viscosity average 中文意思是什麼
viscosity average
解釋
粘度平均值-
Viscosity - average molecular weight viscosity - average molar mass
黏均分子量 -
Increasing ultrasound intensity in the range of cavitation threshold and cavitation peak value, decreasing monomer concentration and increasing the temperature make the induction period shorter. under optimized reaction conditions, the conversion of ba can reach 90 % in 11 min at high n2 flow rate the viscosity average molecular weight of the obtained pba reaches 5. 24 106. the molecular weight of pba varies with ultrasonic irradiation time, indicating that the ultrasonic induced emulsion polymerization is dynamic and quite complicated, polymerization of monomer as well as degradation of polymer occurs concomitantly
一、實現了無常規化學引發劑存在下的超聲輻照引發丙烯酸正丁酯（ ba ）間歇乳液聚合，制備了pba納米粒子，在11min內轉化率達到90 ，分子量達5 . 24 10 ~ 6 ，隨反應時間的延長而降低，表明超聲輻照引發乳液聚合是一個動態的復雜過程，單體的聚合和聚合物的降解同時發生。 -
The results showed that hydrothermal cracking occurred while injecting steam, and the catalyst had catalytic activity for hydrothermal cracking of heavy oil at higher temperature ; viscosity and average molecular weight of heavy oil was thus lowered
實驗結果表明，在注入蒸汽的條件下，遼河稠油可以發生水熱裂解反應，高溫下催化劑對水熱裂解反應具有催化作用。 -
Lactide were investigated. the key factors affecting the polymer intrinsic viscosity were found to be monomer recrystallization times, stannous octoate concentration and polymerization time. the thermal stabilizing agent did not significantly affect the polymer molecular weight. the polymer with a viscosity average molecular weight beyond 200000 was fairly reproducible by optimizing the polymerization conditions. it was found that poly
單體重結晶次數辛酸亞錫濃度聚合時間等條件均是影響聚合物特性粘數的重要因素。熱穩定劑對聚丙交酯的分子量幾乎沒有影響。優化聚合條件可以獲得粘均分子量大於200000的聚丙交酯材料，聚合結果具有良好的重復性。 -
Textiles. cellulose. determination of limiting viscosity number and determination of the average viscosimetric degree of polymerization
紡織.纖維素.特性粘度的測定和平均粘度測定法聚合度的測定