As an advanced materials preparation technology, spray - deposition has shown remarkable superiority in producing large - sized alloys and metal matrix composites. however, the spray deposeted preforms usually contain a certain quantity of porosity. besides, the oxide films on the surface of the particles lead to week metallurgic conjunction between the particles. in order to obtain an ideal structure and performance, the porous preforms need further densifying and plastical forming. in this paper, a new technology named wedge pressing was used to densify spray - deposeted 5a06 aluminium alloy, in which the large deformation can be obtained through the sum - up of local deformation and multi - step small deformation. this method can also solved the problems in traditional processing and greatly decreased the producing cost. what ’ s more, the reserch on the wedge pressing desification rules about the large - sized spray deposeted preforms was significant it was vital not only to the further densification of the prefoums but also to the further research on plastical deforming the research was also benefit to the industrialization an the application of the spray deposeted porous materials
坩堝移動式噴射沉積技術作為一種先進的材料制備新技術，在制備大尺寸合金及金屬基復合材料方面具有顯著的優越性。然而噴射沉積坯件特別是大型坯件通常存在一定量的孔隙，顆粒表面存在一定量的氧化膜，顆粒之間未能完全達到良好的冶金結合狀態，因此需要進行后續緻密化和塑性變形才能獲得理想的組織和性能。本文採用一種新型的楔形壓制工藝，即通過局部變形、多道次小變形累積實現大變形的緻密化加工方法，對噴射沉積多孔坯料進行后續緻密化和塑性變形，很好地解決了傳統加工工藝的難題，大大降低了生產成本。 -
A plain or notched, often wedge - shaped piece of wood or metal designed to hold parts of a machine or structure in place or provide a bearing surface, usually adjusted by a screw or key
扁柱，夾條，凹字形楔一種平的或有凹的經常是一塊楔形的木頭或金屬，用來在一定地方夾住機器或結構的各部分或提供軸承的表面，通常是由螺絲或鑰匙來調整 -
Secondly, the effect of transverse deforming on the property of the wedge pressing was studied. the results showed that : the wedge pressing stock with the transverse deforming amount of 10 % acquired the best performance. the highest density got the biggest rate of slope while with the amount of 30 % the curve was more some special structure and performance as following : the large porosities was crushed into small or linear ones with the high - direction deformation amount of 20 % ; as the increasing of the high - direction deforming, the particles got a further deforming, the porosities got a further crushing, the small porosities were mergered by the large ones and the former then disappeared ; when the amound reached 60 %, the quantity of the porosities would obviously decrease which made the materials compact, the microstructure more uniform and the density and hardness curves more horizontal, the relative desity could reach 99. 7 %, the tensile strength b of the as - compacted samples reached 408mpa with the yield strength s teached 289mpa and the elongation percentage reached 13. 6 %. in addition, the microstructure of the wedge pressing stock under the pressing temperectureof 450 was uniform, the porosities and the boundries of the grains basically disappeared and the conjunction between particles was great
採用雙向楔形壓制，大尺寸噴射沉積5a06鋁合金楔壓坯的組織和性能變化具有如下特點:當高向變形量為20 %時，大的孔洞變形破碎為小的孔洞，或呈線狀孔;隨著高向變形量的增加，顆粒進一步變形，孔洞進一步破碎，大孔「吞併」小孔，小孔塌陷並逐步消失;當高向變形量達到60 %時，孔洞量大為減少，材料基本緻密，組織趨于均勻，楔壓坯料的密度、硬度變化曲線接近水平線，坯料的相對密度達99 . 7 % ，抗拉強度_ b = 408mpa ，屈服強度_ （ 0 . 2 ） = 289mpa ，延伸率= 13 . 6 % ;對比其它的壓制溫度，在450楔形壓制的坯料組織均勻，孔洞及顆粒邊界基本消失，顆粒之間冶金結合良好。 -
Upon analysis of advantages and disadvantages of varieties of support structure of roller of cross wedge rolling mill in existence, a new type of support for the upper roller has been introduced with calculation in design of certain components combined with a specific type of such machine
摘要通過分析現有輥式楔橫軋機上軋輥各種支撐結構的優缺點，重點介紹了一種新型的上軋輥支撐結構並結合具體型號楔橫軋機對其部分部件進行了設計計算。 -
Finite element modeling and modal analysis of wedge - ring connection structure
楔環連接結構有限元建模與模態分析
分享友人