水渣混凝土 的英文怎麼說

中文拼音 [shuǐzhāhúnníngtǔ]
水渣混凝土 英文
foamed slag concrete
  • 水 : 名詞1 （由兩個氫原子和一個氧原子結合而成的液體） water 2 （河流） river 3 （指江、河、湖、海、洋...
  • 渣 : 名詞1 （渣滓） dregs; residue; sediment:煤渣coal cinder; 殘渣 dregs; 豆腐渣 soya bean residue; 豬...
  • 混 : 混形容詞1. （渾濁） muddy; turbid2. （糊塗; 不明事理） foolish; stupid
  • 凝 : 動詞1. （凝結） congeal; curdle; coagulate 2. （注意力集中） fix
  • 混凝土 : concrete; beton; jetereting混凝土壩 concrete dam; 混凝土板 concrete slab; 混凝土標號 concrete gra...
  1. After bfs is put into high strength superplasticized expansive concrete ( substituted for cement ), autogenous shrinkage does n ' t appear in 1 day standard curing, and e2 in 14 day ' s age is higher than that of high strength superplasticized expansive concrete without bfs in the same age

    高強流態膨脹混凝土摻入磨細礦渣（等量替代水泥）后，標準養護1天未出現自收縮， 14天的限制膨脹率明顯高於未摻磨細礦渣的高強流態膨脹混凝土的對應值。
  2. The author has done much research work in examining the functions of raw materials, as well as making graph analysis of the raw material. as a result, achievement have been made : ( 1 ) making sure of the standard factor and t he best mixture proportion, ( 2 ) finding out the best way of measuring the index of the high performance concrete, ( 3 ) the endurance of this high performance concrete and the volume stability have been experimented ; ( 4 ) the great economic and social benifit are obtained by cost analysis

    其主要工作進行了各種原材料的性能檢驗並做出相應圖表分析；對摻超細礦渣粉末的高性能混凝土進行正交試驗，確定了主要水平因子和最佳配合比；通過對高性能混凝土的耐久性試驗及高性能混凝土的體積穩定性試驗，確定檢測高性能混凝土耐久性指標的最佳方法及高性能混凝土的熱脹冷縮率和體積穩定性；通過對高性能混凝土的成本分析，確定摻超細礦渣粉的高性能混凝土其經濟效益和社會效益非常顯著。
  3. This product is extensive to used for all kinds of minerals, cement, fire - proof materials, aluminum soil the familiar anticipating, the emery, glass raw materials, mechanism building sand, stone materials, sand metallurgy of slag. it has the higher yield effect than other types, especially used to crush harder and causticity materials such as carborundum, emery, magnesium sand

    Pcl直通沖擊式破碎機制砂機特別適用於製作建築砂石磨料，耐火材料，水泥石英砂鋼砂爐渣粉銅礦石鐵礦石金礦砂混凝土骨料瀝青骨料等多種硬脆物料的細碎與中碎，是高效，節能的碎石制砂設備。
  4. Additions for concrete. ground glassy blastfurnace siag

    水硬性混凝土添加劑.細磨碎的玻璃狀渣.爐
  5. Ground granulated blast furnace slag used for cement and concrete

    用於水泥和混凝土中的粒化高爐礦渣粉
  6. In this article, the steel fibre is a kind of industrial wastes - stainless steel fibre dregs. the use of it is helpful in comprehensive utilization of resource and environment protection. the author of this article used orthogonal test design, arranged the test scheme scientifically, selected material, at last yield a high strength concret, whose strength exceeded c60, mainly by using 42. 5 ordinary portland cement, silica fume, superplasticizers, stainless steel fibre dregs and so on

    本文所用的鋼釬維是一種工業廢料?不銹鋼纖維渣，它的應用有利於資源的綜合利用和生態環境的保護本文在廣泛閱讀國內外有關資料的基礎上，採用正交設計，科學地安排試驗方案，精心選擇材料，用42 . 5普通硅酸鹽水泥、硅灰、高效減水劑、不銹鋼纖維渣等材料，採用常規工藝配製出了強度達到c60的高強混凝土，並且通過對試驗數據的分析，給出了最優配比方案。
  7. Finally, the author briefly discusses the application of reactive powder concrete with steel slag in engineering and produce, and points out that it is also a new emerging family ultra - high cement - based material

