粗紋裂面 的英文怎麼說
中文拼音 [cūwénlièmiàn]
粗紋裂面
英文
coarse grained fracture-
The microscopic plastic deformation of the local crazes cause the change of crack opening loads. therefore, the fatigue crack closure concept could be introduced. a crack closure model of mdyb - 3 pmma were recommended and phenomenologically formulated for positive and negative stress ratios separately, according to the testing results of fatigue crack propagation
本文討論了有機玻璃疲勞裂紋擴展機理，提出，銀紋的形成是裂紋形成和擴展的基礎，從微觀上解釋了裂紋形成和擴展的原因，並結合金相分析結果，明確提出塑變誘導閉合和粗糙誘導閉合是有機玻璃疲勞裂紋面閉合的兩個主要原因，成功的解析了裂紋面的閉合現象。It is found that the great cracks on the coarse surface are initiated easily than on the smooth surface by the sem observation and the crack size obtained at the dynamic indentation experiment is bigger than at the static indentation experiment under the same load. it is showed the single crystal silicon is easier to initiate the crack and fracture under dynamic load, the single crystal silicon ’ s
然後通過sem觀察單晶硅試件表面壓痕形貌，發現粗糙表面比光滑表面容易生成大裂紋，在相同載荷作用下單晶硅材料在動態壓痕試驗得到的裂紋要大於在靜態壓痕試驗得到的裂紋，表明在動態加載條件下單晶硅材料更容易生成裂紋和破碎。Leather - physical and mechanical tests - determination of resistance to grain cracking and grain crack index
皮革.物理和機械試驗.耐粗糙面裂紋和粗糙面裂紋指數的測定
分享友人