The loss of deoxidizing elements resulting from thermal decomposition of lining materials and the change of total oxygen in molten steel during vim refining are researched
摘要研究真空感應熔煉過程中因爐襯材料熱分解造成的脫氧元素燒損及其全氧含量的變化規律。Abstract : during the heating of scrap with carbon or hydrocarbon contented substances in some process, it will bring problems like explosion of carbon monoxide, fume and smell from oil volatilization, etc. ， if incomplete combustion occurs. through laboratory experiments, the time related variation of gas contents and post combustion ratio of fume during the heating of oil - bearing scrap are studied. the results show that the restrictive chain of reaction procedure is the thermolysis of oil ; that temperature and ( co ) / ( co2 ) ratio influence transformation ratio and post - combustion ratio under lower temperature ; that 900 is the temperature above which the complete reaction can be ensured at all ( co ) / ( co2 ) ratios
文摘:在某些廢鋼熔煉過程中，當爐料中含碳及碳氫物質且燃燒不充分時，會帶來煙氣中一氧化碳的燃爆、油污揮發時造成的煙霧、臭味等問題.通過實驗室裝置研究含油廢鋼在加熱過程中煙氣成分隨時間的改變以及二次燃燒率的變化，試驗結果表明，反應過程的限制性環節是油分的熱分解；在較低的溫度下（ co ） / （ co2 ）比例影響轉化率和二次燃燒率；而在任意比例下保證充分反應的溫度為900以上It ' s pointed out that, under the condition of vim refining, the amount of oxide inclusions residue in molten steel increases with the increased loss of deoxidizing elements, and the key of melting extra - low oxygen steel is to avoid the thermal decomposition of lining material ; the size of deoxidizing products increases with the increased degree of supersaturation of deoxidizing elements ; larger inclusions granules found in extra - low oxygen steel come mainly from lining material
結果表明，在真空感應熔煉條件下，殘留在鋼中的氧化物夾雜數量隨脫氧元素鋁燒損量增加而增加，熔煉超低氧鋼的關鍵是避免爐襯熱分解；脫氧產物尺寸隨脫氧元素過飽和度增加而增加；超低氧鋼的大顆粒夾雜主要來自爐襯材料。