And the finite element method ( fem ) was used to simulate the stress and deformation of the outer casing and the bearing chock. on the basis of the experiments and fem analysis, the strength and fatigue lifetime, the interaction of creep and fatigue lifetime, the creep lifetime of outer casing and bearing chock have been analyzed, at the end of trail, sem analyses of failure section has been conducted
同時對航空發動機燃氣渦輪外機匣和軸承座進行了有限元模擬計算,得到外機匣和軸承座的焊接處的強度和變形情況的模擬結果。根據試驗數據和有限元的計算結果,對發動機燃燒室外機匣和軸承座兩種結構(包含焊縫)進行靜強度分析、疲勞壽命分析、蠕變壽命分析、蠕變疲勞交互作用壽命分析以及斷口的金相分析。The results show that : the strength and fatigue lifetime of the outer casing including welding line can satisfy the design requirement. although the some parts of bearing has been yielded, the strength at the weld is large enough for requirement. and welding defect, indicted by sem analyses of failure section, is main reason affecting fatigue lifetime
分析結果表明:外機匣(包含焊縫)強度和壽命滿足設計強度和壽命的要求;軸承座的強度已經進入屈服階段,而軸承座及其焊縫處的壽命卻是滿足設計壽命要求;另外斷口的金相分析表明焊接缺陷的存在是影響疲勞壽命的主要原因之一,故需提高焊接技術,減少焊接缺陷的存在以提高焊接結構的壽命。
分享友人