滲氫 的英文怎麼說

中文拼音 [shènqīng]
滲氫 英文
hydrogen charging
  • 滲 : 動詞（液體慢慢地透過或漏出） ooze; seep
  • 氫 : 名詞[化學] （氣體元素） hydrogen （h）
  1. Hydrogen embrittlement of 2205 duplex stainless steel has been evaluated using electrochemical permeation measurement, hydrogen microprint technique and slow strain rate tensile test in this study

    摘要本實驗主要利用電化學氫滲透量測、氫原子微印技術及慢速率拉伸試驗，針對2205雙相不?鋼的氫脆性與氫原子擴散方式的關系進行探討。
  2. Objective to study the effect of zinc - oxide phosphorate base on preventing hydrogen peroxide leakage in intracoronal bleaching

    摘要目的研究髓室內漂白時，磷酸鋅水門汀基對抗過氧化氫滲漏的作用。
  3. While cyclic deformation experiment under constant strain control is performed in 400, the material shows the continuous hardening until cyclic invalidation. ( 3 ) back stress attained by kwl " s method is used to analyse the bauschinger effect during an incremental step cyclic test and cyclic deformation test under constant strain control, it is shown that back stress increases with increasing plastic strain and the numbers of cycle, and the back stress is uniform, regardless of tension or compression conditions. ( 4 ) as far as recrystallized zircaloy - 4 plate is concerned, the back stress in transverse direction is higher than that in rolling direction due to the higher schmid factor in rolling direction

    對于再結晶狀態的zr一4合金板材試樣來說， t方向（橫向）試樣的背應力要高於r方向（軋制方向）的背應力，原因在於r方向的schmid因子高於t方向的schmid因子; 400下， zr一4合金的背應力要明顯低於室溫下的背應力;含氫200pg / g的zr一4合金的背應力大小與無滲氫的zr一4合金背應力相比，無明顯區別;固溶處理后， zr一4合金的背應力大小發生了變化，在較高塑性應變下，背應力均高於固溶處理前的背應力。
  4. The hydrogen permeation experiment of manet ii with hot dipping aluminized coating was performed in temperature range of 300 to 450, in gas phase and in liquid pb - 17li phase

    在300 450溫度范圍內，分別在氫氣相和液態鉛鋰合金相中開展了帶熱浸鋁塗層manet馬氏體鋼的氫滲透性能研究。
  5. Aiming at the problems in testing strata with low permeability, hydrogen sulfide - bearing wells and high temperature and pressure, a whole set of mature testing technology and doable construction programs are worked out, which turn out to be mature in technology, secure in construction and objective and accurate in testing results examined by practical construction

    摘要針對低滲透地層測試、含硫化氫井的測試及高濕高壓井測中存在的問題，經過不斷探索和實踐，形成了一整套成熟的測試技術和切實可行的施工方案，經實際施工檢驗證明，技術成熟，施工方案安全可靠，測試結果客觀準確。
  6. Analysis of desquamation of hydrogen permeation barrier in co

    2中氫滲透阻擋層脫落分析
  7. A polyaniline / polyisoprene composite film with permselectivity was synthesized by electrochemical method for the first time, which can determine selectively h2o2 in the presence of electroactive interferent ascorbic acid

    採用電化學方法首次制備了具有特殊滲透選擇性的聚苯胺/聚異戊二烯復合膜，它能在抗壞血酸存在下讓過氧化氫選擇透過。
  8. The zircondri filin wtut rirconia wa prepared and the removing technology of the zirconia on the zirconium sdrices was obtalned. the methods of chemistry and magnetron sputtring plating were used in order to platc a palladium film, which is characteristic of self catalysis for hydrogen and the sole h - permselectivity on the clean rirconium sdrices prepared by the methods of electrochemitw and ( or ) high temperatur vacuum hydrgenization, which was firstly studied. the plating tedrilogy was obained and the surface modified zirconium membran was prepared

