焙燒制度 的英文怎麼說

中文拼音 [bèishāozhìdù]
焙燒制度 英文
firing regime
  • 焙 : 動詞（用微火烘） bake; torrefy; heat over a slow fire
  • 燒 : Ⅰ動詞1 （使東西著火） burn 2 （加熱或接觸某些化學藥品、放射性物質等使物體起變化） cook; bake; hea...
  • 制 : Ⅰ動詞1 （製造） make; manufacture 2 （擬訂; 規定） draw up; establish 3 （用強力約束; 限定; 管束...
  • 度 : 度動詞[書面語] （推測; 估計） surmise; estimate
  1. Hence we combined coprecipitation method, using zinc carbonate as enclosure dose causing the crystal nucleus can not grow up, zinc titanate acts as phase - transition accelerant, thereby we can obtain rutile nanometer tio2 powder at lower calcining temperature and in briefer calcining time relatively

    因此我們結合共沉澱法，引入碳酸鋅作包覆劑控製品粒長大，利用鈦酸鋅作品型促進劑，在相對較低的焙燒溫度和較短的保溫時間內制得到了金紅石型納米tio _ 2粉體。
  2. In this paper, concentrated sulfuric acid and titanium dioxide are used to prepare the tios04 solution that test later required under long time heat. the influences of reaction time and reaction temperature to yield of tioso4 are discussed. in the experiment of preparing tio2 powder, reaction temperature, ph values, material ratio, operation way, velocity of feed, calcining heat and time are researched by the principle of nucleation and growth in thermodynamics and kinetics

    在制備tio _ 2粉體實驗中，根據成核生長的熱力學和動力學原理，深入分析了沉澱反應時環境的溫度、 ph值、反應物配比、操作方式、加料速度等因素對ti （ oh ） _ 4粒度的影響，以及焙燒溫度和保溫時間等因素對制得的納米tio _ 2粉體性能的影響，得出了制備銳鈦型納米tio _ 2粉體的優化工藝條件。
  3. The effect of amorphous hydrated ruo _ 2 power production is discussed here, including : selection and ratio of solvent, selection and concentration of precipitator, terminal ph of titration and anneal temperature and time of colloid. research indicated that terminal ph and anneal temperature are the most important influence factors on physical and electrochemical properties of amorphous hydrated ruo _ 2 power

    討論了超細氧化釕粉體的制備影響因素，包括:溶劑選擇和配比、沉澱劑選擇和濃度、滴定終點ph值以及焙燒溫度和時間對氧化釕粉體粒度分佈及電化學的影響，研究表明:沉澱終點ph值以及膠體焙燒溫度對粉體物理和電化學性能影響較大。
  4. The baking condition of perovskite - type oxide is confirmed by means of tg - dta

    通過熱失重-差熱分析，確定了鈣鈦石型氧化物的焙燒制度。
  5. Abstract : abstract according to the testing results in the shaft furnace, the problems of pellets roasting and heat transferring in the furnace caused by using bf gas were analyzed, and some countermeasures for reformation were proposed

    文摘:根據球團豎爐工業測試結果，從焙燒制度和熱工制度等方面分析了用高爐煤氣作燃料的豎爐存在的問題，提出了球團豎爐強化焙燒的方向。
  6. Lifepo4 / c composite sample synthesized using coal tar bitumen and carbon both as the carbon precursor under 300 / 3 h + 650 / 6 h also gives a good discharge curves, the discharge specific capacity reached 104. 0 mah / g 、 100. 2 mah / g under the measuring current of 183 ma / g 、 366 ma / g respectively, and it keeps the good cycle performance in nearly 140 cycles. few reports were related to the lifepo4 / c composite synthesized using low cost bitumen as the carbon precursor

    採用煤焦油瀝青和乙炔黑同時作為碳前驅體時，在300 / 3h + 650 / 6h的焙燒制度下得到的試樣，在183 、 366ma / g的大電流密度下仍有104 . 0mah / g 、 100 . 2mah / g左右的放電容量，在140次循環內均表現出了很好的循環性能。
  7. The more favorable experiment conditions of preparing anatase nanometer tio2 powder are obtained from a lot of data. preparation technology of rutile nanometer tio2 powder is researched on the base of experiment of anatase nanometer tio2 powder. the influences of enclosure dose ' s quantity, preroasting temperatures phase - transition accelerant ' s quantity and calcining intensity and so on on the properties of inclusion body - zntio3 / ti ( oh ) 4, granule size and properties of rutile nanometer tio2 powder are discussed

    在銳鈦型納米tio _ 2粉體的制備基礎之上，進一步研究了金紅石型納米tio _ 2粉體的制備工藝，探討了包覆劑用量、預焙解溫度、晶型促進劑量及焙燒溫度和保溫時間等因素對znco _ 3 / ti （ oh ） _ 4沉澱包覆體性能、金紅石型納米tio _ 2粉體產品的粒度和性能的影響。
  8. The reaction activity of the catalyst can be adjusted by changing the preparing condition, which including the calcination temperature, the metal load and the carrier

    制備過程中焙燒溫度、負載量以及不同催化劑載體的選用都會影響所得催化劑的性能。
  9. Due to preparing high grade rutile nanometer titanium dioxide in the same method have more disadvantages such as tall calcining heat, easy agglomerate, reunite gravely and difficult to attain the nanometer grade

