淬火表面 的英文怎麼說

中文拼音 [cuìhuǒbiǎomiàn]
淬火表面 英文
hard surface
  • 淬 : 動詞（淬火） temper by dipping in water, oil, etc. ; quench
  • 火 : fire
  • 表 : Ⅰ名詞1 （外面;外表） outside; surface; external 2 （中表親戚） the relationship between the child...
  • 面 : Ⅰ名詞1 （頭的前部; 臉） face 2 （物體的表面） surface; top 3 （外露的一層或正面） outside; the ri...
  • 表面 : surface; superficies; boundary; face; rind; sheet; skin; outside; appearance
  1. The case-hardening or carburizing process is in wide use.

    表面淬火或滲碳法應用十分廣泛。
  2. Induction heated oil tempered spring wire is a kind of new technical material which has been developed since 1980s. it can be heated by means of eddy induced into itself through electromagnetic coil and this method is mainly used in surface quenching. with correct designing and reasonable current frequency, induction coil and heat treatment process selected, as well as plc controlling applied, the wire can be uniform heated along cross - sectional and longitudinal direction and can be quenched and tempered continuously

    應加熱油淬火-回火彈簧鋼絲，是二十世紀八十年代發展起來的新技術材料，在國外稱為itw induction heat oil tempered spring wire 。是通過線圈電磁感應鋼絲本身產生的渦流進行加熱，通常主要用於表面淬火。經正確設計，選擇電流頻率，合理的感應線圈及熱處理工藝，並實施plc控制，可使鋼絲整個截面及長度上得到均勻加熱，進行連續整體淬火和回火。
  3. Smooth tempered glass is manufactured by heating up float glass to swiftly and uniformly, with this special heat treatment and quenching process which increases glass strength up to four to five times vs, annealed glass, in case stresses beyond its capacity, smooth tempered glass simply disintegrates into innumerable small pieces, significantly reducing the risk of serious injury

    鋼化玻璃是將浮法玻璃經過物理性淬火處理，使其表面形成均勻的壓應力，而內部則形成張應力，從而有效的提高了玻璃的抗彎和抗沖擊性能，強度達到了普通玻璃的3 - 4倍，當其破碎時則分裂成均勻純角不易傷人的小顆粒，使其成為一種現代生活中理想的安全玻璃。
  4. Abstract : in this paper, the surface of the ore milling roller was quenchedby the laser, so that increase its surface rigidity and improve its antiwear properties, and prolong its life

    文摘:應用激光束對磨輥表面進行淬火處理，提高磨輥表面硬度，增強磨輥的抗磨損性能，從而達到延壽的目的。
  5. It is shown from results that increasing carburizing time further in the normal technology can not obviously deep the carburizing layer, but can cause nonmartensite microstructure at the bottom of the gear and coarse grain across the gear, these will heavily decrease the fatigue life of the gear

    結果表明：在正常滲碳淬火工藝基礎上再延長滲碳淬火1小時，齒輪滲碳層深度變化不大，但其齒根局部表面處有非馬組織，且晶粒尺寸易產生異常長大現象，從而致使臺架疲勞壽命明顯下降。
  6. Features : hardened and precision - ground bedways, the spindle is supported with precision taper roller bearings, gears in the headstock are made of high - quality steel, hardened and ground, speed - changing levers driven by fan - shaped gears, operating easily, safe interlock and a overload safety devices in apron, electromagnetic braking, cooling and lighting devices are supplied

    特點：床身導軌表面經淬火和精密磨削，主軸支撐採用精密圓錐滾子軸承，主軸箱內齒輪採用優質鋼並經表面淬火和磨削，變速機構採用扇型齒輪傳動，操作靈活方便，溜板箱設有安全互鎖裝置和過載保險機構，配有電磁剎車、冷卻及照明裝置。
  7. Steel products. determination of the effective depth of hardening after flame or induction hardening

    鋼產品.表面或感應淬火后硬化有效深度的測定
  8. Iron and steel. heat treated special steels for quenching after surface treating. types

