yig 中文意思是什麼

yig 解釋
YIG ＝ yttrium iron garnet 釔鐵石榴石〈一種具有多項磁特性的氧化鐵合成晶體，常用於調節激光〉。

  1. The results of x - ray photoelectron spectrum ( xps ) demonstrated the ce ions in pure phase ce : yig ( x < 0. 2 ) were in the state of trivalence. scanning electron microscope ( sem ) analysis showed conglobation of yig and ce : yig particles, whose size were smaller than 1 urn

    Xps的分析結果顯示單相ce ： yig （ x 0 . 2時）中ce離子是以正三價的狀態存在，這與物相分析結果是一致的。
  2. Vibrating samples magnetometer ( vsm ) testing implied that yig were of ferrimagnetism, and cerium substitution had effects on saturation magnetization ( ms ), residual magnetization ( mr ) and coercive force ( hc )

    Vsm測試結果表明yig屬于亞鐵磁性物質， ce離子的摻雜對飽和磁化強度（ ms ） 、剩餘磁化強度（ mr ） 、矯頑力（ hc ）都有一定的影響。
  3. Studies showed that process and condition control had critical effect on the preparation of yig phase, and the proper conditions specialized as follows : using ammonia - ammonium nitrate ( nh3 - nh4no3 ) as precipitant, ph scope from 10 to 10. 5, using dissolving salt as law materials, dropping their mixed solution into precipitant, precipitation rate at 0. 8ml / min

    研究表明，共沉澱的過程和條件控制對yig的合成具有重要影響。實驗得出共沉澱的合適條件為：以nh _ 3 - nh _ 4no _ 3為緩沖溶液，控制ph范圍為10 . 0 ? 10 . 5 ，採用可溶性鹽為原料配製溶液，滴加到沉澱劑中的共沉澱方式，共沉澱速度為0 . 8ml min左右。
  4. Two issues about the yig - tshangs gao - shen system during tubo dynasty

    吐蕃告身制度的兩個問題
  5. The propagation characteristics of msfvws in a double - layered yig waveguide

    波導中靜磁體波的傳播特性
  6. Measurement of magnetic properties of yig single crystal magnetic - films

    釔鐵石榴石單晶磁性薄膜磁特性的測量方法
  7. In this paper, yig and ce : yig were prepared via chemical synthesis method, and their composition, structure, magnetic properties were investigated

    本文在充分分析本領域國內外研究現狀的基礎上，採用化學合成法制得單相yig和ce ： yig ，並對其組分、結構特徵和磁性能進行了分析研究。
  8. The investigation of synthesis, composition and structure analysis, and characterization of magnetic properties of yig and ce : yig would build foundation for the study of ce : yig single crystal in the future

    Yig和ce ： yig的合成及其成分、結構和性能的分析，為ce ： yig單晶的制備和研究奠定了良好的基礎。
  9. Yig and ce : yig precursors were prepared via coprecipitation. by means of improving homogeneity and decreasing synthesis temperature, harmful yfeo3 phase was restrained, the oxidation of ce3 + was under control, and pure phase yig and ce : yig ( x = 0. 2 ) were obtained

    採用共沉澱法合成yig及ce ： yig前驅體，通過提高組分均勻性、降低煅燒溫度等手段，有效地抑制了yfeo _ 3雜相的生成和ce ~ （ 3 + ）離子的氧化，合成了單相yig和ce ： yig 。
  10. Cerium - substituted yttrium iron garnets ( cexy3 - xfe5o12, ce : yig ), the promising materials for magneto - optical ( mo ) application, have been widely attended for great improvement on faraday rotation due to the substitution of ce3 + ions to y3 + ions. however, studies on synthesis of ce : yig were restrained by two factors : the first was radium of ce3 + ions were much larger than that of y3 + ions, the second was ce3 + ions tended to transfer to ce4 + ions which were more chemically stable

    摻鈰釔鐵石榴石（ ce - substitutedyttriumirongarnets ，簡稱ce ： yig ）中，由於ce ~ （ 3 + ）離子對y ~ （ 3 + ）離子的取代，將大大提高釔鐵石榴石（ yttriumirongarnets ，簡稱yig ）磁光材料的法拉第旋轉角和磁光優值，使其能夠廣泛應用於激光和光通信等高技術領域。
  11. The bragg diffraction efficiency of gows in bismuth - doped yig film is caculated by considering the edge cut - off effect. the obtained theoretical curve is basically agreement with the experimental results. it is shown that the diffraction performance for mo bragg cells can be greatly increased by using an appropriately nonuniform bias field

    2 .考慮到邊緣截止效應，論文中計算了靜磁正向體波對導波光的衍射效率，理論結果與實驗符合;從而表明，與均勻場情形相比，適當不均勻場可以大大提高磁光bragg器件的衍射效率。