    在利用電化學法和真空高溫除氧加氫法去除了鋯表面氧化膜的基礎上，分別採用化學法、磁控濺射法兩種鍍膜技術在其表面上鍍上了一層對氫具有自催化分解、唯一選擇滲透性的金屬鈀膜，首次獲得了鋯基材膜表面上鍍鈀的制備工藝，成功制備了鋯表面改性選擇滲氫膜。
  9. Behavior of hydrogen permeation in zn - ni alloy electrodeposition

    合金電沉積過程中的滲氫行為
  10. Method of measurement of hydrogen permeation and determination of hydrogen uptake and transport in metals by an electrochemical technique

    氫滲透的測量方法和用電化學法測定金屬中的氫吸收和遷移
  11. The hydrogen permeation reduction factor ( prf ) evaluated in gas phase is 620 ~ 263 and in liquid pb - 17li phase is 45 ~ 30

    結果表明，實驗所得到的氫滲透率減低因子（ prf ）為：在氣相中， 620 263 ；在液態鉛鋰合金相中， 45 30 。
  12. Methods intracoronal bleaching was given to exsomatized teeth, and the amounts of penetrated hydrogen peroxide was determind by spectro - photo - metry

    方法對離體牙行內漂白，用分光光度法檢測過氧化氫滲漏量。
  13. The sims, ir and raman analysis results show that the tritium permeation barrier ( tpb ) is formed when tic and sio2 films are annealed in hydrogen at about 350 ?

    利用二次離子質譜（ sims ） 、紅外吸收光譜（ ir ）及激光喇曼光譜（ raman ）技術，證實了tic和sio2在350左右的氫中退火可形成防氚滲透阻擋層。
  14. Supply of concentrate haemodialysis solution with bicarbonate powder buffer to the hospital authority and the department of health as a 24 - month contract from date of acceptance design, supply, delivery, installation, commissioning, maintenance of hardware, software and related services for the implementation of the automated tag and information display system for the immigration department on or before december 2006 supply of 320 000 kg. of polyelectrolyte type ii to the drainage services department as a 36 - month contract from date of acceptance provision of dental laboratory work for the department of health as a 24 - month contract from date of acceptance supply, installation and commissioning of a ground reception system for meteorological data from multi - functional transport satellite for the hong kong observatory from date of acceptance to fulfillment of contractual obligations supply and installation of 1 set of automated dna sequencing system to the department of health from date of acceptance to fulfillment of contractual obligations

    承投為醫院管理局和?生署供應高濃度血液滲析液連炭酸氫鹽緩沖粉劑，合約由發出接納書日期開始，為期24個月為入境事務處於2006年12月或之前推行自動化籌號及資訊顯示系統供應硬體和軟體，包括設計、送貨、安裝、試機、保養及有關服務為渠務署供應320000公斤高分子電解質（第ii類） ，合約由發出接納書日期開始，為期36個月為?生署提供牙科製品服務，合約由發出接納書日期開始，為期24個月為香港天文臺供應一套多用途輸送衛星氣象數據地面接收系統，包括安裝及試機服務，由發出接納書當日至履行合約訂明的責任為止為?生署供應和安裝一套核酸序列自動測定系統，由發出接納書當日至履行合約訂明的責任為止
  15. The oxide film of zirconium on the sdses conceals its high hydrogen permeability because of its self passive effect with oxygcn, which limits its application as high h - permse1ective membran

    1幾個納米厚的氧化鋯膜掩蓋了其本體的滲氫性能，使其在作為高選擇滲氫膜的應用上受到限制。
  16. To deal with gas separaion at high pressure and high temperature, inoghc membranes are used widely in the ligh of the production and the uitrahigh purity of hydrogen isotope requlred by some special professions and the defects of the current einpoyed membranes separation technology the preparation teehnology of high h - permselective membrane

    在涉及高溫、高壓環境下的氣體分離中，主要使用的是無機膜分離技術。針對特殊行業對氫同位素氣體處理量及超高純度的需求和現有膜分離技術存在的問題和不足，創新性地提出了利用耐熔金屬鋯等對氫的高滲透性，制備高選擇滲氫膜的分離技術。
  17. However, the lcf of r specimen containing - 200 g / g hydrogen is better than that of the hydrided t specimen, and shows slightly superior to unhydrided r specimen, whereas the hydrided t specimen has not the apparent difference as compared with t specimen

