Inorganic salts, such as a1 ( no3 ) 3, zrocl2, ticl3, et al. was used as raw materials and corresponding hydroxides were deposited on the surface of graphite particle with heterogeneous nucleation process ; composite particles of graphite / oxides were obtained after heat treatment. in this paper, preparing conditions and properties of composite particles were studied
本論文以無機鹽（硝酸鋁、氧氯化鋯、三氯化鈦等）為原料，在石墨的稀懸浮液中應用非均勻成核技術，使水解產物（水合氧化物）沉積到微米級鱗片石墨表面，經洗滌、烘乾和熱處理制備出石墨氧化物復合粉體。In this study, the preparing processes of zro2 - ni nanocrystalline composite powder aremixing the nickel salt, zirconium salt and stabilizer, solvent ( distilled water ) together to prepare the mixing solution according to certain ratio ; commingling the mixing solution, coordination solution of carboxylic ammonia, intrusion aid in accordance with certain rate to form sol, drying the sol and turning it into gel, pre - sintering the gel to get the zro2 - nio powder and gaining zro2 - ni nanocrystalline composite powder by reducing the zro2 - nio powder. xrd, x - ray wide - angle diffractometer, bet, sem, tem, hrtem analyses are used to study the zro2 - ni nanocrystalline composite powder and zro2 - ni cermet. the sintering temperature is determined
本研究的zro _ 2 - ni納米復合粉末的制備方法如下：將鎳鹽、鋯鹽、穩定劑和溶劑（水）按所需成分配成混合溶液，再將混合溶液、外加劑和氨羧絡合劑按比例混合形成溶膠，溶膠經乾燥成為凝膠，凝膠經預燒得到zro _ 2 - nio納米粉，將該氧化物粉還原得到zro _ 2 - ni納米復合粉。
分享友人