    由於用與之相同的方法制備金紅石型納米tio _ 2粉體存在焙燒溫度高、易燒結、團聚現象嚴重等缺點，難以達到納米級。
  10. In this paper, the optimum conditions of catalyst preparation were found by studying the influences of the sol - gel process parameters on the crystal structure of the nanometer la1 - xsrxmno3, such as the value of original solution ph, the temperature of water bath, the baking temperature of sol

    本文研究了採用溶膠-凝膠法制備納米鈣鈦石型氧化物催化劑過程中，初始溶液ph值、水浴溫度、焙燒溫度對納米la1 - xsrxmno3晶體結構影響。
  11. In order to overcome the disadvantages of traditional solid brick, to protect environment and to economize resources, the author first recommended the experimental study of drying and firing of coalstore - shale fired perforated brick. the result assumed the effect of percentage of water content, raw material fineness, temperature and insulation time on property of coalstore - shale perforated or hollow brick

    論文首先針對傳統實心磚存在的問題，從環境保護和資源綜合利用出發，以頁巖、煤矸石為原料制磚，通過頁巖、煤矸石制磚中乾燥、焙燒試驗研究，總結了原料化學成份、顆粒粗細程度、乾燥速度、含水率以及焙燒溫度等因素對煤矸石多孔磚、空心磚性能的影響。
  12. Methods of sampling and test for carbonaceous materials used in aluminium manufacture - electrode coke - determination of tapped bulk density of green and calcined coke

    制鋁工業用炭素材料取樣與試驗方法.第2部分:電極用焦炭.第13節:未焙燒焦炭和焙燒焦炭散裝密度測定
  13. By the increasing of temperature, liyco3 - xo4 was further changed into licoo2 and lixco1 - xo, and then licoo2 formed by the reaction of lixco1 - xo with li2o. the reaction that produces licoo2 is almost completely done at 700, although some remaining li2o and li2co3 present as a partially amorphous film dispersed on the surface of licoo2, which can accelerate the growth of licoo2 crystallites. however, when temperature is higher than 850, some of licoo2 begin to decompose into the solid solution phase of liyco2 - yo2 and lixco1 - xo, and damaged its own crystal structure

    制備licoo _ 2的合成反應中licoo _ 2的微結構不斷發生變化，隨著焙燒溫度升高， co _ 3o _ 4晶粒逐漸減小， licoo _ 2晶粒和顆粒逐漸長大，晶格內部缺陷減少， licoo _ 2晶格趨于完整，在焙燒溫度為850時licoo _ 2晶粒達到最大值；焙燒溫度低於700 ，晶胞參數a隨著焙燒溫度上升而減小，晶胞參數c隨著焙燒溫度上升而增大；而高於700則晶胞參數基本保持不變。
  14. Through the synthesis of licoo2 by using non - water dispersant and two - step roasting, influences of microstructures of precursor, the roasting temperature and the reaction time on the electrochemical properties of licoo2 were studied. it indicated that co3o4 with nano - crystalline have very good electrochemical property, and can shorten solid reaction time

    02的制備工藝，考察了不同微結構的co30 ;先驅物，焙燒溫度和焙燒時間等工藝條件對licoo ，電化學性能的影響，其中以納米晶co3o ;制備出的licooz表現出優良電化學性能，且大大縮短了反應時間。
  15. ( 2 ) the affecting factors such as components in precipitation process, the add - on, add on of precipitator, calination temperature and calination time were studied in the preparation process of ceo2 nanoparticles. the tg was used to analyze the processor, the xrd, sem and tem were used to characterize the size of crystal type of products. by a series of designed experiments the interaction between different factors and impacts on the preparation of ceo2 nanoparticles were probed, and the optimum preparation condition was gotten

    （ 2 ）對納米二氧化鈰制備過程中可能的一些影響因素（反應組分的濃度，沉澱劑的加入量，焙燒溫度，焙燒時間等）進行了研究，並通過tg ? dta分析手段對前驅物進行熱重分析；用xrd 、 sem及tem等測試手段對產物的粒度和晶型進行分析；探索了各個因素對納米二氧化鈰制備的影響及各因素間的交互作用；確定了在該試驗條件下制備納米二氧化鈰比較優化的制備條件。
  16. After prep - baking and making - granule, under different temperature we baking on the preceding powder, and it proof the most proper baking temperature is 1440. under 1440, we do the excessive zinc oxide experiment, and find when zinc oxide excessiving3 %, we can get the best production which i is 5962

    將制備得到的前驅粉在850 2 . 5h條件進行預燒、制粒后，在不同焙燒溫度下進行了鐵氧體焙燒試驗，並對最優配方下zno過量條件進行試驗研究。結果表明，在焙燒溫度1440 ， zno過量3 %的條件下，可制得i為5962的高磁導率鐵氧體。
  17. Methods of sampling and test for carbonaceous materials used in aluminium manufacture - electrode coke - determination of the density in xylene of calcined cokes

    制鋁工業用炭素材料取樣與試驗方法.第2部分:電極用焦炭.第6節:焙燒焦炭二甲苯密度測定