The summary about this paper is as follows : by adjusting the composition of the glass, the author prepared two kinds of glassy laser material : tellurite glass ( shorten form : tbzre ) and phosphate glass ( shorten form : npre - 1 )
具體內容如下： 1 ）通過調整配料組份，制備出了兩種新型的玻璃激光材料：亞碲酸鹽玻璃（簡稱tbzre ）和磷酸鹽玻璃（簡稱npre - 1 ） 。Research on preparation and luminescence of rare earth doped tellurite and phosphate glassy laser materials is author ' s mainly researched topics. in addition, the author has also studied for the application about the two kinds of materials
作者碩士期間所作工作主要是摻稀土亞碲酸鹽和磷酸鹽玻璃激光材料的制備和發光的研究，在這基礎上對它們的應用也作了相應探討。High quality cube - like mnse2 and sphere - like ( - mnse micro - crystals have been obtained in aqueous solution at low temperatures ( 100 ( c ~ 180 ( c ). by using tellurite as reactant, uniform cote and nite nanocluster wires were successfully synthesized through a co - reduction process
用亞碲酸鹽代替亞硒酸鹽，上述方法被成功應用到金屬碲化物的動力學調控合成中，通過共還原反應機理，利用新生的元素co 、 ni與活性碲，於水溶液中合成了cote和nite的一維納米線。The evaporation of sodium tellurite glass in low gravity is explored and the formation and growth processes of teo2 microspheres are explained. the size of teo2 microspheres from low gravity is much larger than that from ground experiments and it is affected mainly by the temperature of melt in the heating coil and the duration time of vapor cloud during drop experiments
探索了微重力對亞碲酸鈉玻璃熔體氣化的影響，分析了微重力下由於玻璃熔體氣化而生成teo _ 2玻璃微球的過程，解釋了微重力下形成的微球尺寸遠遠大於摘要地面模擬實驗所得微球的原因。In the present dissertation, some properties of sodium tellurite glasses, including density, chemical durability, stability against crystallization and fragility of glass forming liquid are studied. the melting, evaporation and solidification of sodium tellurite glasses in low gravity during drop shaft experiments are observed. except this, the phase - separation of lead borate glasses under different gravity condition is also studied
本文亞碲酸鈉玻璃作為研究對象，系統探索了亞碲酸鈉玻璃的熔化條件，化學穩定性，玻璃抗析晶能力以及玻璃形成液體的脆性等問題，著重研究了na _ 2o - teo _ 2玻璃在落塔實驗中的熔化和氣化以及pbo - b _ 2o _ 3玻璃在落塔實驗中的分相，為解釋玻璃在不同重力條件下的熔化和分相等現象提供了理論依據。The main point can be summarized as follows : a low - temperature elemental - direct - reaction route to nanocrystalline cdse and znse, and further more, by using the newly produced se with high reactivity as reactant, a controllable synthetic route named " selenite reduction hydrothermal method " have been developed
在合成新途徑的探索方面，從發現了水熱元素直接反應法，發展到亞硒酸鹽水熱還原法，提出了化學調控合成的新概念，為液相中金屬硒碲化合物的合成提供了可能的動力學調控手段和方法。The tbzre glass has great forming ability, which can form glassy body under relative slow cooling ratio. moreover, the technique of glass ' s annealing is easy. the npre - 1 glass has strong viscosity
其中亞碲酸鹽玻璃（ tbzre ）成玻能力強，在較慢的冷卻速率下也能得到非晶玻璃；且退火工藝簡單，退火溫度下保持一小時后再冷卻到室溫即可。分享友人