    與室溫下未滲氫態試樣相比，滲氫后r向試樣的低周疲勞性能稍稍優于未滲氫態r向試樣，但對t向zr一4合金試樣，滲氫對其室溫低周疲勞性能幾乎沒有影響。
  18. The prepared sdse modified zirconum meinbrane was tested at the wider range of tcmperaure and pressure and differellt composihons of hydrogen mixturc gases ( i. e. different hydrgen panal pressure ) in order to examine the performance of this membrane and the sole hpermselechvity of the membrane. the results showed tha the purity of the permeated hydrgen is l00 % at the base of the detection greatest lower lanit of the qhle mass spectrometer, and there was no impurity gas passed, the permeating flux and permeability of this membrane are from several decades times to one decade times more higher than tha of a palladum membran in the range of from 593k to 773k, puv = 0. 2 ~ 0. 3mpa, pdn = 4x l04pa - - 0. lmpa, the hydrogen permeatng flux is increased with the difference of the squto root of pressure, and presents a linear relationship, the pressure seems has no influence on the permeablity, the permeabi1ity is decreased with the increasing of the temperature, and presents an exponential relationship, accondng to the fitting curve of the relationship betwen the permeability and the temperatur derived from the experimenta daa, in the range of 593k ~ 773k, pup0. 2 ~ 0. 3mpa, pha = 4 x l0 # pa ~ 0

    在更寬的溫度范圍、壓差范圍內，在不同原料氣組成（即不同的氫氣分壓）條件下，對所制備的鋯表面改性膜進行了滲氫性能實驗，考核了膜對氫的唯一選擇滲透性，結果表明：在四極質譜的檢測下限內，只有氫氣存在，而無雜質氣體通過；在593k 773k溫度范圍內，鋯表面改性選擇滲氫膜具有高於鈀膜數十倍至十幾倍的滲氫流量和滲氫系數；其滲氫流量隨著膜兩側氫分壓平方根摘要差的增大而增大，並且呈線性關系；壓力對膜的滲氫系數幾乎無影響；膜的滲氫系數隨著溫度的升高而下降，井巨呈指數關系：根據對實驗數據所作滲氫系數與溫度關系曲線的擬合，在溫度593k 773k范圍內，壓差p 、 0二0
  19. Lmpa, the relationship is f di = l 55xl0 - " e47j l t ) in this range, the relative error of the hydrgen permeabilty bbeen the experimental values and the formula values are less than 3 %, the durability test showed that after the cycle experiments of prcssure and tempebe for 30 days, the perfrmance of the membran did not change, at last, the theory of hydrogen permeaton was discussed, too. through this work, the pfepared surf ases modified zirconium memran can satisfy the requirement of the purity and the permeating fiux of hydrogen isotope gas

    Imp范圍內，鋁表面改性選擇滲氫膜的數學表達式為： （ 1320 i 155x10 」 exd l 「 t ）在這個溫度和壓差范圍內，滲氫系數的實驗數據計算值與數學公式計算值的誤差在3以內；鉻表面改性選擇滲氫膜的壽命考核實驗表明，經過連續30大的循環溫度、壓力實驗，膜的質量、性能無變化；並討論了膜的滲氫理論。
  20. At room temperature, the fracture for r specimen is the characteristic of fatigue stripe, while tire - like pattern appears on the fracture of the t specimen, and the hydrided sample is characterized by skeleton - like pattern and quasi - cleavage fracture at room temperature. however, the fracture characterized by second - crack at 400

    常溫下， r向試樣的低應變幅疲勞斷口上較為明顯的特徵是疲勞條紋的存在; t向試樣的疲勞裂紋擴展區斷口上則為輪胎痕花樣;滲氫態試樣室溫下疲勞斷口的主要特徵為脊骨狀花樣和準解理斷裂特徵。