The corrosion behavior of nanocrystalline ( nc ) copper bulks with various grain sizes prepared from igc ( inert gas condemsation ) and vacuum annealing in comparison with conventional microcrystalline ( mc ) copper ( as - rolled and electrolytic ) in acid copper sulphate solution and neutral solution containing chlorides under free corrosion conditions and anodic polarizations has been studied using potentiodynamic polarization, potentiometric analysis, cyclic voltammetry and electrochemical impedance spectroscopy. x - ray diffraction was used to estimate the grain size of the annealed nc copper. field emission gun scanning electron microscopy and x - ray energy - dispersive spectroscopy was used to characterize the surface morphology and analyze the surface composition after the polarization and potentiometric test of both nc and mc copper
本文研究了用igc (惰性氣體蒸發凝聚原位溫壓法)制備並真空退火到不同晶粒尺寸的納米晶銅和微米晶銅(冷軋紫銅、電解銅)在酸性硫酸銅溶液和中性含氯溶液中,在自腐蝕狀態和陽極極化狀態下的腐蝕性能。使用了動電勢極化、電位測定、循環伏安法( cv )和電化學阻抗譜( eis )等方法。 x -射線衍射( xrd )的方法用來估算納米晶銅晶粒尺寸。If the focal point of the len shifts around the surface of the sample, the mass ablation, the temperature of the plasma and the spectral intensity appear asymmetric and their maximum occur at the location which is about 0. 4mm under the surface of the sample. ( 2 ) to the plasma of the aluminum alloy sample, when the operating voltage is 1600v, the height from the observed location of the plasma to the surface of the sample is 2mm and the argon pressure is 660 torr, the spectral intensity have the maximum values
( 2 )對于標準鋁樣品,在激光器工作電壓為1600v 、等離子體觀測高度為2mm 、氬氣壓力為660乇時,其譜線強度最強;以al 308 . 22nm 、 al 309 . 27nm兩條譜線為分析線,發現隨著環境氣壓的增大,譜線自吸效應明顯增強,當環境氣壓達到600 - 700乇時,譜線幾乎產生自蝕。The formation of self - assembled interfacial n - dodecanethiol monolayer and its effect on the corrosion protection of epoxy coating were evaluated using the x - ray photoelectronic spectroscopy, electrochemical impedance spectroscopy, impedance - time transition, and phase angle - time transition method
採用x射線光電子能譜、電化學阻抗譜、阻抗時間譜和相位角時間譜等方法對硫醇自組裝界面層及其對塗層腐蝕防護性能的影響進行了研究。
分享友人