oxychloride cement-
The microstructure of fly ash foamed concrete and the water resistance of magnesium oxychloride cement foamed concrete were analysed in virtue of sem method, at the same time, whose process to hydrate and carbonization resistance were analysed correspondly
藉助sem測試手段對粉煤灰發泡混凝土的微觀結構和氯氧鎂水泥基發泡混凝土的耐水性進行了機理分析,同時對其水化過程及抗碳化性能也進行了相應的機理分析。In this paper, the effects of fly ash, cement, lime, fine sands, foam agent, w / c ratio and additional agent on foamed concrete were studied by experiments, the best combination ratio of fly ash foamed concrete whose density varies from 551kg / m3 to 650kg / m3 was obtained through orthogonal test design, the foam agent quantity and the fly ash quantity effect the fly ash foamed concrete greatly, so the author selected them as independents to establish duality linear regression equations, the equations were quite ideal through the test of model summary r. moreover, the author also did some experiments about the water resistance of magnesium oxychloride cement fly ash foamed concrete, the outcome showed that phosphoric acid has good effect on water resistance, and its appropriate quantity was found
本文通過試驗研究了粉煤灰、水泥、石灰、細砂、發泡液、水灰比及外加劑對粉煤灰發泡混凝土性能的影響,採用正交設計試驗方法得出了600級粉煤灰發泡混凝土的最佳配合比,同時發現發泡液和粉煤灰摻量對發泡混凝土的影響最為顯著,因此,以二者為自變量建立了二元線性回歸方程,通過全相關系數的檢驗發現方程較為理想。此外,還對氯氧鎂水泥基粉煤灰發泡混凝土的耐水性進行了相關實驗,發現磷酸有較好的耐水性效果,同時找到了其合適的摻量范圍。Chemical industry information not merely embodyed the ordinary chemistry information substance, chemistry manufacture technological process and representative installation introduction are still have, in case contacing legal institutions sulphuric acid ? nitric acid industry system law ( ammonia oxidate law ), synthetic ammonia industry, chlorine and caustic soda are manufacture to electrolysis salt water, along with electrogilding, refine aluminium, iron - smelting and steel - smelting, cement and glass manufacture summarized account, the mineral oil is refined, hence, the chemical industry information education is contrastd against the ordinary chemistry information education, proper such representative means, be living, the means interpreted is in speech oridinarily wholly adoptd in the chemical industry information education, now most of tutors also is adopt the means interpreted in speech, cause that the chemical industry information education is insipid like this, student lack interest to chemical industry information study, but as a result of value the pair foundation, light practice, student may say the become a mere formality to chemical industry information study o since multi - med
化工知識不僅包含了一般化學知識的內容,還帶有化學生產工藝流程及典型設備的介紹,如接觸法制硫酸,硝酸的工業製法(氨氧化法) ,合成氨工業,電解食鹽水製造氯氣和燒堿,以及電鍍、煉鋁、煉鐵和煉鋼,水泥和玻璃的生產簡介,石油的煉制等,因此,化工知識教學與一般化學知識教學相比,應有其典型的方法。在過去,化工知識的教學一般都採用口頭講解的方法,現在大多數教師也是採用口頭講解的方法,這樣使得化工知識的教學乏味,學生對化工知識的學習缺乏興趣,又因重視雙基,輕實踐,學生對化工知識的學習可以說流於形式。由於多媒體的輔助教學的高效性、形象直觀性、新穎性和多樣性、人工模擬等特點,很適合化工知識的教學,應用多媒體教學化工知識可以解決目前存在的諸多問題,如:模型短缺、組織參觀活動困難、教育經費不足、學生不易觀察等。Magnesium oxychloride cement
鎂氧氯水泥Technical standard for glass fiber magnesium oxychloride cement and composite material ventilation duct
玻璃纖維氯氧鎂水泥通風管道技術規程Technical specification for glass filer ventilation duct with magnesium oxy - chloride cement
玻璃纖維氯氧鎂水泥通風管道技術規程The paper adopts such materials as common cement materials, mineral modified cement - based materials, polymer modified cement - based materials and epoxy resin and places emphasis on the polymer modified cement - based materials. polymers include np powder, sbr latex, acrylic acid latex, pure acrylic acid latex, chlorobutyl latex and epoxy latex
研究中採用的界面粘結材料有普通水泥基材料、礦物摻合料改性水泥基材料、聚合物改性水泥基材料和環氧樹脂,其中重點研究了聚合物改性水泥基材料,所用聚合物包括np粉末、丁苯乳液、丙烯酸乳液、純丙乳液、氯丁乳液、水乳環氧。分享友人