煅燒高嶺土 的英文怎麼說

中文拼音 [shāogāolǐngtǔ]
煅燒高嶺土 英文
cacined daolin
  • 煅 : 動詞1. （中藥製法: 放在火里燒） calcine2. （鍛造） forge
  • 燒 : Ⅰ動詞1 （使東西著火） burn 2 （加熱或接觸某些化學藥品、放射性物質等使物體起變化） cook; bake; hea...
  • 高 : Ⅰ形容詞1 （從下向上距離大; 離地面遠） tall; high 2 （在一般標準或平均程度之上; 等級在上的） above...
  • 嶺 : 名1. （頂上有路可通行的山） mountain; ridge 2. （高大的山脈） mountain range 3. （專指大庾嶺等五嶺） the five ridges
  • 高嶺土 : （瓷土） kaolin; kaoline; tervalba; hydrite; barden; carclazyte; kleit; [礦物學] bolus alba; china-clay
  1. An experimental study on the calcination of kaolinite from maoming, guangdong

    廣東茂名高嶺土煅燒實驗研究
  2. The factorial experiment on activity of calcined kaolinite

    煅燒高嶺土活性的析因實驗分析
  3. Surface modification of calcined coal - series kaolin

    煅燒高嶺土表面改性
  4. Surface modification of kaolin in coal series and its application in rubber

    宜昌煤系煅燒高嶺土表面改性及在丁苯橡膠中的應用
  5. Suface modification and application effect of calcined kaolin in coal series

    煤系煅燒高嶺土的表面改性和應用效果及應注意的問題
  6. The analysis results of reaction between calcined kaolin and saturation ca ( oh ) 2 solution and xrd results of reaction products of calcined kaolin and cement indicated that calcined kaolin has a high volcanic ash active

    通過對煅燒高嶺土與飽和石灰水的反應及煅燒高嶺土與水泥混合后的xrd分析，確認煅燒高嶺土具有較好的火山灰活性。
  7. The addition of calcined kaolin to cement increased the chemical shrinkage of cement stone, but it had no distinct impact on the self - shrinkage of cement stone

    煅燒高嶺土摻入水泥中，增加了水泥石的化學收縮，對水泥石的自收縮的影響並不明顯。
  8. The processes influencing the particle size, distribution of micro - prwder of graphite is studied by orthogonal layout in this paper. for certain particle distribution, the optimizing process is scheduled

    本文綜述了我國在煤系高嶺土的煅燒、超細磨工藝等方面的研究現狀、煅燒高嶺土的用途、以及研究中存在的問題。
  9. It can be seen from this study that avoiding a hardened and impervious lump formed in calcination can accelerate al extraction from coarse metakaolin pellets, and a high leaching rate can be reached within a batch process

    該研究結果表明，避免高嶺土球粒在煅燒時被「燒死」 ，能使粗粒煅燒高嶺土的酸溶反應易於進行。
  10. Research on surface modification of calcined sedimentary kaolin and its application

    沉積型煅燒高嶺土表面改性與應用研究
  11. Surface modification of calcined sedimentary deposit kaolin and its application

    沉積型煅燒高嶺土表面改性與應用試驗研究
  12. Surface modification of yichang calcined sedimentary deposit kaolin and its application

    宜昌沉積型煅燒高嶺土表面改性與應用研究
  13. Considering energy conservation and effects of calcined kaolin on the strength of cement, it was optimum method to produce calcined kaolin by calcining it at 980 c for 0. 5h and then cooling it suddenly

    結合煅燒高嶺土對水泥強度的影響，考慮到節約能源，以採用980恆溫0 . 5h然後快速冷卻的方法作為最佳煅燒溫度與時間。
  14. Coal based hard calained kaolin 20, 000t y

    煤系硬質煅燒高嶺土項目
  15. Quality comparison among calcined coal - series kaolin products under different productive processes and their influences on properties of paper coating

    煤系煅燒高嶺土不同生產工藝產品質量的比較及對紙張塗層性能的影響
  16. The relation between addition content of calcined kaolin, aluminium powders and aluminum sulfate in concrete and compressive strength, slump constant, 30min slump and permeability altitude were studied, and according to the experiment results, the component percent contents of crack - resistant and water - repellent admixture in cement were determined as following : calcined kaolin 6 %, aluminum sulfate 4 % and aluminium powders 0. 005 %

    通過對煅燒高嶺土、鋁粉、硫酸鋁在混凝土中摻量對其抗壓強度、初始武漢理工大學碩士學位論文坍落度、 3omin坍落度保留值及透水高度的影響，確定了配製抗裂防水外加劑的各組成成分以其占水泥質量的百分比分別為:鍛燒高嶺土6 % ，硫酸鋁4 % ，鋁粉為0 . 005 % 。
  17. The calcined kaolin, aluminium powders and aluminum sulfate were used as components of water - repellent agent, which effects on cement hydration and concrete impermeability were discussed in this paper

    本文以煅燒高嶺土、鋁粉、硫酸鋁作為防水劑的組份，研究了它們對水泥水化及混凝土的抗滲性的影響。
  18. The research results revealed that activated alumina content of calcined kaolin of kaolin had a strong correlation with the calcined temperatures and time. the activated alumina content of calcined kaolin increased with the calcined temperatures increasing from 750 c to 950 c, and increased with the calcined time prolonging at 750 c, 800 c, 850 c, 900 c and 950 c. however, the elevated speed of the activated alumina content decreased at 950 c for 4h

    研究發現，高嶺土的煅燒溫度及煅燒時間對煅燒高嶺土中的活性氧化鋁的含量具有較大的影響：高嶺土在750 、 800 、 850 、 900 、 950溫度下煅燒，其活性氧化鋁含量隨溫度和時間的增加而增加，但在950 、 4h時后活性氧化鋁的增加速度降低。
  19. The experiment was done that the cured cement stone with addition of calcined kaolin were dipped into nacl solution of 2. 5wt %, and the experiment results showed that addition of calcined kaolin made cement stone pore fine and cement mortar displayed high property of impermeability

    煅燒高嶺土的摻入可以使水泥石中的孔細化，通過對煅燒高嶺土摻入水泥中標養后在2 . 5氯化鈉溶液中浸泡試驗發現，煅燒后的高嶺土摻入水泥砂漿使其具有極好的抗滲透性。
  20. The activated alumina content had a reduce with time prolonging from 2h to 5h at calcined temperature of 1000 c. the research results also revealed that products obtained by sudden cooling from high temperature had a higher content of activated alumina than that by cooling naturally

    1000時煅燒高嶺土中活性氧化鋁的含量在煅燒時間2h 5h隨煅燒時間的延長還有所下降。另外，高嶺土煅燒后採用急冷方法比採用自然降溫方法中制得的煅燒高嶺土具有更高的活性氧化鋁含量。