無壓燒結 的英文怎麼說

中文拼音 [wúyāshāojiē]
無壓燒結 英文
loose sintering
  • 無 : 無Ⅰ動詞（沒有） not have; there is not; be without Ⅱ名詞1 （沒有） nothing; nil 2 （姓氏） a surn...
  • 壓 : 壓構詞成分。
  • 燒 : Ⅰ動詞1 （使東西著火） burn 2 （加熱或接觸某些化學藥品、放射性物質等使物體起變化） cook; bake; hea...
  • 結 : 結動詞（長出果實或種子） bear （fruit）; form （seed）
  1. Mas precursor powders were uniaxially pressed at 100 mpa employing a lubricated steel cylindrical mold. after sintering at 1450 for 2 hours, single - phase cordierite ceramic is prepared, and its relative density is 95. 1 %

    Mas先驅體粉末在100mpa的軸向壓力下成型后，經1450無壓燒結2小時，得到單相堇青石陶瓷，其緻密度達95 . 1 。
  2. At present, our country is the largest producer and consumer in the horniness - alloy scopes. but now, this stove depends on import, hip - sinter stove ’ s self - develop and corresponding control system has important apply value

    目前我國是世界上最大的硬質合金生產與消費國，但生產所需的燒結爐仍主要依賴進口，自主研製低壓真空燒結爐及配套的控制系統無疑具有重要的應用價值。
  3. It has been found that all the elements in the addition act respectively in the way that affect the material ' s properties during the calcining process and the increase of the pms / pzn ratio can weaken the stability of the crystal structure of the sintered ceramics and cause the crystal structure transformation from the tetragonal to the rhombohedral as well

    發現多元壓電陶瓷材料中，無論是主加組元還是微量摻雜，預燒階段，它們在陶瓷中的作用都表現為單獨離子對陶瓷結構和性能所起的作用。燒結后，隨著pms pzn相對量的提高，陶瓷晶體結構由四方相向三方相轉化，同時穩定性下降。
  4. The expansion and dehiscence behavior during the vacuum reactive sintering below 660 of compact ti / al composite powders was experimentally investigated, and the reasons of expansion and dehiscence were theoretically analyzed. the method of low temperature reactive sintering was generalized, and the experiment testified the method effective. the rule of the expansion of the billets was generalized from the result of density of the billets

    低溫反應燒結工藝:研究了高能球磨ti / al復合粉體在溫度低於660下真空無壓反應燒結過程中的膨脹和開裂行為，分析了產生膨脹和開裂的主要原因;並提出了能夠有效預防坯料開裂的方法;通過測定坯料在低溫燒結后的密度，總結了其體積膨脹的規律;通過x射線衍射技術分析了隨球磨時間不同，金屬間化合物的生成情況。
  5. The company possesses advanced machinery and equipment as well as testing instrument, for example, hip sintering furnace, 1000 tons press, high precision grinding machine for roll ring, ultrasonic no damage detector and so on

    公司擁有國際先進的熱等靜壓燒結爐1000噸壓機高精度輥環磨床無損探傷儀等專業化生產設備和檢驗儀器，保證產品質量。
  6. Powder metal is often used instead because it is undesirable or impractical to join the elements through alloying or to produce parts by casting or other forming consists of producing small particles, compacting, and sintering. the squeezing pressure with added heat bonds the metal powder into a strong solid. powdered metals can be ferrous, nonferrous or a combination of ferrous and nonferrous elements

    金屬合金一般是無孔隙固體；因為煉制出的合金的實際效果不理想，或者通過鑄造和其他成型方式對小的顆粒進行壓制，燒結出來的產品零件無法滿足需求，因而人們常常使用粉末金屬來代替金屬合金。
  7. Material is cement, sand, coal dust, high pressure molding, need not sinter. the product with good strength, colourful

