爐料熔結 的英文怎麼說
中文拼音 [lúliàoróngjiē]
爐料熔結
英文
sticking of the charge-
Silica tamping material of the electric furnace used for melting cast iron
鑄鐵熔煉電爐的硅砂打結料Rapid repairing mass for converter ismade of electro baked magnesite and high - quality synthetic sandand manufactured by adding high fluidity recarburizer ( beveloped by ourselves ) as addition agent withspecial technique. lt has the characteristics of well fluidity, well rapid fluidityand rpid sintering etc. it is applied to hot patching of large area before or after the converter as rapping hole patching and other parts for converter
轉爐快速補爐料是以電熔鎂砂和優質合成砂為主要原料,配以自行研製的高流動性的增碳劑為添加劑,以特殊工藝生產製成,具有流動性好、快速燒結等特點,適合於轉爐的前後大面的熱修補及出鋼口等部位的修補Abstract : during the heating of scrap with carbon or hydrocarbon contented substances in some process, it will bring problems like explosion of carbon monoxide, fume and smell from oil volatilization, etc. , if incomplete combustion occurs. through laboratory experiments, the time related variation of gas contents and post combustion ratio of fume during the heating of oil - bearing scrap are studied. the results show that the restrictive chain of reaction procedure is the thermolysis of oil ; that temperature and ( co ) / ( co2 ) ratio influence transformation ratio and post - combustion ratio under lower temperature ; that 900 is the temperature above which the complete reaction can be ensured at all ( co ) / ( co2 ) ratios
文摘:在某些廢鋼熔煉過程中,當爐料中含碳及碳氫物質且燃燒不充分時,會帶來煙氣中一氧化碳的燃爆、油污揮發時造成的煙霧、臭味等問題.通過實驗室裝置研究含油廢鋼在加熱過程中煙氣成分隨時間的改變以及二次燃燒率的變化,試驗結果表明,反應過程的限制性環節是油分的熱分解;在較低的溫度下( co ) / ( co2 )比例影響轉化率和二次燃燒率;而在任意比例下保證充分反應的溫度為900以上The material of electro - fused magnesia sinter is selected from special grade a natural magnesite or high - purity caustic calcined magnesite, which is fused in arc furnace to finish the products. the products possess high purity, crystal with and compact texture, have high heat - vibration steady and cinder corrosion resistant, it is used for making high quality magnesite bricks, magnesia - carbon bricks
電熔鎂砂是用精選的特a級天然菱鎂石,在電弧爐中熔融制得,該產品具有純度高,結晶緻密,抗渣性強熱震穩定性好,是製作高檔鎂磚,鎂碳磚及不定形耐火材料的重要原料。It ' s pointed out that, under the condition of vim refining, the amount of oxide inclusions residue in molten steel increases with the increased loss of deoxidizing elements, and the key of melting extra - low oxygen steel is to avoid the thermal decomposition of lining material ; the size of deoxidizing products increases with the increased degree of supersaturation of deoxidizing elements ; larger inclusions granules found in extra - low oxygen steel come mainly from lining material
結果表明,在真空感應熔煉條件下,殘留在鋼中的氧化物夾雜數量隨脫氧元素鋁燒損量增加而增加,熔煉超低氧鋼的關鍵是避免爐襯熱分解;脫氧產物尺寸隨脫氧元素過飽和度增加而增加;超低氧鋼的大顆粒夾雜主要來自爐襯材料。They have excellent corrosion, thermal shock resistance and spalling resistance. they wide applications and can be used in key locations of thermal processing equipment such as bof, eaf, lf and so on. 2 alumina - magnesia - carbon brick made from high - purity bauxite or fused alumina and fused magnesia grain or high purity magnesia by pressing, resin - bond for thermal shock resistance
1 ,鎂碳磚是不燒的耐火材料,經過摩擦壓磚機的成型以及乾燥處理后而成,它的主要原料是電熔鎂,高純鎂砂和高純石墨,結合劑為樹脂,鎂碳磚有良好的耐侵蝕性,熱震穩定性和抗剝落性,它已經被廣泛地用在鋼廠的轉爐電爐鋼包精煉鋼包等關鍵部位。Additions of carbon for improved slag resistance. spinel formation improves hot strength, slag resistance and brick joint erosion. 3 repairing material for bof uses fused magnesia or sintered magnesia as the main raw material and after modifid pitch and special additives are added, it has the following characteristcs than other conventional converter pitch temperature, shorter sintering time, longer service life and less pollution. it is mainly used for repairing converter working face, also for tapping side, tapping hole and bottom
3 ,轉爐大面補料是採用電熔鎂砂或燒結鎂砂為主要原料,通過加入改性瀝青和特種添加劑使它和傳統瀝青補爐料相比具有高溫附著性好燒結時間短流動性好使用壽命長污染小等特點,主要用於修補轉爐迎鋼面通常稱「大面」也可以用於修補出鋼側,出鋼口及爐底等部位。A new measuring instrument for melting and crystallizing temperature of smelting slag is designed by adopting advanced microcomputer technology, micro - controller technology, and computer image processing technology in order to accurately and efficiently measure physical features of smelting slag, e. g. melting temperature, flowing temperature, crystallizing temperature, and crystallizing rate, etc
設計了一種採用先進的微型計算機技術、微控制器技術、計算機圖像處理技術相結合的冶金爐渣熔化結晶溫度測定儀,能夠準確高效地測試冶金爐渣等材料的熔化溫度、流動溫度、結晶溫度、結晶率等物理特性。It is made of fused magnesite and high purity flake graphite by adding metal composite antioxidant and phenolic resin as binder. it has the excellent properties of corrosion resistance, spalling resistance, resistance to oxidation and better thermal shock resistance. it can be used in all kinds of converters, eaf, refining ladles and common ladles. upon request, multiple lining - up designs of reasonable materials can be provided according to the working conditions of above mentioned furnaces
採用電熔鎂砂、高純鱗片石墨為主要原料,添加金屬復合抗氧化劑,以酚醛樹脂為結合劑製成的製品具有優良的抗浸蝕性、抗剝落性、抗氧化性和良好的抗熱震性,適用於各種容量的轉爐、電爐、精煉鋼包及普通鋼包,本公司可根據用戶要求,針對上述4種熱工窯爐的具體使用條件提出爐襯的材質綜合砌築方案。Clay pond furnace bricks made by us use advanced technology and the inner structure is fine. they can be widely used at bottom and wall part of glass melting pond
我公司生產粘土質池爐大磚歷史悠久,採用注漿成工藝品內部結構均勻,是應用於玻璃熔化的池底及池墻的主要材料。分享友人