耐磨塗層 的英文怎麼說

中文拼音 [nàimótúcéng]
耐磨塗層 英文
wear-resistant coating
  • 耐 : 動詞（受得住; 禁得起） be able to bear or endure
  • 磨 : 磨動詞1 （摩擦） rub; wear 2 （研磨） grind; mull; polish 3 （折磨） grind down; wear down [out]:...
  • 塗 : Ⅰ動詞1 （抹） spread on; apply; smear 2 （亂寫或亂畫） scrawl; scribble 3 （抹去） cross [blot; s...
  • 層 : i 量詞1 （用於重疊、積累的東西 如樓層、階層、地層） storey; tier; stratum 2 （用於可以分項分步的...
  • 耐磨 : abrasion resistant; anti friction; wear resistant; wear resisting; wearproof耐磨材料 high abrasiv...
  • 塗層 : paint-coat; paintcoat; coat; coating; covering; lining; wrapping flux
  1. Test method for abrasion resistance of pipeline coatings

    管道塗層耐磨性的試驗方法
  2. The research results show that, from the viewpoint of second phase morphologies, there exist quite differences between the grain - type materials ( such as wc / bcu brazing deposit material, wrs1000 and 1zt tungsten carbide strengthening overlaying material, as well as the wear - resistant material of polymer adhesive coating etc. ), and the aggregation - type as well as dispersion - type ones ( such as zg35simn, wrd - 1 and khc - k2 depositing material ) in the wear - resistance and sand slurry abrasion mechanism. the sand slurry abrasion mechanisms are brought forward, of new wear - resistant materials with the features of grain - type second phase morphologies

    研究發現，與聚合型、彌散型第二相的材料（如zg35simn 、 wrd ? 1和khc ? k2熔敷材料等）相比，顆粒型第二相的材料（如wc bcu釬焊熔敷耐磨材料、 wrs1000型耐磨材料、 1zt碳化鎢顆粒增強熔敷材料及ktc ? 1耐磨膠粘塗層材料等）在耐磨性能和磨損機理等方面均有不同，總結提出了以「顆粒型第二相」為特徵的耐磨新材料泥沙磨損機理。
  3. Wear properties of reactive plasma clad cr, fe 7c3 - fe ceramal composite coatings

    金屬陶瓷復合材料塗層的耐磨性
  4. In the investigations on laser cladding, experiments and analyses of laser clad nickel - based alloys and nickel - based ceramal composite alloys on steel substrates were performed to improve wear - resistance and corrosion - resistance properties of the coatings

    以提高材料表面的耐磨、耐蝕等性能為目的，採用預置和送粉熔覆工藝方式，對常用的鎳基合金和鎳基碳化鎢金屬陶瓷合金塗層進行系統研究。
  5. Tribological properties of a laser - clad cr2ni3si cr3si metal silicide composite coating

    金屬硅化物復合材料塗層耐磨性研究
  6. The lubrication aluminum oxide coatings with high hardness, antiwear and corrosion resistance by using microarc oxidation technology were discussed as well as its application

    對應用微弧氧化技術制備具有潤滑性能的高硬度耐磨、防腐蝕氧化鋁塗層及其應用進行了初步探討。
  7. Effect of rare earth metal yttrium on microstructure and wear resistance of vacuum fusion sintered ni - based coating

    基塗層顯微組織和耐磨性的影響
  8. When fillings is other materials ( unprocessed montmorillonite, powder coal ash, co - composite of powder coal ash and organo - montmorillonite, co - composite ofcarbonizing calcium and organo - montmorillonite ) in the binder and content of organo - montmorillonite in the binder is five percent decided by tensile - shear experiment, tensile - shear strength of binder is up to tiptop ; at the same time, this paper carries out abrasion experiment, and, by comparison, concludes abrasion property of coating is optimum when content of organo - montmorillonite in the binder coating is five percent, and observes abrasion sample under set

