耐高溫膠粘劑 的英文怎麼說

中文拼音 [nàigāowēnjiāoniánjì]
耐高溫膠粘劑 英文
high temperature resistant adhesives
  • 耐 : 動詞（受得住; 禁得起） be able to bear or endure
  • 高 : Ⅰ形容詞1 （從下向上距離大; 離地面遠） tall; high 2 （在一般標準或平均程度之上; 等級在上的） above...
  • 溫 : Ⅰ形容詞（不冷不熱） warm; lukewarm; hot; gentle; mild Ⅱ名詞1 （溫度） temperature 2 （瘟） acute ...
  • 膠 : Ⅰ名詞1 （某些具有黏性的物質） glue; gum 2 （橡膠） rubber 3 （姓氏） a surname Ⅱ動詞（用膠粘） st...
  • 粘 : 粘動詞（粘附） glue; stick; paste; adhere to; bond
  • 劑 : Ⅰ名詞1 （藥劑; 制劑） a pharmaceutical or other chemical preparation 2 （某些有化學作用的物品） a...
  • 高溫 : high temperature; elevated temperature; hyperthermia; megatemperature; inferno
  1. They can also be used for fiber sizing, textile finishing, the reinforcing agent for cement and ceramics, and the preparation of various kinds of latex paints, and all kinds of special adhesion agents. the products of vinyl acetate - acrylic ester copolymer emulsion, which have overcome some defect of homopolymerized products, are newly developed. the modified emulsion has stronger water resistance, better flexibility, and lower glass state temperature

    醋-丙共聚系列乳液產品是針對均聚產品的某些缺陷而發展起來的新膠種，它通過醋酸乙烯與丙烯酸脂類共聚改性，提高膠粘劑的耐水性和柔韌性，降低共聚物的玻璃化溫度，使產品對一些均聚乳液難以粘接的材料具有良好的粘接性能，主要產品有：寶麗板膠鋁箔紙膠塑板膠等。
  2. Dalian kerui economics trade co., ltd. sell tapes for bonding in industry, reclosable fasteners, adhesives, polish and grind material, anti - electrostatic and insulation tape america 3m company, heat shrinkable tubing, wire and cable, electrical thermal wire and system america raychem company, masterbatch hanna - wilson, silicone products ge toshiba company and electrostatic electronic hydrotreater, water tank self - cleaning sterilizer beijing enfi company

    公司經銷美國3m各種工業用單雙面膠帶尼搭扣粘接劑拋光研磨材料防靜電材料絕緣膠帶美國瑞侃公司單雙層熱縮管鉸鏈薄壁耐高溫導線電伴熱線及系統漢納威爾遜色母料ge東芝有機硅產品和各種靜電水處理器水箱自潔消毒器。
  3. An excellent adhesive was prepared from bismaleimide ( bmi ), epoxy resin ( e - 51 and tde - 85 ), 4, 4 ' - diaminodiphenyl sulfone ( dds ) in this thesis. the influence of liquid rubber and polymer ether imide ( pei ) on the properties ( especially high - temperature strength and the peeling strength ) were discussed, their different toughening characteristics and mechanisms were discussed. last, the process and effection of heat - resisted structural adhesive were studied by adhesive experiment of synchronizer in automobile. the results of investigation made clear : the adhesive, has good properties, especially heat - resisted properity

    根據材料分子設計的原理，研究了二苯甲烷雙馬來酰亞胺（ bmi ） 4 ， 4 』 ?二胺基二苯基碸（ dds ） e ? 51 tde ? 85組成的環氧膠粘劑體系，研究該體系在作為高溫結構膠粘劑使用時的粘接性能；然後研究了用無規羧基液體丁腈橡膠（ ctbn ? x ）和聚醚酰亞胺（ pei ）分別來增韌該體系的增韌效果；最後通過碳纖維耐磨材料與同步器圓錐環的粘接實驗，研究了耐高溫結構膠粘劑的粘接工藝和使用效果。
  4. Abstract : this paper introduces a new class f epoxy glass - cloth laminate. the synthesis of a epoxy adhesive and the production process were studied. the properties of the laminate were compared with those of some similar products abroad. the results show that the laminate has higher adhesive strength 、 resistivity in moist conditions 、 dielectric strength and mechanical strength in higher temperatures. it is applicable for electric equipments, especially those to run in higher moisture or higher temperature conditions

    文摘:本文介紹了最近開發成功的一種新型f級耐高溫層壓板，研究了環氧樹脂膠粘劑的合成，層壓板的製造工藝及其性能，並與國外同類產品進行了對比，結果表明，它具有粘接強度、浸水后絕緣電阻及耐電壓、高溫機械強度高等特性，可用作大型高壓電機、輸變電設備以及核電工程、低溫高真空工程中絕緣結構材料，尤其適用於高電壓、高溫、高機械強度的工作環境。
  5. High temperature resistant structural adhesives in former soviet union

    俄羅斯的耐高溫結構膠粘劑
  6. Synchronizer in automobile is made up of carbon fiber strip, tach and adhesive, which is used at 180 in loog peried. powerful torsinal strength in synchronizer operation request that the adhesive is heat - resisted structural

    汽車同步器由圓錐環與制動帶粘接組成，要求可在180環境下長期使用，同步器在運轉時存在強大的圓錐同步扭矩以及苛刻的溫度環境均要求用於粘接制動帶的膠粘劑必須是耐高溫結構膠粘劑。
  7. When change the component of adhesive its shear strength increased from 39. 3 mpa to 53. 5 mpa at room temperature and it have long - term usage at 180 with 25 mpa and can be served at 230 in short period. the addition of liquid rubber resulted in a 300 % increase in the peeling strength. the addition of polymer ether imide led to a 260 % increase in the peeling strength, a 15 % increase in shear strength and a 10 increase in tg ( tg = 195. 54 )

    研究結果表明： bmi dds e ? 51 tde ? 85組成的膠粘劑體系的室溫剪切強度為39 . 3mpa ，當改變環氧樹脂的含量時，剪切強度提高到53 . 5mpa ；用無規羧基液體丁腈橡膠改性環氧樹脂膠粘劑時室溫剝離強度提高3 . 0倍；用聚醚酰亞胺改性環氧樹脂膠粘劑，室溫剪切強度最高可達45 . 2mpa ，剝離強度提高2 . 6倍，玻璃化轉變溫度tg = 195 . 54 ，比未增韌體系提高10以上；碳纖維耐磨材料與同步器圓錐環的粘接實驗結果表明，膠粘劑的使用工藝性能良好，滿足室溫剪切強度30mpa和180剪切強度12 . 5mpa的技術要求。