片狀聚合物 的英文怎麼說

中文拼音 [piānzhuàngjùgěwù]
片狀聚合物 英文
sheet polymer
  • 片 : 片構詞成分。
  • 狀 : Ⅰ名詞1 （形狀） form; shape 2 （情況） state; condition; situation; circumstances 3 （陳述事件或...
  • 聚 : 動詞（聚集; 聚積） assemble; gather; get together
  • 合 : 合量詞（容量單位） ge, a unit of dry measure for grain （=1 decilitre）
  • 物 : 名詞1 （東西） thing; matter; object 2 （指自己以外的人或與己相對的環境） other people; the outsi...
  • 片狀 : schistose片狀避雷器 plate protector; 片狀電容器 chip capacitor; 片狀結構 laminated structure; 片...
  • 聚合物 : [化學] polymer; polymerizate; polymeric compound; polymeric substance; polymeride; polymerized su...
  • 聚合 : 1 （聚集到一起） get together2 [化學] （單體結合成高分子化合物） polymerization; polymerize 3 [生...
  1. As the content of vermiculite minerals increased, the content of the " intercalated " shape, in which crystal gallery breadth was about of 40nm, also increased. in the curing reaction processing of polybenzoxazine / vermiculite hybrid nanocomposites intercalated with bisphenol a type precursor. according to the content of vermiculite minerals, while different shape of crystal was forming, these crystals were retarding the heat ring - opening polymerization of bisphenol a type precursors in the nanocomposites

    通過對雙酚a型ben蛭石納米插層物固化過程的分析：不同蛭石含量的插層物，在形成不同納米分散狀態固化結構的過程中，蛭石晶片對雙酚a型ben的熱開環聚合有明顯不同的阻礙作用，蛭石含量為3的插層物160的凝膠化時間較純樹脂的延長約7min ，活化能高約8kj mol ，固化反應熱晗低約14j g ，使得固化物的固化程度較純樹脂低約10 ，阻礙作用最大，其它含量的次之。
  2. With the increasing of montmorillonite content, the composites showed a trend of pseudo - solidlike at lower frequencies, the montmorillonite layers could align along the stress direction, and as a result, the dependence of dynamic modules on the frequency was quite different before and after suffering from large amplitude oscillatory shear

    然而當蒙脫土含量低於和臉或蒙脫土片層在基體中呈完全團聚狀態，則復合材料表現出與聚合物基體類似的線性粘彈特性。實驗發現，在熔體經大振幅振蕩剪切后，上述「類固.
  3. ( 1 ) two edt monomer synthetic paths have been investigated. ( 2 ) using the method of depositing the pedt film on the glass base, the affect of processing and environmental conditions - - such as the polymerizing temperature, the state of the polymer material, the polymerization correctives, the drying temperature, and the amount of the solution etc. - - to the pedt material ' s electroconductivity has also been examined in this paper

    主要研究內容包括： （ 1 ） edt單體合成路線的兩種方案，以及具體的制備過程； （ 2 ）在玻璃基片上淀積pedt膜層，研究了聚合溫度、聚合物狀態、聚合改良劑、烘乾溫度、溶劑含量等工藝及環境條件對pedt材料電導率和成膜速度的影響。
  4. Based on tem images and ft - ir characteristics, it is found that most of layers formed as " pseudoparticles ", which connected due to very strong interaction. as a result, the tensile modulus of the composites were more tower than the corresponding values calculated by using halpin - tsai continuous equation, but higher than those of polymer matrix

    Tem 、 ft - ir等表徵發現，復合材料中蒙脫土片層可以很好地剝離分散於聚合物基體中，但片層並非完全以單片層分散狀態剝離，而是以片層堆疊形成「準粒子」 ；同時，還存在一定量的團聚體。