    當膠粘劑中填料為其它物質（未處理蒙脫土、粉煤灰、粉煤灰和有機化蒙脫土共復合、碳化鈣和有機化蒙脫土共復合）時，通過拉伸剪切試驗確定膠粘劑中有機化蒙脫土含量為5時，膠粘劑的拉伸剪切強度最高；同時進行了沖蝕磨損試驗，通過比較得出，當膠粘劑塗層中有機化蒙脫土含量達到5時，塗層的耐沖蝕磨損性能最佳，並對沖蝕磨損試樣在掃描電子顯微鏡（ set ）上進行觀察。
  9. The mechanism of corrosion and erosion resistance of nicr alloy and cermet coatings were explored and their performance were compared with 20g, 20g covered by dope and the coatings of fecral, nicrti used widely at present

    並將由這些新的塗層材料和目前廣泛使用的fecral ， nicrti以及與未加以保護的20g基體和刷塗料保護的20g在抗高溫氧化、高溫腐蝕、耐沖蝕磨損和熱震性等方面加以比較。
  10. With thermal spray technology, the surface of water wall tubes is easily covered by varied high performance coatings. in this paper, several new alloy and cermet coatings applied to water wall tubes were designed and their performance was studied according to the research item of hanchuan power station of hubei province " the study and development on the corrosion - resistant and wear - resistant coatings of water wall tubes in boiler "

    採用熱噴塗技術可以方便地在鍋爐管道表面獲得各種高性能的防腐耐磨塗層。本文結合湖北省漢川電廠的研究項目「鍋爐水冷壁管防腐耐磨塗層的開發研究」進行水冷壁管新型合金和金屬陶瓷復合塗層的設計和性能研究。
  11. Coating materials - determination of abrasion behaviour of decontaminable coatings - method using a tube with falling abrasive

    塗覆材料.可去污覆層耐磨特性測定.磨料吹管法
  12. Application research on the anti - wear coatings of axial - flow id fan blades for coal - fired boiler

    燃煤鍋爐軸流式引風機葉片耐磨塗層的應用研究
  13. Research and application of rate of target contribution in raising ability of business beneficial result

    自蔓延噴焊耐磨塗層的基礎研究
  14. Wearable and anti - eroding coat is added after renewing the shape and dimensions to insure the life of mixer blade

    修復后的攪拌槳葉是在恢復原有的形狀后，表面再施加抗磨抗腐蝕耐磨塗層，確保攪拌槳的使用壽命。
  15. Tribological properties and mechanism of fe - cr - ni coating

    耐磨塗層的摩擦性能及作用機理
  16. Application of supersonic arc spraying coating resistant to abrasion on power station boiler heating surface

    超音速電弧噴塗耐磨塗層在電站鍋爐受熱面上的應用
  17. Some problems in development and application of novel epoxy resin - based lubricative and wear - resistant coatings

    新一代環氧潤滑耐磨塗層研製與應用中需解決的若干問題
  18. Abstract : the paper presents the development and applications of thermal barrier coating, seal ( clearance control ) and wear resistance coating for aero gas turbine engine

    文摘:介紹了在現代航空燃氣渦輪發動機上熱噴塗熱障、封嚴、耐磨塗層的開發應用實例。
  19. A special black anti - wear coating has been presented to renovate the wearing anodized layer of aluminum alloy

    摘要針對黑色陽極氧化膜層的修復研製了一種專用耐磨塗料，該塗料可直接噴塗在原陽極氧化膜層上，熱固化成膜。
  20. To solve the performance problems, low hardness and poor wear resistance and antifriction, of the zinc / aluminium based corrosion resistance coating at the special high speed and large friction service conditions, a trial adding diamond particles into the coating was made to enhance the coating properties

    摘要為解決鋅鋁基耐蝕塗層在高速、強摩擦等特殊服役條件下硬度低、耐磨減摩性能差等問題，嘗試通過添加金剛石粒子對其進行強化。
分享友人
分享到 Line