Based on plane section assumption, this paper presents the methods of calculating the ultimate strength of the columns strengthened with cfrp, and makes a simplification of the methods. a fortran program on nonlinear method is presented to numerically analyze the characteristics of large eccentrically loaded columns strengthened by longitudinal straps of cfrp, calculating results compare well with experimental data
本文在平截面假定的基礎上分別推導了碳纖維布縱向粘貼大偏心受壓柱的正截面承載力校核和截面加固基本計算公式,並對公式進行了相應的簡化;運用fortran語言編制相應程序對縱向粘貼碳纖維布大偏壓柱進行了數值分析,本文公式計算結果和程序計算結果均與試驗結果吻合良好。Viscose plain cloth
粘纖平布The parameters of impregnation are as follows : ph is about 3, the range of temperature is from 20 to 45, and the time is about 2 to 6 hours. after the necessary treatments, zirconia cloths had the optimal strength when the diameters of zirconia fibers were controlled in 4um to 7um, and the sizes of zirconia grains were in 50nm to 100nm. the affec - ting factors were discussed and the liner regression analysis of the cloths was made, from w hich they show that the diameters and grain sizes have the significant influences on zirconia cloths. the obtained zirconia cloths have been accepted for use in nickel - hydrogen batteries by practical use
研究結果表明:粘膠類纖維布最適合制備氧化鋯纖維布的前軀體;鋯液濃度以飽和溶液為宜;浸漬工藝參數為ph值3左右,溫度20 45 ,時間2 6小時;多餘鋯鹽的去除、浸鋯液后纖維布的整平處理及平燒施應力燒成有利於氧化鋯纖維布的柔軟及平整; 200 600燒成溫度段應緩慢燒成,控制氧化鋯纖維直徑在4 7 m ,氧化鋯晶粒尺寸50 100nm時氧化鋯纖維布的強度最好。Jiangsu yizheng nonwoven factory imported from italy, germany, austria and other countries the complete and most advanced polyester spun - bonded production line, staple fiber geotextiles and geo - compound film production line with a yearly capacity of 6000 tons. the width can reach 4. 5m, and the weight is from 80 to 800gm2 at your choice
江蘇省儀征無紡布廠現有從義大利、德國、奧地利等國家全套引進具有世界先進水平的聚酯紡粘生產線、短纖土工布及土工復合膜生產線,年生產能力60000屯,幅寬可達4Chajes mj, thomson ta jr, farschman ca. durability of concrete beams externally reinforced with composite fabrics. constr build mater 1995 ; 9 ( 3 ). 141 - 8
楊勇新,葉列平,岳清瑞.碳纖維布與混凝土的粘結強度指標[ j ] .工業建築, 2003分享友人