    原料由水泥、黃砂、粉煤灰組成，高壓成型無需燒結，成品瓦強度高、色彩豐富。
  8. The effects of such elements as primary flow total pressure, flow rate, degree of fuel rich, nozzle structure, flying speed and secondary combustion on ejecting mode performance were researched. it was found that thrust augmentation can be achieved on the condition that the flying mach number is above 0. 7. to deeply analyze thrust augmentation mechanism in low speed range, the research was further continued by changing secondary combustion organization and aft - body configuration

    研究了一次流總壓、流量、富燃程度、噴管結構、二次流來流速度、二次燃燒組織對引射模態性能的影響，發現實驗樣機構型在0 . 7ma以上的飛行條件下可以獲得推力增強，而在0 . 7ma以下無推力增強。
  9. Sintering or friction all brought about chemical change in the surface of solid lubricant and the change of valen ce state of mo, s, fe and so on ; the micro - hardness of pure ptfe was minimum and the surface - hardness of solid lubricant was increased with the increase of additional packing filler in formula ; the compressive strength of pure ptfe was minimum and its compressive strength could be increased notably by adding organic and inorganic filler. but not more additional amount, more notable increase of compre

    、 feso4 、 cus等物質;燒結及摩擦均使固體潤滑劑表面發生化學變化，使mo 、 s 、 fe等元素的價態發生變化;純ptfe的顯微硬度最低，固體潤滑劑的表面硬度基本是隨著填料加入量的增加而增加的;純ptfe的抗壓強度最低，在ptfe樹脂中加入無機填料均可明顯提高其抗壓強度，但並不是加入量越多，抗壓強度提高越明顯。
  10. In the section of non - pressing sintered, the influence of different raw material system and sintered temperature on the phase composition of the material were studied. and two conclusions were achieved. the one is that it is good for phase composition design and control because the final phase composition of the material fabricated by ti, sic and c raw material system is comparatively stable

    在無壓燒結階段，研究了原料體系與工藝制度對材料物相組成的影響，結果表明使用ti 、 sic 、 c的原料體系得到的材料最終物相組成比較穩定，有利於進行材料組成設計與控制； 1500得到的材料中的雜質相含量較少，是比較合適的反應溫度。
  11. By using the high pure alumina micro - powder ( > 99. 0 % ) and the polymorphous alumina fiber as materials, by adding alumina sulfate as the binder or polypropylene - amide as the disperser respectively, through mixing, dispersing, and compression molding, at different temperatures of 1200 c, 1350 c, 1400 c, 1500 c, and 1550 c with no pressure, the alumina fiber - alumina composites were made

    本試驗採用高純氧化鋁微粉（ 99 . 0 ）和多晶氧化鋁纖維為原料，分別加入硫酸鋁和聚丙烯酰胺作結合劑和分散劑，經混合、分散、壓力成型及在1200 、 1350 、 1400 、 1500 、 1550下無壓燒成制得氧化鋁纖維? ?氧化鋁復合材料。
  12. Effect of phase transformation and grain size on pressureless sintering behavior for tio2 ceramics

    相變和晶粒尺寸對二氧化鈦陶瓷無壓燒結行為的影響
  13. The la1 - xsrxmno3 powder has been sintered by constant pressure sintering, heat pressure sintering ( hp ) and spark plasma sintering ( sps )

    通過無壓燒結，熱壓燒結和sps燒結工藝對lal . xsrxmno3粉末進行燒結，其中sps燒結在900 ，保溫1omin得到的燒結樣品緻密化程度最好。
  14. In this paper, ti3sic2 material and ti3sic2 / sic composites, which were fabricated by non - pressing sintered and hot - pressing sintered methods are mentioned and the effects of the synthesis conditions on the phase composition, microstructure and mechanical properties were investigated

    本文通過無壓真空燒結和熱壓燒結制備了ti _ 3sic _ 2材料和ti _ 3sic _ 2 sic復合材料，研究了工藝制度對復合材料物相組成、顯微結構和力學性能的影響。