傳統的熱蒸發鍍膜工藝相比，在真空沉積過程牛採用離子束輔助沉積技術，可以大大提高膜層的光學特性及膜層品質。
  2. Phase composition and surface morphology of tic coating by chemical vapor deposition

    塗層的相組成和表面形貌
  3. Lppp thin films were prepared by spin coating from a solution of lppp in toluene and alq was formed by vapor deposition. different configuration devices with lppp single - layer, lppp micocavity and lppp / alq heterojunction were fabricated

    利用lppp甲苯溶液旋塗制備lppp薄膜，真空蒸鍍法制備alq膜和電極，分別製作了lppp單層無腔、 lppp單層微腔、增強型lppp / alq異質結結構的有機電致發光器。
  4. In this thesis, the history, structure. preparation method and basic properties of nano - composite materials and photoluminescence of nanocrystalline silicon have been summarized. research of the novel antireflecting energy saving coating glass has also been presented. the si / sic composite films are prepared with siht and ? 2 ^ 4 as the source gas by atmosphere pressure chemical vapor deposition ( apcvd )

    本論文全面介紹了納米材料，特別是納米鑲嵌復合材料的發展概況、特性、常用的制備方法、常見的幾種硅系納米材料以及有關納米硅材料的發光，並對新型無光污染節能鍍膜玻璃的研製和發展作了概述。
  5. In order to prolong the lifetime of the phosphor, na2sio3 liquid phase hydrolyzation and atmospheric chemical vapor deposition of teos and o2 is adopted to form coating of silicon dioxide film on the surface of the electroluminescent phosphor zns : cu in this paper for the first time

    為了延長材料的使用壽命，本論文首次採用na _ 2sio _ 3液相水解和teos與o _ 2的常壓化學氣相沉積的方法在zns ： cu發光材料的表面包覆sio _ 2膜層。
  6. The influence of deposition conditions and the coating mass on the response of the films were also considered. the determination lower limit of films to formic acid vapor was measured and it attained ppm grade

    同時還摘要對微量甲酸蒸氣的響應進行了研究並討論了摻胺碳膜對甲酸蒸氣的檢測下限，其下限達到ppm數量級。
  7. For the liquid phase method, it is discovered that the optimal encapsulation is obtained at stalling ph equal 8. 5 by the analysis of the influence of ph on the compactness. for the atmospheric chemical vapor deposition, the optimal experimental condition of coating is determined by the analysis of the influence of different reaction temperature and different flow rate of o2 and different reaction time on the compactness of the coating and the luminescent performance of the phosphor in the experimental scope

    對于液相包膜，通過分析陳化ph值對膜層緻密性能的影響，發現在ph值為8 . 5陳化能夠得到最佳的包覆；對于化學氣相沉積法，通過分析不同溫度、不同氧流速、不同時間對包覆膜層緻密性能和zns ： cu材料的發光性能的影響，找到了該實驗范圍內包覆的最佳條件。
  8. Essentially, the process of reactive plasma spraying tin coating is combination of the plasma - assisted chemical vapor deposition ( pacvd ), and combustion synthesis of ti in nitrogen gas

    反應等離子噴塗tin塗層本質上是等離子輔助化學氣相沉積，以及ti在n _ 2氣中燃燒合成tin 。
  9. 3. the gap defects in multilayer cvd sic coatings could be effectively controlled by means of slow deposition in low - pressure chemical vapor deposition ( lpcvd ). 2d c / sic composites with a multi - layer cvd sic coating prepared by slow lpcvd showed weight gain at 1300 @ in air condition

    （ 3 ）採用慢速減壓化學氣相沉積工藝實現了對多層cvdsic塗層面缺陷的有效控制，實現了單一cvdsic塗層保護2dc sic在高溫下（ 1300 ）的氧化增重。
  10. Finally, it is realized preliminarily that the fabrication of hollow fibers with sic films, which concludes the process of fiber - drawing and coating, can be done in an organic whole with modified chemical vapor deposition ( mcvd )

    最後，利用改進化學氣相沉積法（ mcvd ）方法，對具有sic內膜的空芯傳能光纖的內層鍍膜、拉絲一次性完成進行了探索。
  11. Study on medium temperature chemical vapor deposition mt - cvd technology and super coating material

    工藝技術及超級塗層材料的研究
  12. Coating cracks and defects are main reasons for the limited oxidation resistance of sic - c / sic. in this thesis, surface modification of sic coating was carried out with physical vapor deposition ( pvd ) and ion implantation & deposition, using al, b and si. effects of the modified coatings on the oxidation resistance of sic - c / sic were studied with sem, xrd and aes and so on

    本文採用了物理氣相沉積方法和離子注入沉積方法，以al 、 b 、 si為改性元素，對sic塗層表面進行改性，封填裂紋和缺陷；結合掃描電鏡（ sem ） 、 x射線衍射（ xrd ）和俄歇能譜（ aes ）分析，研究了改性層對sic - c sic復合材料抗氧化性能的影響。