玻璃粉燒結 的英文怎麼說

中文拼音 [bōlífěnshāojiē]
玻璃粉燒結 英文
glass powder sintering
  • 粉 : Ⅰ名詞1 （粉末） powder 2 （用澱粉製成的粉條或粉絲） noodles or vermicelli made from bean potato o...
  • 燒 : Ⅰ動詞1 （使東西著火） burn 2 （加熱或接觸某些化學藥品、放射性物質等使物體起變化） cook; bake; hea...
  • 結 : 結動詞（長出果實或種子） bear （fruit）; form （seed）
  • 玻璃 : 1. （一種質地硬而脆的透明物體） glass 2. [口語] （指某些像玻璃一樣透明的尼龍、塑料等） nylon; plastic
  1. The material was sintered at 1050 for three hours to get the porous artificial bone, that its apparent porosity was54 %, its volume density was 1. 28 g / cm3, and its bending strength was 13. 25mpa. the results showed that the sintering temperature was reduced by adding bioglass

    本研究採用含生物玻璃前驅體粉末原料，添加檸檬酸造孔劑，模壓成型，在1050燒結保溫3小時，獲得了顯氣孔率為54 、體積密度為1 . 28s cm ~ 3 、抗彎強度為13 . 25mpa的多孔hap人工骨材料。
  2. The influence of nano - al2o3 on the sintering and the properties of the si3n4 ceramics was researched in this paper. the samples with different amount of nano - al2o3 were obtained by using pressureless sintering at 1600, 1650, 1700 in the nitrogen atmosphere. the microstructure and the composition of the ceramics were determined by the means of x - ray, sem, micro - hardness meter etc. it is show that the sisty ceramics can be densified at 1650c to % percent of the theory density through the addition of nano - al2o3 ( the value could be 90 percent by other technique ). the crystalline growth of the cylindrical - si3n4 and the ratio of its longitude to its diameter are increased with the addition of nano - al2o3. a uniform microstructure and an fined crystal as well as more sialon phases can be obtained in the si3n4 ceramics through the addition of that

    實驗結果表明：在碳管爐中、氮氣保護下進行燒結，添加劑為納米al _ 2o _ 3粉末時，由於納米粉末的高活性、高燒結驅動力，在1650就可使si _ 3n _ 4完全地燒結，並使其緻密度可達理論密度的96以上（比其它工藝高6左右） ；同時，納米al _ 2o _ 3地加入大大促進了長柱狀? si _ 3n _ 4的生長和發育及柱狀晶長徑比的提高，使微觀結構均勻、細化，形成了更多力學性能優異的固體? sialon相，減少了不利於陶瓷材料性能的晶間玻璃相，凈化了晶界。
  3. Made of high - speed mixing polytetrafluoethylene resin and a certain volume of filling agent ( such as carbon fiber, graphite, molybdenum disulfide, glass fiber and bronze powder etc. ) shaped by moulding then through high heat sintering

    用聚四氟乙烯樹酯與一定量的填充劑（如：碳纖維、石墨、二硫化組、玻璃纖維、青銅粉等）經高速混合均勻後用模塑成型經高溫燒結製成。
  4. The results show that factors affecting the pore diameter of porous materials are the sintering temperature and time, the added quantity of pore former and the granularity of glass powder etc

    研究結果表明：燒結溫度和時間、造孔劑的用量及玻璃粉體的粒度等都將影響多孔材料的孔徑。
  5. Foamed glass was prepared by powder sintering process using the rejected glass and the fly ash as basic material, as well as foaming agent, flux and stabilizer as auxiliary materials

    以粉煤灰和廢平板玻璃為基礎原料，以發泡劑、助熔劑、穩泡劑為輔助原料，用粉末燒結法制備了泡沫玻璃。