Some main results of testing research were as fellows : i. in the course of testing of leaching zinc dross, leaching zinc dross by sulfuric acid was researched and the effects on the leaching rate of the zinc dross were analyzed by author, the optimum conditions of leaching testing of zinc dross were determined as fellows : liquid - solid ratio 6 : 1, stirring ratio 250r / min, granularity 120 mesh, the soaking time 5h, the concentration of sulfuric acid of 30 %, and under these conditions, the rate of leaching zinc is above 92. 0 %. ii. in the course of testing of purification, on the basis of comprehending and comparing all present methods of the manganese - removal and iron - removal, the oxidizing method of manganese - removal in zinc sulfate solution using ammonium persulfate was put forward and the oxidizing method of iron - removal in zinc sulfate solution using the goethite process and oxidation - hydrolysis process was adopted
研究的主要結果具體如下: 1 、研究了硫酸浸出鋅浮渣並分析了影響浸出率的各種因素,確定了浸出鋅浮渣的最佳條件為:液固比為6 : 1 ,攪拌速度為250r min ,粒度為- 120目,酸浸時間為5 . 0h ,硫酸濃度30 ,鋅浮渣的浸出率大於92 . 0 ; 2 、在綜合和比較了目前除錳和除鐵的各種方法基礎上,提出了過硫酸銨氧化除錳方法和選擇了針鐵礦-氧化水解聯合法除鐵方法,並分析和討論了影響除錳率和除鐵率等各種因素,確定了除錳的條件為:溫度90 , ph值5 . 4 ,反應時間3h ,過硫酸銨達到理論值的1 . 2倍,除錳率超過99 . 86 ;聯合法除鐵的條件為:氧化反應時間1 . 5小時、溫度控制在90 92 、 ph值5 . 2 5On the base of the analysis on the advanced technology of hard ferrite in foreign country, the main procedures of preparing hard ferrite pre - sintering material are determined as follows : first, the ferrite oxides coming from the main cold rolling line and strontium carbonate are conveyed to storage tank by gas power and weighed automatically according to the demands of constituent composition. and then they are mixed and grinded by using method of wet treatment. finally the mixtures is transported to the devices of storage by transporting pump
在分析國外先進的永磁鐵氧體生產工藝的基礎上,確定了生產高檔永磁鐵氧體預燒料的主要過程:首先,利用攀鋼冷軋鐵紅為主要原料,將氧化鐵紅及碳酸鍶採用氣力輸送至貯料料倉,經自動稱量裝置,按工藝配方稱量後分別由氧化鐵紅及碳酸鍶發送罐氣力輸送進入預混攪拌筒加水攪拌,然後再送入混磨機濕法混磨;最後,混合物經輸送泵輸送至料漿存儲裝置,經定量進料泵定量輸送至回轉窯進行濕法預燒,預燒料經緩冷至室溫后,再球磨。The technique of cement power - sprayed piles is one of improving soft - soil roadbed technology presently. combining with the construction and field tests of nanjing - qidong railway, some research of using cement power - sprayed piles to improve soft - soil roadbed was conducted and the research includes several aspects below : 1. the authour first introduces the formation. distribution, physical mechancial behaviour and engineering characteristic of soft soil, and clarifies the necessity of improving soft - soil roadbed
本文結合寧啟鐵路工程的水泥粉體噴攪樁(簡稱粉噴樁)復合地基的現場施工及試驗,對粉噴樁加固軟土路基作了研究,具體研究內容包括以下幾方面: 1作者首先介紹了軟土的成因和分佈,軟土的物理力學以及工程性質,闡明了軟土加固處理的必要性及目前軟土路基加固處理的方法。It is believed that the slurry making method using electromagnetic stirring which is contactless stir ring will be suitable for high melting point iron and steel material
筆者認為電磁攪拌制備漿料方法中的攪拌是無接觸攪拌,更適用於高熔點鋼鐵材料。分享友人