  1. It focuses on the theory of the mineral functional materials " improving the anti - chloride permeability and the chloride binding. the main achievements of this article include : 1 ) use the technology of xrd, sem, bet, laser particle size distributor etc to test the component, the construction, particle size distributor, specific surface etc of micro - silica, ultra - fined slag, high quality fly ash, meta - kaolin clay, four types of the mineral functional material, theoretically analysis the functions which the four mineral functional minerals act on cement concrete, namely pozzolanicity effect, filling effect, micro - aggregate effect, surface adsorption effect and so bring into play the affect of plastification, lowing of temperature, reinforcement, improvement of durability. base on this analysis we can conclude that the proper diameter of the mineral functional material is 5 m - 15 m, that is blain fineness 4500cm2 / g - 7500cm2 / g

    本論文的主要成果包括以下幾個方面： （ 1 ）採用xrd 、 sem 、 bet 、激光粒度分析儀等多種測試手段，探明了以硅灰，超細磨粒化高爐礦渣，優質粉煤灰及偏高嶺土超細粉等4種超細礦物功能材料的組成、結構、粒度分佈、比表面積等基本性質；從理論上分析了礦物功能材料在混凝土中的4種效應，即火山灰效應、填充密實效應、微集料效應、表面吸附效應，並由此發揮出增塑、溫峰削減（降熱） ，增強及耐久性改善等作用；通過相關理論分析，推導出礦物功能材料的合理粒徑范圍在5 m 15 m ，即勃氏比表面積為4500cm ~ 2 g 7500cm ~ 2 g 。
  2. Granulated electric furnace phosphorous slag used for cement production

    用於水泥中的粒化電爐磷渣
  3. Some main results of testing research were as fellows : i. in the course of testing of leaching zinc dross, leaching zinc dross by sulfuric acid was researched and the effects on the leaching rate of the zinc dross were analyzed by author, the optimum conditions of leaching testing of zinc dross were determined as fellows : liquid - solid ratio 6 : 1, stirring ratio 250r / min, granularity 120 mesh, the soaking time 5h, the concentration of sulfuric acid of 30 %, and under these conditions, the rate of leaching zinc is above 92. 0 %. ii. in the course of testing of purification, on the basis of comprehending and comparing all present methods of the manganese - removal and iron - removal, the oxidizing method of manganese - removal in zinc sulfate solution using ammonium persulfate was put forward and the oxidizing method of iron - removal in zinc sulfate solution using the goethite process and oxidation - hydrolysis process was adopted

    研究的主要結果具體如下： 1 、研究了硫酸浸出鋅浮渣並分析了影響浸出率的各種因素，確定了浸出鋅浮渣的最佳條件為：液固比為6 ： 1 ，攪拌速度為250r min ，粒度為- 120目，酸浸時間為5 . 0h ，硫酸濃度30 ，鋅浮渣的浸出率大於92 . 0 ； 2 、在綜合和比較了目前除錳和除鐵的各種方法基礎上，提出了過硫酸銨氧化除錳方法和選擇了針鐵礦-氧化水解聯合法除鐵方法，並分析和討論了影響除錳率和除鐵率等各種因素，確定了除錳的條件為：溫度90 ， ph值5 . 4 ，反應時間3h ，過硫酸銨達到理論值的1 . 2倍，除錳率超過99 . 86 ；聯合法除鐵的條件為：氧化反應時間1 . 5小時、溫度控制在90 92 、 ph值5 . 2 5
  4. Granulated blastfurnace slag used for cement production

    用於水泥中的粒化高爐礦渣
  5. Cold shots develop from low casting temperature, and dirt spots result from pickup of sand or slag by molten metal

    較低的鑄造溫度會形成冷疤，熔化金屬出現的沙粒或爐渣的累積會導致污點。
  6. With the very low water to cement ratio, rpc has ultra - high strength high ductility and low permeability. in this paper, the compressive strength of rpc can reach to a high point with the number approximately 135mpa. as illustrated from the study results, we can approve some fundamental conclusions : there are big effects on rpc with deferent kinds and properties of raw materials and deferent curing conditions ; stress - strain curve shows the process of destroy with rpc samples ; x - ray diffraction analysis indicates that heat treatment at temperatures 90 accelerate the hydration of rpc sharply, therefore, mechanical and microstructural properties of rpc are highly dependent on heat treatment ; it is believed that rpc materials have excellent resistance to chloride permeability ; during the heat treatment, the shrinkage of rpc developed quickly because of chemical reactions ; the rpc with slag mostly has the advantage of rpc without slag about resistance to solutions corrosion

