裂紋傾向 的英文怎麼說
中文拼音 [lièwénqīngxiàng]
裂紋傾向
英文
rianflligkeit susceptibility to cracking-
Experimental study on outburst proneness coal seam of meso character and crack destabilization
沖擊傾向性煤體的細觀特徵與裂紋失穩的試驗研究The paper mainly discussed the reasons of stress from liquid ammonia pressure vessel causing crack through examing data and experimental results and analysing relevant referential documents and materials, taking 1200 ammonia vessel ' s crack and leaking in a certain fertilization company as an example : there existed remaining welding, stress in the equipment ; there existed a stress decaying surrounding, i. e., moisture 0. 2 %, and temperature > - 5 with o2 or co2 inside ; the higher the intensity of raw materials, more possible it was to have stress decaying crack
摘要以某化肥公司1200氨冷器殼體開裂泄漏的失效分析為例,通過對檢驗數據和結果及有關文獻資料的分析研究,探究了液氨介質壓力容器產生應力腐蝕裂紋的原因:設備中存在較高的焊接殘余應力;液氨介質具備應力腐蝕環境,即含水量0 . 2 % ,且有空氣( o2或co2 )污染(或摻入) ,使用溫度高於零下5 ;母材強度越高,應力腐蝕裂紋產生的傾向就越大。Minimal the tendency of microcracks can be obtained by improving the shape of weld pool and enhancing the welding energy input
通過改善焊縫成形和提高焊接線能量有助於減小兩類熱影響區微裂紋傾向。Author thinks that the direction of the maximum plastic distortion along a constant radius around the crack tip may be considered as the direction of shear - mode fracture ( named pmax - criterion ) and the load when located shear band prongs the ligament in the front of crack tip is regarded as the limited load of shear - mode fracture. ( 3 ) the fad ( fracture assessment diagram ) of titled crack is proposed based on achievements of mesomechanics about i - ii complex ductile fracture of metal, and the titled crack is classified two kinds : void - mode fracture is assessed by fracture assessment curve, and shear - mode fracture by limited load. ( 4 ) using a fe program based on plantle - ressue theory to calculate some mesomechanical parameters, a flange joint structure of a high pressure vessel ( design pressure 31. 4mpa and the thickness of the hemispherical head is half of that of shell. ) is analyzed to determine whether the structure under operation pressure is safe or not, forecast the mode of potential invalidation and argue for the rationality of design of the structure
試件的整體斷裂為剪切型,但在試件芯部裂尖鈍化區中部出現了韌窩型啟裂並有一定的擴展,說明局部較高的應力三軸度也會使韌窩型機制得以發展,但是不改變試件整體的剪切型斷裂模式;對韌性斷裂的剪切模式的細觀機理做了一定的探討,並且提出了含裂紋構件剪切型斷裂的宏觀判據:認為裂紋前方的集中剪切帶中與裂紋尖端等半徑處最大有效塑性應變出現的方向可以作為裂紋剪切斷裂的方向(可簡稱為_ ( pmax )準則) ,集中剪切滑移帶貫穿裂紋前方承載韌帶時的載荷可以作為極限載荷;本文運用金屬韌性斷裂細觀力學在一復合型韌性斷裂方面的研究成果,採用失效評定圖的形式,提出了傾斜裂紋的安全性評定方法的基本框架。分享友人