爐料 的英文怎麼說

中文拼音 [lúliào]
爐料 英文
furnace burden; furnace charge; [冶金學] burden; charging material; charging stock
  • 料 : 名詞1 （材料; 原料） material; stuff 2 （喂牲口用的穀物） feed; fodder 3 （料器） glassware 4 （...
  1. The influences of furnace charges, chemical composition, quality of vermicularizing alloy, holding duration after vermicularizing treatment and tapping temperature on percentage of vermicular graphite were discussed

    摘要討論爐料、化學成分、蠕化劑質量、處理后包內保留時間和溫度對蠕墨鑄鐵蠕化率的影響。
  2. The main reasons causing increased chilling tendency of nodular iron are as follows : using metal charge containing trace and alloy elements which can increase chilling tendency ; molten iron being holded at high temperature too long ; abnormal nodularizing and / or inoculation treatment, as well as abnormal composition control

    摘要引起球鐵白口傾向大的主要原因是：爐料穩定性差、電爐保溫、球化處理及鐵液成分控制和孕育處理出現異常。
  3. As predicted theoretically, the ps polymer spreaded over the surface of the titania particles to form composite particles with core - shell structure. the influence of ph value and non - ion surfactant in heterocoagulation was discussed. the property of the coated particles was characterized by sem, and zeta potential, particle size distribution of the particles before and after encapsulation was obtained by laser particle size analyzer

    根據機械力化學的原理，採用自行制備的微米級ps和pmma （聚甲基丙稀酸甲酯）高聚物微球、金屬粒子、納米級的tio _ 2 、爐料為原料粒子，通過採用自行研製的乾式沖擊設備和lg攪拌磨製得以高聚物微球、金屬粒子為核，納米tio _ 2 、碳黑粒子等為包覆粒子的具有不同特殊功能的納米微米復合粒子。
  4. It shows that with a metallization degree of burden more than 40 per cent, blast furnace can t be operated with oxygen enriched blast. combining lower burden metallization degree with oxygen enriched blast and coal injection, higher coal injection rate and higher productivity can be obtained. by use of higher burden metallization degree lower coke rate can be obtained than oxygen enriched blast and coal injection

    結果表明：爐料金屬化率達到40后，高爐不能富氧操作；較低的爐料金屬化率與富氧噴煤相結合，能夠獲得更大的噴煤比和更高的產量；使用金屬化率較高的爐料，能夠比富氧噴煤達到更低的焦比。
  5. High loading windlass

    高爐料車卷揚機
  6. Rapid repairing mass for converter ismade of electro baked magnesite and high - quality synthetic sandand manufactured by adding high fluidity recarburizer ( beveloped by ourselves ) as addition agent withspecial technique. lt has the characteristics of well fluidity, well rapid fluidityand rpid sintering etc. it is applied to hot patching of large area before or after the converter as rapping hole patching and other parts for converter

    轉爐快速補爐料是以電熔鎂砂和優質合成砂為主要原料，配以自行研製的高流動性的增碳劑為添加劑，以特殊工藝生產製成，具有流動性好、快速燒結等特點，適合於轉爐的前後大面的熱修補及出鋼口等部位的修補
  7. Iron ore, coke, and limestone are put into the top of the furnace. these are called "charge".

    鐵礦石、焦碳、石灰石裝進爐子的頂部。這些東西叫爐料。
  8. Occupational hygienic survey of a charging factory

    樂山市某公司爐料廠職業衛生學調查
  9. Study on seismic behavior of buckling restrained braced steel frame structure

    唐鋼合理爐料結構研究
  10. Research into metal charge used in eaf

    電爐用金屬爐料的研究
  11. Study and application of high level sinter in blast furnace burden

    高比例燒結礦高爐爐料結構的研究與應用
  12. Study of the radial conductive intensifier for magnesium reduction jar

    煉鎂還原罐爐料成分及離心鑄造工藝研究
  13. Repairing material for bof

    轉爐大面補爐料
  14. Descent velocity of burden

    爐料下降速度
  15. Guimeng chromium alloy, furnace charge ores, manganese residue rich production sales

    硅錳鉻合金、爐料礦石、富錳渣的生產銷售。
  16. Tiejingfen processing, metallurgy furnace charge, civil building materials distribution

    鐵精粉加工、冶金爐料、民用建材的經銷。
  17. Abstract : in this paper, the distinct element method is adopted to study the force and the motion of granular burden from a kinematic view point. the numerical model of bell - less top charging is established. the charging process and burden surface profile have been imitated

    文摘:從動力學角度，採用離散單元法研究爐料顆粒的受力和運動，建立高爐無鐘爐頂布料數值計算模型，模擬無鐘爐頂布料過程和料面形狀。
  18. Abstract : according to material and local heat balance in the blast furnace, refering to the result of oxygen enriched blast and coal injection into blast furnace and use of metallized burden, the influence of burden metallization degree on oxygen enriched - coal injection rate 、 coke rate and productivity is calculated

    文摘:根據高爐物料平衡和區域熱平衡理論，參照高爐富氧噴煤和使用金屬化爐料的冶煉結果，計算了爐料金屬化率對富氧噴煤率、焦比和產量的影響。
  19. Abstract : during the heating of scrap with carbon or hydrocarbon contented substances in some process, it will bring problems like explosion of carbon monoxide, fume and smell from oil volatilization, etc. ， if incomplete combustion occurs. through laboratory experiments, the time related variation of gas contents and post combustion ratio of fume during the heating of oil - bearing scrap are studied. the results show that the restrictive chain of reaction procedure is the thermolysis of oil ; that temperature and ( co ) / ( co2 ) ratio influence transformation ratio and post - combustion ratio under lower temperature ; that 900 is the temperature above which the complete reaction can be ensured at all ( co ) / ( co2 ) ratios

    文摘:在某些廢鋼熔煉過程中，當爐料中含碳及碳氫物質且燃燒不充分時，會帶來煙氣中一氧化碳的燃爆、油污揮發時造成的煙霧、臭味等問題.通過實驗室裝置研究含油廢鋼在加熱過程中煙氣成分隨時間的改變以及二次燃燒率的變化，試驗結果表明，反應過程的限制性環節是油分的熱分解；在較低的溫度下（ co ） / （ co2 ）比例影響轉化率和二次燃燒率；而在任意比例下保證充分反應的溫度為900以上
  20. Abstract : some small blast furnace in tanshan district, which based on the resource predominance, make effort to burden material preperation, increase the qualities of sinters and pellets, optimize the burden structure, so there technico - econonic indeces were improved, and the cost of pig iron decreased to 700yuan / t

    文摘:唐山地區的一些小高爐憑借資源優勢狠抓精料，提高燒結礦和球團礦質量，優化爐料結構，從而改善了小高爐的技術經濟指標，使生鐵成本降到接近700元/ t的水平。