    研究結果表明：通過對rpc各組分摻量變化的研究，可以找到rpc的最優配合比；試件成型后的熱養護制度對rpc的性能影響巨大； rpc的抗壓應力?應變曲線可以反映出試件受破壞時微裂紋的擴展情況，剛纖維的摻入可以大幅改善rpc的韌性； rpc在成型后存在較大的收縮，而其中的化學收縮要遠遠大於乾燥收縮； rpc具有很強的抗氯離子滲透性能，漿體的密實度很高；通過x射線衍射實驗，可以發現rpc的膠凝體中ch晶體已經幾乎不存在，膠凝體主要由c - s - h凝膠和未水化水泥顆粒組成；在抗溶液侵蝕的實驗中，摻礦渣rpc的抗溶液侵蝕性能在絕大多數情況下要好於不摻礦渣試件，酸、堿溶液和浙江工業大學碩士學位論文摘要一些鹽溶液都會對rpc的結構產生侵蝕作用，但是機理各有不同。
  7. Granulated blastfurnace slag used for

    用於水泥中的粒化高爐礦渣
  8. Ground granulated blast furnace slag used for cement and concrete

    用於水泥和混凝土中的粒化高爐礦渣粉
  9. On the other hand, under the force of mechanical, the carbon and cao & sio2 superfine powder are obtained ; the specific surface area of these particles is increased. the tem photos indicated that, the carbon particles are composites on the surface of the melting superfine particles uniformly

    另一方面，在機械力作用下，碳黑及cao sio _ 2的熔融顆粒被超細粉碎，比表面積增大，同時tem照片顯示，中超碳黑均勻地復合於超細熔融顆粒表面，並有逐步嵌入的趨勢，提高了碳的有效利用率，降低了保護渣的熔化速度。
  10. Saponification slag stabilization granule soil can be used as bottom course of all highway

    皂化渣穩定細粒土可以用做各等級公路的底基層。
  11. Saponification slag - fly ash stabilization granule soil can be used as bottom course of all highway

    皂化渣粉煤灰穩定細粒土可以用做各等級公路的底基層。
  12. The phases of sulfuric acid slag of various sizes were drawn by seven - step method in the improved separation condition of disturber, and phases of thallium were compared before and after the slag was grinned to analyze phase migration

    為了進一步探討顆粒物中鉈相態提取的技術和方法，在優化干擾物分離條件下，採用七步法提取了幾種不同粒徑硫酸廢渣中鉈的相態，比較了廢渣研磨前、后各相態鉈的異同。
  13. Investigation and application of comprehensive utilizing the ground granulated blast furnace slag

    粒化高爐礦渣綜合利用的研究和應用進展
  14. It is used to scrape and collect some thing like the organic sludge 、 active sludge 、 inorganic grit 、 chemical sludge, etc which are under the bottom of the tanks ; the return flights can also be made use of to collect some things like floating sludge 、 rubbish and oil slick on the water surface

    用於刮除沉澱在池底的有機污泥、活性污泥、無機砂粒、化學污泥等；並可利用在水面上的回程刮板收集漂浮在水面上的浮渣、垃圾及浮油等。
  15. This thesis fabricated successfully a wc particle reinforced iron matrix composite using a vacuum infiltration process for severely erosion and application in the slurry pump. the casting process was optimized. the microstructure and wear resistance were researched and analyzed

    本文針對承受嚴重沖蝕磨損的渣漿泵過流件，採用負壓鑄滲工藝成功制備了碳化鎢顆粒增強鐵基表面復合材料，改善和優化了復合工藝、鑄造工藝。
  16. How to make the saponification slag profit us ? according to saponification slag is one kind of substandard lime, in this research, i use saponification slag to stabilize granule soil instead of lime. the intensity, rigidity, water stability, anti - scouring, shrinkage index of saponification slag stabilization is the same as the index of lime stabilization

    根據皂化渣屬等外石灰的特點，利用皂化渣替代石灰用於皂化渣穩定細粒土、皂化渣粉煤灰穩定細粒土、皂化渣粉煤灰等結構，並對這幾種結構的強度、剛度、水穩定性、抗沖刷能力、收縮性等指標進行了分析，結果顯示這幾種結構性能指標與石灰類結構相當。
  17. The fine powder flows into the product cyclone collector together with air flow and is expelled from the powder output pipe as product. raymond grinder. in the grinding chamber, since the stuff contains moisture to some extent, raymond grinder the heat generated during grinding makes the moisture evaporated ; since the pipeline joints are not airtight, raymond grinder the external air is sucked in and the circulation air mass increased, in order to enable the grinder to work in negative pressures, raymond grinder the increased air flow is guided to the deduster and sepuentially to the atmosphere after purification. raymond grinder. raymond grinder function tehnical datum

    雷蒙磨粉機-本機適用於粉碎重晶石石灰石陶瓷礦渣等莫氏硬度不大於9 . 3級，濕度在以下的非易燃易爆的礦業冶金化工建材等行業280多餘種物料的高細制粉加工如：各種礦石化工原料等，雷蒙磨粉機成品粒度60 425目范圍內根據需要任意調節雷蒙磨粉機最細1000目。