  1. The resistivity of the films drops compared with the as - grown films, but the temperature of maximum magnetoresistance reaches 287k, very close to the room temperature. therefore it is not only an important improvement to fabricate the cmr bolometer which can work near room temperature, but also a prospective research for other applications such as magnetic - sensors, spintronics devices and infrared detectors

    同時，退火后薄膜的電阻率明顯下降，外加5t磁場時，最大磁電阻率溫度點上升到287k ，接近於室溫，這不僅為製作室溫超巨磁電阻測輻射熱儀打下了堅實的基礎，也為其它許多器件的應用提供了可能。
  2. The results showed that the microstructure of as - deposited tbdyfe ii 1ms were amorphous and the crystal of tbfe2 were found in films after annealing at 500. annealing films in vaccum could improve the saturation magnetization ms and the susceptibility, decrease the coercivity and the saturaion field, and make the direction of the magnetic moments parallel to the film plane

    結果表明，制備態薄膜為非晶態結構，經過500真空退火熱處理后，薄膜出現了tbfe _ 2的結晶物，薄膜的矯頑力和外場的飽和磁場大大降低，飽和磁化強度增強，初始磁化率提高，易磁化軸轉向膜面。
  3. The soft magnetic properties have become better in samples annealed at 400 c for 1 hour in a transverse magnetic field of 15 oe at vacuum atmosphere

    在真空條件下400加15oe磁場退火1小時后，樣品軟磁性能得到較大改善。
  4. The sandwiched films with the structure of 2. 5um / 2um / 2um and 2u m / 2um / 2 u m have been prepared by covered - module method. gmi effect will be studied in deposited and annealed samples with variation of magnetic field, driving frequency and current

    用掩膜法制備了每層厚度為2 m和2 . 6 m的三明治膜，將研究退火前後樣品的gmi效應，包括隨磁場、驅動頻率、交流幅值的變化。
  5. This paper improves some commonly used stochastic optimization algorithms, such as genetic algorithm, simulated annealing algorithm and tabu search algorithm, and improved algorithms are verified by the standard mathematical functions. then, improved algorithms are used to solve practical electromagnetic problems and the items of practical application of algorithms worthy of paying attention to are emphasized

    本文對遺傳演算法、模擬退火演算法、禁忌搜索演算法等幾種常用的隨機類優化演算法進行了改進，以標準數學函數作為檢驗依據對改進演算法作出評價，並將各改進的演算法應用於實際電磁場逆問題的求解，總結其應用的實際經驗和見解。
  6. The results of gmr testing indicate that the gmr effect is much little in the assputtered films, but they will be enhanced after vaccum annealling in magnetic fileld. and we also found that the thickness of the films and the

    磁阻性能測試結果表明，沉積態薄膜的磁阻性能微弱甚至沒有，經過真空磁場熱處理后的薄膜磁阻性能明顯得到提高，並且薄膜厚度與退火溫度均對薄膜的巨磁阻性能有重要影響。
  7. After annealed and co ion implantation, the highest gmr of the former is higher than that of the latter. the saturation magnetic field of discontinuous multilayer films is ikoe, nine times lower than that of granular films

    退火和注入co離子后， nifeco ag非連續多層膜的最大gmr效應大於nifeco ag顆粒膜的最大gmr效應，而且飽和磁場也降低了九倍，為1koe 。