    最後，作者探討了鋼渣活性粉末混凝土在工程和生產製品中的應用，指出鋼渣活性粉末混凝土是有非常廣闊應用前景的新型的超高強水泥其復合材料。
  8. Abstract : during construction of the capital international airport ' s garage building project, the c50 and over c60 high performance concrete has been adopted for its construction. for the aim of 1, to get a maximum reduction of cement comsumption 2, to lower the concrete ' s hydration heat 3, to reduce concrete ' s shrinkage and cracks, and 4, to promote concrete ' s performance, a high quality chilled blast furnace superfine slag has been adopted as an admixture. furthermore, the adoption of some other minerals as the admixtures to get a high performance concrete has been carried out. as a result, these procedures and operations would have developed considerably the potential activity of concrete, and eventually the multiple performance and multiple function of concrete would have been improved and promoted. in conclusion a good result has been achieved in practice

    文摘:首都國際機場停車樓工程中，採用c50及c60以上高性能混凝土，為最大限度減少水泥用量，降低水化熱，減少收縮與裂縫，提高混凝土的性能，優選了有效成分含量高、質量好的水淬高爐礦渣磨細后單獨摻用，或再與其他礦物組分復合作為高性能混凝土的摻合料，以充分發揮礦渣的潛在活性，從而使混凝土的多項性能得到極大的改善和提高，並在實際應用中取得了良好的效果。
  9. During construction of the capital international airport ' s garage building project, the c50 and over c60 high performance concrete has been adopted for its construction. for the aim of 1, to get a maximum reduction of cement comsumption 2, to lower the concrete ' s hydration heat 3, to reduce concrete ' s shrinkage and cracks, and 4, to promote concrete ' s performance, a high quality chilled blast furnace superfine slag has been adopted as an admixture. furthermore, the adoption of some other minerals as the admixtures to get a high performance concrete has been carried out. as a result, these procedures and operations would have developed considerably the potential activity of concrete, and eventually the multiple performance and multiple function of concrete would have been improved and promoted. in conclusion a good result has been achieved in practice

    首都國際機場停車樓工程中，採用c50及c60以上高性能混凝土，為最大限度減少水泥用量，降低水化熱，減少收縮與裂縫，提高混凝土的性能，優選了有效成分含量高、質量好的水淬高爐礦渣磨細后單獨摻用，或再與其他礦物組分復合作為高性能混凝土的摻合料，以充分發揮礦渣的潛在活性，從而使混凝土的多項性能得到極大的改善和提高，並在實際應用中取得了良好的效果。
  10. When they mix each other, in one rate, they can compensate it ' s defect and improve the compability. 5 ) in the concrete with slag or fly ash, the changing of addition has more affection in slag ' s concrete than fly ash

    5 ）摻礦渣和粉煤灰的混凝土，外加劑摻量的變化對摻加礦渣的混凝土中的水泥與外加劑的相容性影響大於摻加粉煤灰的混凝土中水泥與外加劑的相容性。
  11. The result of experiment states hpc which initial slump is more than 230mm, after 120min is still above 190mm ; the 7d and 28d hydration, the compression strength of concrete is more than vompa and 90mpa can be made from the ground high - ti bfs instead of 10 - 30 percent of equal p. o. 525r, with the aid of superplasticizer and additive on the water cement ratio is 0. 26

    利用磨細的高鈦礦渣等量取代10 - 30的硅酸鹽水泥，並摻入高效減水劑b和外加劑ua ，在水灰比為0 . 26時，可以配置出初始塌落度大於230mm ， 120min后，塌落度仍大於190mm ， 7天強度大於70mpa ， 28天強度大於80mpa的高性能混凝土。
  12. Water cement ratio and mixing fly ash or slag into concrete effect on ability of resisting chloride penetrating that are considered in the model. the effect of environment that include temperature, relative humidity and cumulating of surface chloride concentration of concrete are also considered. moreover, chloride diffusion changing with time is included in this model as well as

    模型中考慮水灰比和混凝土配合比（摻入不同量的粉煤灰和礦渣）變化對混凝土抵抗氯離子侵蝕能力的影響，同時考慮溫度、相對濕度和表面氯離子濃度累積變化等環境因素對氯離子侵入混凝土過程的影響，以及氯離子擴散系數隨時間的變化。
  13. For details, the main contents are as follow : 1. the research is conducted on the confecting method of steel - slag concrete by indoor experiment. through comparison of the physical and mechanical properties between steel - slag concrete and plain concrete, it can analyze the advantages of using steel - slag concrete. based on the test results, empirical formulae is developed, which provides some bases for practical projects

