oil temper wire-
Induction heated oil tempered spring wire is a kind of new technical material which has been developed since 1980s. it can be heated by means of eddy induced into itself through electromagnetic coil and this method is mainly used in surface quenching. with correct designing and reasonable current frequency, induction coil and heat treatment process selected, as well as plc controlling applied, the wire can be uniform heated along cross - sectional and longitudinal direction and can be quenched and tempered continuously
應加熱油淬火-回火彈簧鋼絲,是二十世紀八十年代發展起來的新技術材料,在國外稱為itw induction heat oil tempered spring wire 。是通過線圈電磁感應鋼絲本身產生的渦流進行加熱,通常主要用於表面淬火。經正確設計,選擇電流頻率,合理的感應線圈及熱處理工藝,並實施plc控制,可使鋼絲整個截面及長度上得到均勻加熱,進行連續整體淬火和回火。Hot - rolled wire rod for quenched and tempered springs
油淬火-回火彈簧鋼絲用熱軋盤條Oil - hardened and tempered stell wire for mechanical springs
油淬火回火彈簧鋼絲Oil tempered carbon steel spring wire and springs
油回火碳素鋼彈簧鋼絲和彈簧Oil tempered chromium - vanadium valve spring quality wire and springs
油回火鉻-釩汽門彈簧優質鋼絲和彈簧Standard specification for steel wire, oil - tempered carbon valve spring quality
閥簧級油回火碳素鋼絲的標準規范Steel wire for mechanical springs - oil hardened and tempered spring steel wire
機械彈簧鋼絲.油硬化和回火的彈簧鋼絲Sino - foreign joint venture nanjing dongwu metal material co., ltd. is a hi - tech enterprise which specially produces and sells induction heat oil tempered spring wire and die pusher rod
中外合資南京東吳金屬製品有限公司是一家專門生產經營感應加熱油淬火-回火彈簧鋼絲冷鐓鋼絲軸承鋼絲異形鋼絲退火磨光定尺線材冷拉鋼絲和模具推桿線材的高新技術企業。Oil tempered carbon steel valve, spring quality wire, and springs
油回火碳素鋼閥彈簧鋼絲和彈簧Steel wire for mechanical springs - part 3 : oil - hardened and tempered wire
機械彈簧用鋼絲.第3部分:油淬火和回火鋼絲Steel wire for mechanical springs - part 2 : oil hardened and tempered spring steel wire
機械彈簧用鋼絲.第2部分:油淬火和回火彈簧鋼絲Steel wire for mechanical springs - part 2 : oil hardened and tempered spring steel wire ; german version en 10270 - 2 : 2001
機械彈簧鋼絲.第2部分:油淬火和回火彈簧鋼絲Due to the rapid heating rate, the time for wire stayed in high temperature zone is very short and no enough time for grain grows largely, hence the structure size of continuously induction heated wire is smaller than that of conventional heated wire and grain size is 2 to 4 level higher. due to the fine grain size, the induction heat oil tempered spring wire can acquire more reasonable comprehensive mechanical properties under same strength
可見,由於加熱快,在高溫停留時間短,組織晶粒來不及長大,因此,連續感應加熱鋼絲的組織晶粒尺寸比一般加熱小,晶粒度高2 - 4級。由於組織晶粒尺寸細小,因此,感應加熱油淬火-回火鋼絲,在同樣強度下,具有更高的綜合b力學性能。Induction heat oil tempered wire and rod can be directly used in the manufacture of spring and pusher and the quenching - tempering process thereafter can be omitted, thus the quality problems such as deformation of workpiece, decarburization, un - stability and un - qualification of mechanical property can be avoided and the quality stability and reliability of product can be improved
感應加熱油淬火-回火鋼絲及線材,能直接用於繞簧和製造推桿,可省去一般材料繞簧和推桿加工成形后的淬火-回火工序,避免了由此帶來的工件變形脫碳及力學性能不穩定甚至不合要求等質量問題,提高了產品的質量穩定性和可靠性。Standard specification for steel wire, oil - tempered for mechanical springs