    鋼鐵.表面處理后淬火用熱處理的特殊鋼.類型
  9. Austemper case hardening

    等溫淬火表面硬化
  10. Sf - gp - cyp - iii mainly used for surface quenching, welding, metal powder sintering tube seam annealing and metal parts heat penetrating

    主要用於鋼鐵機械零件的表面淬火釬焊粉末金屬的燒結，鋼管焊縫的退火，以及金屬部件的透熱等。
  11. The reason analysis of the formation of surface pores on quenched camshafts

    凸輪軸重熔淬火表面孔洞缺陷形成原因分析
  12. Heat treatment of ferrous materials - methods of heat treatment - part 5 : surface hardening

    鋼鐵材料熱處理.熱處理方法.第5部分:表面淬火
  13. Strengthening mechanism of ion nitriding is different from surface quenching and cementation, which makes surface strengthen by quenching to get martensite. ionic nitriding is the way to make materials strengthe n, which result from the steady compound formed on the surface of the metal. there is no need for quenching after treatment

    離子滲氮的強化機理不同於表面淬火，滲碳等表面熱處理方法，這些方法必須進行淬火得到馬氏體使表面強化，而離子滲氮是在金屬表面形成穩定化合物而使材料強化，處理后不須淬火。
  14. Standard test method for non - destructive photoelastic measurement of edge and surface stresses in annealed, heat - strengthened, and fully tempered flat glass

    在退火淬火和全回火平面玻璃中邊緣和表面應力的無損光彈性測量的標準試驗方法
  15. The difference among the elasticity modulus of various microstructures is probably the main reason, which caused the experiment results above. under the same experiment conditions, such as sample shape, size, surface roughness, establishment of testing system, pressure on the probe, and thickness of coupling medium, the variety of relative attenuation coefficient ( or ) in different heat treatment samples is measured and compared by measuring the attenuation obtained from the cylindrical surface of column. the result is as following : for 40cr and 38crmoal, a mt < az mq < a s < a p + f ; for gcrlssimn, a mt < a annea < s < a p + f ; and a increased with the increasing of frequency

    在保證試樣形狀、尺寸、表面光潔度、系統參數設置、施加在探頭上的壓力以及耦合層厚度等測試條件一致的情況下，利用棒材圓柱面測衰減系數法，分別測定並比較上述不同熱處理試樣相對衰減系數的變化情況，得到的實驗結果是：對於40cr及38crmoal鋼， _ （低溫回火） （淬火） _ （高溫回火） _ （正火） ；對于gcr15simn鋼， _ （低溫回火） _ （退火） _ （高溫回火） _ （正火） ；且隨著頻率的提高，衰減系數均呈現增加的趨勢。
  16. Technology of laser quenching treatment 40cr steel surface

    鋼表面激光淬火的工藝研究
  17. Abstract : compared with the normal technique the paper introduces many advantages of the laser quenching the ductile iron crankshaft

    文摘:介紹了激光淬火球鐵曲軸與常規的曲軸表面處理方法相比有許多優點，提出了一種激光淬火球鐵曲軸圓角部分掃描的新方法。
  18. I. investigation on laser surface hardening for metal materials in this work, the effect of the process parameters in laser surface hardening on the properties and surface feature of the hardened layer was studied

    一、金屬材料激光表面硬化技術研究。研究了激光表面淬火工藝參數和硬化層性能、強化效果之間的關系，對大面積激光淬火技術的基礎理論及搭接方法對組織性能的影響規律進行了探討。
  19. Ferrous metals, non - ferrous metals, ic thin sections, coatings, ply - metals ; glass, ceramics, agate, precious stones ; hardness testing such as that on the depth and the trapezium of the carbonized layers and quench hardened layers

    黑色金屬、有色金屬、 ic薄片、層壓金屬、表面塗層；玻璃、陶瓷、瑪瑙、寶石等；炭化層和淬火硬化層的深度及梯度的硬度測試。
  20. The reasons why surface of workpiece is moistened from bottom to top in quenching and axial hardness gradient is generated after quenching are also given in this paper

    對試驗中所觀察到的工件表面由底部向頂部逐漸潤濕的現象，以及淬火后工件產生軸向硬度梯度的原因進行了解釋。