    通過試驗研究了廢鋼渣作為原材料配製混凝土的方法，並將鋼渣混凝土與普通混凝土在配製過程中的某些性質指標作了比較，分析了其原因，並在試驗的基礎上建立了強度與灰水比經驗公式，為工程設計提供了依據。
  14. The result of macro - quality experiments show : mineral admixtures markedly slow the hydrating velocity of cement slurry, decrease and delay the hydrating max - temperature, in which steel slag is more effective ; expansive agents compensate concrete shrinkage, enhance the concrete dense degree, strengthen the interfacial layer between fiber and cement matrix and improve the physical mechanics qualities of acic ; minimal admixtures markedly improve the concrete workability property, increase the concrete later intensity & density and the capability of anti - chemical attack and anti - permeability ; hybrid fiber reinforces the toughness of obviously acic by the means of anti - cracking effect of fiber with different sizes and different properties in the corresponding construction levels

    實驗結果顯示：鋼渣摻合料能顯著減緩水泥漿體水化速率，降低砂漿的水化溫升並延遲最高溫升時間；補償混凝土收縮，提高混凝土密實度，加強纖維與水泥石的界面粘結，增強混凝土力學性能，但不能明顯改善混凝土韌性。混雜纖維通過纖維的不同尺度與不同性質在相應的結構層次上產生阻裂效應，增韌鋼渣防滲抗裂混凝土；增加混凝土的破壞極限能，極大提高混凝土抗彎曲能力和韌性指數，改善混凝土脆性。
  15. It analyzes the effect of water / binder ratio, percentage of silica fume and slag and super plasticizer on the strength of the high strength & high performance concrete. and then, the optimum of mix proportions of every composition is acquired according to the comprehensive equilibration theory

    分析了水膠比、硅灰摻量、礦渣摻量和高效減水劑摻量對高強高性能混凝土強度的影響，並根據綜合平衡法得出本文所採用的原材料體系的最優配合比。
  16. By research the effect of mineral mixture on cement and admixture, we can improve it ' s utility in cement concrete. in this article we use the slag and fly ash as research object. we study the effect of the mineral " s dosage on the compability of different fineness cement and admixture, the effect of mineral fineness to the compatibility of cement and admixture. wo also research the effect of mineral to different cement and admixture in chongqing. by the study, we continue changing the character of mineral to improve it ' s effect to compatibility. slag and fly ash mix each other can have better character to the compatibility of cement and admixture. changing slag by admixture and gypsm also can improve it ' s compatibility to cement and admixture

    礦物摻合料對水泥與不同摻量的外加劑之間的相容性影響。並結合重慶市現有的資源，研究了礦物摻合料對重慶地區不同廠家的水泥與外加劑的相容性影響。進而對礦物料的缺陷進行改善，採用礦渣與粉煤灰混摻，膨脹劑與礦渣混摻，礦渣與石膏，礦渣與外加劑混磨，優化礦物摻合料，更好的促使其在重慶市水泥混凝土中的應用。
  17. The main ingredient in concrete, cement is made by heating limestone and clay until they fuse into a material called clinker, which is then ground up and mixed with various additives

    混凝土中的主要成分水泥的生產是通過加熱熔解石灰石和粘土，生成一種名為溶渣的物質，然後再對溶渣進行碾磨，並加入各種添加劑加以混合。
  18. Furthermore the systematical investigation on the pozzolanic activity of the compound admixture of lithium - salt residue and fly ash has been carried out. it can confect high performance concrete for hydraulic engineering. the main results in this paper are as following : 1

    本課題還對鋰鹽渣-粉煤灰復合摻合料活性進行了深入系統的研究，該復合摻合料與外加劑共用，可配製大摻量復合摻合料高性能水工混凝土。
  19. The mechanical properties of steel - slag concrete prevails more advantages than the plain concrete, also the quantities of cement and gravel are reduced, consequently reducing the capital cost of the project materials, so this method is economically and safely to be used and it can solve the environmental problems of unused steel - slag

    配製出的鋼渣混凝土力學性能比普通混凝土力學性能要高，而且節省了水泥和石子，具有很好的經濟效益。由於利用了廢物，變廢為寶，解決了環境污染問題，故又有很好的社會效益。
  20. As a new mineral additive of cement and concrete, ground steel - making slag powder has quite high activity and its activity is obvious higher first grade fly ash and close to blast furnace slag. furthermore, its distribution is very wide and quantity is quit plenty in our country

    磨細鋼渣粉作為一種新的水泥混凝土摻合料，它的活性明顯優於一級粉煤灰，與礦渣活性不相上下，而且分佈較廣，數量較多，有較高的應用與研究價值。